牌号简介 About |
---|
Lotr_ne Q1018系列是用丁烯(C4)共单体在气相反应器中生产的线性低密度聚乙烯树脂。它们是为吹塑薄膜应用而设计的,可以纯形式使用,也可以与其他聚乙烯树脂(例如,用于单挤出或共挤出工艺的低密度聚乙烯或高密度聚乙烯和MPE树脂)混合,以改变薄膜性能。Lotr_ne Q1018系列适用于消费者、农业、工业、食品或卫生包装领域的许多应用,例如:整理收缩、衬垫、FFS袋、重型袋、垃圾、隧道膜、覆盖膜…… Lotrène® Q1018 Series are Linear Low Density Polyethylene resins produced in a gas phase reactor using butene (C4) co-monomer. They are designed for blown film applications and can be used in pure form as well as blended with other PE resins, such as LDPE or HDPE and mPE resins for mono extrusion or co-extrusion process to modify film properties. Lotrène® Q1018 Series are suited for many applications in the field of consumer, agricultural, industrial, food or hygiene packaging, for example: collation shrink, liners, FFS bags, heavy duty sacks, refuse, tunnel films, mulching films… |
产品描述 Product Description
厂家:卡塔尔石化 QAPCO
类别:LLDPE Linear low density polyethylene
用途:重包装袋;薄膜;衬里;包装;袋子;工业应用;收缩性薄膜;食品包装;消费品应用领域;薄壁包装;混合;农业应用;
加工条件:吹塑薄膜
性能特点: 抗结块性; 热稳定性好; 高光滑性; 丁烯共聚单体; Smoothness,High anti-blocking,Butylene copolymer,Heat Stabilized
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.918 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
1.0 | g/10min | ASTM D1238 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
割线模量 Secant modulus |
ASTM D882 | ||
1% 正割,MD:40 µm,吹塑薄膜 1% secant, MD: 40 µ m, blow molded film |
215 | MPa | ASTM D882 |
1% 正割,TD:40 µm,吹塑薄膜 1% secant, TD: 40 µ m, blow molded film |
245 | MPa | ASTM D882 |
拉伸强度 tensile strength |
ASTM D882 | ||
MD,屈服,40 µm,吹塑薄膜 MD, yield, 40 µ m, blow molded film |
11.0 | MPa | ASTM D882 |
TD,屈服,40 µm,吹塑薄膜 TD, yield, 40 µ m, blow molded film |
MPa | ASTM D882 | |
MD,断裂,40 µm,吹塑薄膜 MD, fracture, 40 µ m, blow molded film |
MPa | ASTM D882 | |
TD,断裂,40 µm,吹塑薄膜 TD, fracture, 40 µ m, blow molded film |
MPa | ASTM D882 | |
拉伸应变 Tensile strain |
ASTM D882 | ||
MD,断裂,40 µm,吹塑薄膜 MD, fracture, 40 µ m, blow molded film |
% | ASTM D882 | |
TD,断裂,40 µm,吹塑薄膜 TD, fracture, 40 µ m, blow molded film |
% | ASTM D882 | |
落锤冲击 Drop hammer impact 2 |
|||
40 µm,吹塑薄膜 40 µ m, blow molded film 2 |
g | ASTM D1709 | |
埃尔曼多夫抗撕强度 Elmandorf tear strength |
ASTM D1922 | ||
MD:40 µm,吹塑薄膜 MD: 40 µ m, blow molded film |
g | ASTM D1922 | |
TD:40 µm,吹塑薄膜 TD: 40 µ m, blow molded film |
g | ASTM D1922 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 | |
结晶峰温度 Crystallization peak temperature |
|||
DSC DSC |
℃ | 内部方法 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
45°,40.0 µm,吹塑薄膜 45 °, 40.0 µ m, blow molded film |
ASTM D2457 | ||
雾度 Haze |
|||
40 µm,吹塑薄膜 40 µ m, blow molded film |
% | ASTM D1003 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 F50 |
【新闻资讯】查看全部
新力新材“尼龙66聚合项目”正式投产成功
2022-01-16 搜料网资讯: 1月9日,新力新材滨海分公司生产的尼龙66聚合项目正式投产成功。该项目是新力目前改性产品的上游源头材料,预计年产量达到15000吨,产值超5个亿,可助力新力以聚合、 |
新力新材“尼龙66聚合项目”正式投产成功 搜料网资讯:1月9日,新力新材滨海分公司生产的“尼龙66聚合项目”正式投产成功。该项目是新力目前改性产品的上游源头材料,预计年产量达到15000吨,产值超5个亿,可助力新力以聚合、改性为中心,创造新品类,实现从“跟跑”到“领跑”,用更附有创造力的方式满足不同客户的需求,并加速使之成为国内最具竞争力的工程塑料改性企业。 浙江新力新材料股份有限公司,前身为瑞安市杜邦工程塑料有限公司,是一家集研发、生产、销售、服务为一体的高科技民营企业,专注于改性塑料领域相关产品和解决方案的提供。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
价格走势图
开始时间:
结束时间:
材料厂家:
【牌号齐全,内容全面】
全网共2500+项牌号+上游原料单体+原油价格,最长可追溯近20年价格行情
【精准,及时,权威!】
专业团队挖掘行情信息,第一时间发布行情
抱歉!该牌号暂无认证数据。
免责声明:参考价格是搜料网根据网络大数据拟合分析的结果,仅供参考。实际成交价取决但不限于以下因素:下单时间,付款方式,交货方式,数量,税费,色号,产地,项目信息。
抱歉!暂无数据。
抱歉!暂无数据。