牌号简介 About |
---|
Texin® 270树脂是一种芳香族聚酯基热塑性聚氨酯,肖氏硬度约为70d,可通过注塑加工,不建议采用挤出工艺。 Texin 270 resin is an aromatic polyester-based thermoplastic polyurethane with a Shore hardness of approximately 70D. It can be processed by injection molding; extrusion processes are not recommended. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.24 | g/cm³ | ASTM D792 |
密度 Density |
1.24 | g/cm³ | ISO 1183 |
收缩率 Shrinkage rate |
ISO 2577 | ||
TD:2.54 mm TD:2.54 mm |
0.80 | % | ASTM D955 |
MD:2.54 mm MD:2.54 mm |
0.80 | % | ASTM D955 |
TD:2.54 mm TD:2.54 mm |
0.80 | % | ISO 2577 |
MD:2.54 mm MD:2.54 mm |
% | ISO 2577 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
ISO 868 | ||
邵氏 D Shaw's D |
ASTM D2240 | ||
弯曲模量 Bending modulus |
ASTM D790 | ||
-30℃ -30℃ |
MPa | ASTM D790 | |
23℃ 23℃ |
MPa | ASTM D790 | |
70℃ 70℃ |
MPa | ASTM D790 | |
弯曲模量 Bending modulus |
ISO 178 | ||
-30℃ -30℃ |
MPa | ISO 178 | |
23℃ 23℃ |
MPa | ISO 178 | |
70℃ 70℃ |
MPa | ISO 178 | |
泰伯耐磨性 Taber abraser |
|||
1000 周期,1000 g,H-18 转轮 1000 cycles, 1000 g, H-18 wheels |
mg | ISO 4649 | |
1000 周期,1000 g,H-18 转轮 1000 cycles, 1000 g, H-18 wheels |
mg | ASTM D1044 | |
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
屈服 yield |
MPa | ISO 37 | |
屈服 yield |
MPa | ASTM D412 | |
300% 应变 300% strain |
MPa | ASTM D412 | |
300% 应变 300% strain |
MPa | ISO 37 | |
100% 应变 100% strain |
MPa | ISO 37 | |
100% 应变 100% strain |
MPa | ASTM D412 | |
50% 应变 50% strain |
MPa | ISO 37 | |
50% 应变 50% strain |
MPa | ASTM D412 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D412 | |
断裂 fracture |
% | ISO 37 | |
撕裂强度 tear strength 2 |
kN/m | ASTM D624 | |
撕裂强度 tear strength |
kN/m | ISO 34-1 | |
压缩形变 Compression deformation |
ASTM D395B | ||
23℃,22 hr 23℃,22 hr 3 |
% | ASTM D395B | |
23℃,22 hr 23℃,22 hr |
% | ASTM D395B | |
70℃,22 hr 70℃,22 hr 3 |
% | ASTM D395B | |
70℃,22 hr 70℃,22 hr |
% | ASTM D395B | |
压缩形变 Compression deformation |
ISO 815 | ||
23℃,22 hr 23℃,22 hr |
% | ISO 815 | |
23℃,22 hr 23℃,22 hr 3 |
% | ISO 815 | |
70℃,22 hr 70℃,22 hr |
% | ISO 815 | |
70℃,22 hr 70℃,22 hr 3 |
% | ISO 815 | |
巴肖氏弹性 Basho's elasticity |
% | ASTM D2632 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ASTM D648 | |
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
脆化温度 Embrittlement temperature |
℃ | ASTM D746 | |
脆化温度 Embrittlement temperature |
℃ | ISO 974 | |
玻璃化转变温度 Glass transition temperature |
℃ | DMA | |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 4 | |
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306/50 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD MD |
1/℃ | ASTM D696 | |
老化性能 Aging performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
空气中拉伸强度的变化率 The rate of change in tensile strength in air |
ASTM D573 | ||
100℃,70 hr 100℃,70 hr |
% | ASTM D573 | |
100% Strain,100℃,70 hr 100% Strain,100℃,70 hr |
% | ASTM D573 | |
300% Strain,100℃,70 hr 300% Strain,100℃,70 hr |
% | ASTM D573 | |
100℃,168 hr 100℃,168 hr |
% | ASTM D573 | |
100% Strain,100℃,168 hr 100% Strain,100℃,168 hr |
% | ASTM D573 | |
300% Strain,100℃,168 hr 300% Strain,100℃,168 hr |
% | ASTM D573 | |
100℃,336 hr 100℃,336 hr |
% | ASTM D573 | |
100% Strain,100℃,336 hr 100% Strain,100℃,336 hr |
% | ASTM D573 | |
300% Strain,100℃,336 hr 300% Strain,100℃,336 hr |
% | ASTM D573 | |
100℃,504 hr 100℃,504 hr |
% | ASTM D573 | |
100% Strain,100℃,504 hr 100% Strain,100℃,504 hr |
% | ASTM D573 | |
300% Strain,100℃,504 hr 300% Strain,100℃,504 hr |
% | ASTM D573 | |
空气中拉伸强度的变化率 The rate of change in tensile strength in air |
ISO 216 | ||
100℃,70 hr 100℃,70 hr |
% | ISO 216 | |
100% Strain 100℃,70 hr 100% Strain 100℃,70 hr |
% | ISO 216 | |
300% Strain 100℃,70 hr 300% Strain 100℃,70 hr |
% | ISO 216 | |
100℃,168 hr 100℃,168 hr |
% | ISO 216 | |
100% Strain 100℃,168 hr 100% Strain 100℃,168 hr |
% | ISO 216 | |
300% Strain 100℃,168 hr 300% Strain 100℃,168 hr |
% | ISO 216 | |
100℃,336 hr 100℃,336 hr |
% | ISO 216 | |
100% Strain 100℃,336 hr 100% Strain 100℃,336 hr |
% | ISO 216 | |
300% Strain 100℃,336 hr 300% Strain 100℃,336 hr |
% | ISO 216 | |
100℃,504 hr 100℃,504 hr |
% | ISO 216 | |
100% Strain 100℃,504 hr 100% Strain 100℃,504 hr |
% | ISO 216 | |
300% Strain 100℃,504 hr 300% Strain 100℃,504 hr |
% | ISO 216 | |
空气中极限伸长率的变化率 The rate of change in ultimate elongation in air |
ASTM D573 | ||
100℃,70 hr 100℃,70 hr |
% | ASTM D573 | |
100℃,168 hr 100℃,168 hr |
% | ASTM D573 | |
100℃,336 hr 100℃,336 hr |
% | ASTM D573 | |
100℃,504 hr 100℃,504 hr |
% | ASTM D573 | |
在空气中断裂时拉伸应力变化 Changes in tensile stress during fracture in air |
ISO 216 | ||
100℃,70 hr 100℃,70 hr |
% | ISO 216 | |
100℃,168 hr 100℃,168 hr |
% | ISO 216 | |
100℃,336 hr 100℃,336 hr |
% | ISO 216 | |
100℃,504 hr 100℃,504 hr |
% | ISO 216 | |
空气中硬度计硬度的变化率 The rate of change in hardness of a hardness tester in the air |
ASTM D573 | ||
邵氏 D,100℃,70 hr Shore D, 100 ℃, 70 hr |
ASTM D573 | ||
邵氏 D,100℃,168 hr Shore D, 100 ℃, 168 hr |
ASTM D573 | ||
邵氏 D,100℃,336 hr Shore D, 100 ℃, 336 hr |
ASTM D573 | ||
邵氏 D,100℃,504 hr Shore D, 100 ℃, 504 hr |
ASTM D573 | ||
空气中邵氏硬度的变化率 The rate of change of Shore hardness in air |
ISO 216 | ||
邵氏 D,100℃,70 hr Shore D, 100 ℃, 70 hr |
ISO 216 | ||
邵氏 D,100℃,168 hr Shore D, 100 ℃, 168 hr |
ISO 216 | ||
邵氏 D,100℃,336 hr Shore D, 100 ℃, 336 hr |
ISO 216 | ||
邵氏 D,100℃,504 hr Shore D, 100 ℃, 504 hr |
ISO 216 | ||
拉伸强度的变化率 The rate of change in tensile strength |
ASTM D471 | ||
23℃,70 hr,in Reference Fuel A(Isooctane) 23℃,70 hr,in Reference Fuel A(Isooctane) |
% | ASTM D471 | |
100% Strain,23℃,70 hr,in Reference Fuel A(Isooctane) 100% Strain,23℃,70 hr,in Reference Fuel A(Isooctane) |
% | ASTM D471 | |
300% Strain,23℃,70 hr,in Reference Fuel A(Isooctane) 300% Strain,23℃,70 hr,in Reference Fuel A(Isooctane) |
% | ASTM D471 | |
23℃,70 hr,甲醇 23 ℃, 70 hr, methanol |
% | ASTM D471 | |
100% Strain,23℃,70 hr,in Reference Fuel C 100% Strain,23℃,70 hr,in Reference Fuel C |
% | ASTM D471 | |
300% Strain,23℃,70 hr,in Reference Fuel C 300% Strain,23℃,70 hr,in Reference Fuel C |
% | ASTM D471 | |
23℃,168 hr,in Reference Fuel A(Isooctane) 23℃,168 hr,in Reference Fuel A(Isooctane) |
% | ASTM D471 | |
100% Strain,23℃,168 hr,in Reference Fuel A(Isooctane) 100% Strain,23℃,168 hr,in Reference Fuel A(Isooctane) |
% | ASTM D471 | |
300% Strain,23℃,168 hr,in Reference Fuel A(Isooctane) 300% Strain,23℃,168 hr,in Reference Fuel A(Isooctane) |
% | ASTM D471 | |
23℃,168 hr,甲醇 23 ℃, 168 hr, methanol |
% | ASTM D471 | |
100% Strain,23℃,168 hr,in Reference Fuel C 100% Strain,23℃,168 hr,in Reference Fuel C |
% | ASTM D471 | |
300% Strain,23℃,168 hr,in Reference Fuel C 300% Strain,23℃,168 hr,in Reference Fuel C |
% | ASTM D471 | |
23℃,336 hr,in Reference Fuel A(Isooctane) 23℃,336 hr,in Reference Fuel A(Isooctane) |
% | ASTM D471 | |
100% Strain,23℃,336 hr,in Reference Fuel A(Isooctane) 100% Strain,23℃,336 hr,in Reference Fuel A(Isooctane) |
% | ASTM D471 | |
300% Strain,23℃,336 hr,in Reference Fuel A(Isooctane) 300% Strain,23℃,336 hr,in Reference Fuel A(Isooctane) |
% | ASTM D471 | |
23℃,336 hr,in Reference Fuel C 23℃,336 hr,in Reference Fuel C |
% | ASTM D471 | |
100% Strain,23℃,336 hr,in Reference Fuel C 100% Strain,23℃,336 hr,in Reference Fuel C |
% | ASTM D471 | |
300% Strain,23℃,336 hr,in Reference Fuel C 300% Strain,23℃,336 hr,in Reference Fuel C |
% | ASTM D471 | |
23℃,504 hr,in Reference Fuel A(Isooctane) 23℃,504 hr,in Reference Fuel A(Isooctane) |
% | ASTM D471 | |
100% Strain,23℃,504 hr,in Reference Fuel A(Isooctane) 100% Strain,23℃,504 hr,in Reference Fuel A(Isooctane) |
% | ASTM D471 | |
300% Strain,23℃,504 hr,in Reference Fuel A(Isooctane) 300% Strain,23℃,504 hr,in Reference Fuel A(Isooctane) |
% | ASTM D471 | |
23℃,504 hr,in Reference Fuel C 23℃,504 hr,in Reference Fuel C |
% | ASTM D471 | |
100% Strain,23℃,504 hr,in Reference Fuel C 100% Strain,23℃,504 hr,in Reference Fuel C |
% | ASTM D471 | |
300% Strain,23℃,504 hr,in Reference Fuel C 300% Strain,23℃,504 hr,in Reference Fuel C |
% | ASTM D471 | |
100℃,70 hr,在ASTM #1油中 100 ℃, 70 hr, in ASTM # 1 oil |
% | ASTM D471 | |
100% Strain,100℃,70 hr,in ASTM #1 Oil 100% Strain,100℃,70 hr,in ASTM #1 Oil |
% | ASTM D471 | |
300% Strain,100℃,70 hr,in ASTM #1 Oil 300% Strain,100℃,70 hr,in ASTM #1 Oil |
% | ASTM D471 | |
100℃,70 hr,在ASTM #3油中 100 ℃, 70 hr, in ASTM # 3 oil |
% | ASTM D471 | |
100% Strain,100℃,70 hr,in ASTM #3 Oil 100% Strain,100℃,70 hr,in ASTM #3 Oil |
% | ASTM D471 | |
300% Strain,100℃,70 hr,in ASTM #3 Oil 300% Strain,100℃,70 hr,in ASTM #3 Oil |
% | ASTM D471 | |
100℃,168 hr,in ASTM #1 Oil 100℃,168 hr,in ASTM #1 Oil |
% | ASTM D471 | |
100% Strain,100℃,168 hr,in ASTM #1 Oil 100% Strain,100℃,168 hr,in ASTM #1 Oil |
% | ASTM D471 | |
300% Strain,100℃,168 hr,in ASTM #1 Oil 300% Strain,100℃,168 hr,in ASTM #1 Oil |
% | ASTM D471 | |
100℃,168 hr,in ASTM #3 Oil 100℃,168 hr,in ASTM #3 Oil |
% | ASTM D471 | |
100% Strain,100℃,168 hr,in ASTM #3 Oil 100% Strain,100℃,168 hr,in ASTM #3 Oil |
% | ASTM D471 | |
300% Strain,100℃,168 hr,in ASTM #3 Oil 300% Strain,100℃,168 hr,in ASTM #3 Oil |
% | ASTM D471 | |
100℃,336 hr,in ASTM #1 Oil 100℃,336 hr,in ASTM #1 Oil |
% | ASTM D471 | |
100% Strain,100℃,336 hr,in ASTM #1 Oil 100% Strain,100℃,336 hr,in ASTM #1 Oil |
% | ASTM D471 | |
300% Strain,100℃,336 hr,in ASTM #1 Oil 300% Strain,100℃,336 hr,in ASTM #1 Oil |
% | ASTM D471 | |
100℃,336 hr,in ASTM #3 Oil 100℃,336 hr,in ASTM #3 Oil |
% | ASTM D471 | |
100% Strain,100℃,336 hr,in ASTM #3 Oil 100% Strain,100℃,336 hr,in ASTM #3 Oil |
% | ASTM D471 | |
300% Strain,100℃,336 hr,in ASTM #3 Oil 300% Strain,100℃,336 hr,in ASTM #3 Oil |
% | ASTM D471 | |
100℃,504 hr,in ASTM #1 Oil 100℃,504 hr,in ASTM #1 Oil |
% | ASTM D471 | |
100% Strain,100℃,504 hr,in ASTM #1 Oil 100% Strain,100℃,504 hr,in ASTM #1 Oil |
% | ASTM D471 | |
300% Strain,100℃,504 hr,in ASTM #1 Oil 300% Strain,100℃,504 hr,in ASTM #1 Oil |
% | ASTM D471 | |
100℃,504 hr,in ASTM #3 Oil 100℃,504 hr,in ASTM #3 Oil |
% | ASTM D471 | |
100% Strain,100℃,504 hr,in ASTM #3 Oil 100% Strain,100℃,504 hr,in ASTM #3 Oil |
% | ASTM D471 | |
300% Strain,100℃,504 hr,in ASTM #3 Oil 300% Strain,100℃,504 hr,in ASTM #3 Oil |
% | ASTM D471 | |
拉伸强度的变化率 The rate of change in tensile strength |
ISO 175 | ||
23℃,70 hr,in Reference Fuel A(Isooctane) 23℃,70 hr,in Reference Fuel A(Isooctane) |
% | ISO 175 | |
100% Strain,23℃,70 hr,in Reference Fuel A(Isooctane) 100% Strain,23℃,70 hr,in Reference Fuel A(Isooctane) |
% | ISO 175 | |
300% Strain,23℃,70 hr,in Reference Fuel A(Isooctane) 300% Strain,23℃,70 hr,in Reference Fuel A(Isooctane) |
% | ISO 175 | |
23℃,70 hr,甲醇 23 ℃, 70 hr, methanol |
% | ISO 175 | |
100% Strain,23℃,70 hr,in Reference Fuel C 100% Strain,23℃,70 hr,in Reference Fuel C |
% | ISO 175 | |
300% Strain,23℃,70 hr,in Reference Fuel C 300% Strain,23℃,70 hr,in Reference Fuel C |
% | ISO 175 | |
23℃,168 hr,in Reference Fuel A(Isooctane) 23℃,168 hr,in Reference Fuel A(Isooctane) |
% | ISO 175 | |
100% Strain,23℃,168 hr,in Reference Fuel A(Isooctane) 100% Strain,23℃,168 hr,in Reference Fuel A(Isooctane) |
% | ISO 175 | |
300% Strain,23℃,168 hr,in Reference Fuel A(Isooctane) 300% Strain,23℃,168 hr,in Reference Fuel A(Isooctane) |
% | ISO 175 | |
23℃,168 hr,甲醇 23 ℃, 168 hr, methanol |
% | ISO 175 | |
100% Strain,23℃,168 hr,in Reference Fuel C 100% Strain,23℃,168 hr,in Reference Fuel C |
% | ISO 175 | |
300% Strain,23℃,168 hr,in Reference Fuel C 300% Strain,23℃,168 hr,in Reference Fuel C |
% | ISO 175 | |
23℃,336 hr,in Reference Fuel A(Isooctane) 23℃,336 hr,in Reference Fuel A(Isooctane) |
% | ISO 175 | |
100% Strain,23℃,336 hr,in Reference Fuel A(Isooctane) 100% Strain,23℃,336 hr,in Reference Fuel A(Isooctane) |
% | ISO 175 | |
300% Strain,23℃,336 hr,in Reference Fuel A(Isooctane) 300% Strain,23℃,336 hr,in Reference Fuel A(Isooctane) |
% | ISO 175 | |
23℃,336 hr,in Reference Fuel C 23℃,336 hr,in Reference Fuel C |
% | ISO 175 | |
100% Strain,23℃,336 hr,in Reference Fuel C 100% Strain,23℃,336 hr,in Reference Fuel C |
% | ISO 175 | |
300% Strain,23℃,336 hr,in Reference Fuel C 300% Strain,23℃,336 hr,in Reference Fuel C |
% | ISO 175 | |
23℃,504 hr,in Reference Fuel A(Isooctane) 23℃,504 hr,in Reference Fuel A(Isooctane) |
% | ISO 175 | |
100% Strain,23℃,504 hr,in Reference Fuel A(Isooctane) 100% Strain,23℃,504 hr,in Reference Fuel A(Isooctane) |
% | ISO 175 | |
300% Strain,23℃,504 hr,in Reference Fuel A(Isooctane) 300% Strain,23℃,504 hr,in Reference Fuel A(Isooctane) |
% | ISO 175 | |
23℃,504 hr,in Reference Fuel C 23℃,504 hr,in Reference Fuel C |
% | ISO 175 | |
100% Strain,23℃,504 hr,in Reference Fuel C 100% Strain,23℃,504 hr,in Reference Fuel C |
% | ISO 175 | |
300% Strain,23℃,504 hr,in Reference Fuel C 300% Strain,23℃,504 hr,in Reference Fuel C |
% | ISO 175 | |
100℃,70 hr,在ASTM #1油中 100 ℃, 70 hr, in ASTM # 1 oil |
% | ISO 175 | |
100% Strain,100℃,70 hr,in ASTM #1 Oil 100% Strain,100℃,70 hr,in ASTM #1 Oil |
% | ISO 175 | |
300% Strain,100℃,70 hr,in ASTM #1 Oil 300% Strain,100℃,70 hr,in ASTM #1 Oil |
% | ISO 175 | |
100℃,70 hr,在ASTM #3油中 100 ℃, 70 hr, in ASTM # 3 oil |
% | ISO 175 | |
100% Strain,100℃,70 hr,in ASTM #3 Oil 100% Strain,100℃,70 hr,in ASTM #3 Oil |
% | ISO 175 | |
300% Strain,100℃,70 hr,in ASTM #3 Oil 300% Strain,100℃,70 hr,in ASTM #3 Oil |
% | ISO 175 | |
100℃,168 hr,in ASTM #1 Oil 100℃,168 hr,in ASTM #1 Oil |
% | ISO 175 | |
100% Strain,100℃,168 hr,in ASTM #1 Oil 100% Strain,100℃,168 hr,in ASTM #1 Oil |
% | ISO 175 | |
300% Strain,100℃,168 hr,in ASTM #1 Oil 300% Strain,100℃,168 hr,in ASTM #1 Oil |
% | ISO 175 | |
100℃,168 hr,in ASTM #3 Oil 100℃,168 hr,in ASTM #3 Oil |
% | ISO 175 | |
100% Strain,100℃,168 hr,in ASTM #3 Oil 100% Strain,100℃,168 hr,in ASTM #3 Oil |
% | ISO 175 | |
300% Strain,100℃,168 hr,in ASTM #3 Oil 300% Strain,100℃,168 hr,in ASTM #3 Oil |
% | ISO 175 | |
100℃,336 hr,in ASTM #1 Oil 100℃,336 hr,in ASTM #1 Oil |
% | ISO 175 | |
100% Strain,100℃,336 hr,in ASTM #1 Oil 100% Strain,100℃,336 hr,in ASTM #1 Oil |
% | ISO 175 | |
300% Strain,100℃,336 hr,in ASTM #1 Oil 300% Strain,100℃,336 hr,in ASTM #1 Oil |
% | ISO 175 | |
100℃,336 hr,in ASTM #3 Oil 100℃,336 hr,in ASTM #3 Oil |
% | ISO 175 | |
100% Strain,100℃,336 hr,in ASTM #3 Oil 100% Strain,100℃,336 hr,in ASTM #3 Oil |
% | ISO 175 | |
300% Strain,100℃,336 hr,in ASTM #3 Oil 300% Strain,100℃,336 hr,in ASTM #3 Oil |
% | ISO 175 | |
100℃,504 hr,in ASTM #1 Oil 100℃,504 hr,in ASTM #1 Oil |
% | ISO 175 | |
100% Strain,100℃,504 hr,in ASTM #1 Oil 100% Strain,100℃,504 hr,in ASTM #1 Oil |
% | ISO 175 | |
300% Strain,100℃,504 hr,in ASTM #1 Oil 300% Strain,100℃,504 hr,in ASTM #1 Oil |
% | ISO 175 | |
100℃,504 hr,in ASTM #3 Oil 100℃,504 hr,in ASTM #3 Oil |
% | ISO 175 | |
100% Strain,100℃,504 hr,in ASTM #3 Oil 100% Strain,100℃,504 hr,in ASTM #3 Oil |
% | ISO 175 | |
300% Strain,100℃,504 hr,in ASTM #3 Oil 300% Strain,100℃,504 hr,in ASTM #3 Oil |
% | ISO 175 | |
极限伸长率的变化率 Change rate of ultimate elongation |
ASTM D471 | ||
23℃,70 hr,in Reference Fuel A(Isooctane) 23℃,70 hr,in Reference Fuel A(Isooctane) |
% | ASTM D471 | |
23℃,70 hr,甲醇 23 ℃, 70 hr, methanol |
% | ASTM D471 | |
23℃,168 hr,in Reference Fuel A(Isooctane) 23℃,168 hr,in Reference Fuel A(Isooctane) |
% | ASTM D471 | |
23℃,168 hr,甲醇 23 ℃, 168 hr, methanol |
% | ASTM D471 | |
23℃,336 hr,in Reference Fuel A(Isooctane) 23℃,336 hr,in Reference Fuel A(Isooctane) |
% | ASTM D471 | |
23℃,336 hr,in Reference Fuel C 23℃,336 hr,in Reference Fuel C |
% | ASTM D471 | |
23℃,504 hr,in Reference Fuel A(Isooctane) 23℃,504 hr,in Reference Fuel A(Isooctane) |
% | ASTM D471 | |
23℃,504 hr,in Reference Fuel C 23℃,504 hr,in Reference Fuel C |
% | ASTM D471 | |
100℃,70 hr,在ASTM #1油中 100 ℃, 70 hr, in ASTM # 1 oil |
% | ASTM D471 | |
100℃,70 hr,在ASTM #3油中 100 ℃, 70 hr, in ASTM # 3 oil |
% | ASTM D471 | |
100℃,168 hr,in ASTM #1 Oil 100℃,168 hr,in ASTM #1 Oil |
% | ASTM D471 | |
100℃,168 hr,in ASTM #3 Oil 100℃,168 hr,in ASTM #3 Oil |
% | ASTM D471 | |
100℃,336 hr,in ASTM #1 Oil 100℃,336 hr,in ASTM #1 Oil |
% | ASTM D471 | |
100℃,336 hr,in ASTM #3 Oil 100℃,336 hr,in ASTM #3 Oil |
% | ASTM D471 | |
100℃,504 hr,in ASTM #1 Oil 100℃,504 hr,in ASTM #1 Oil |
% | ASTM D471 | |
100℃,504 hr,in ASTM #3 Oil 100℃,504 hr,in ASTM #3 Oil |
% | ASTM D471 | |
断裂时拉伸应力变化 Changes in tensile stress during fracture |
ISO 175 | ||
23℃,70 hr,in Reference Fuel A(Isooctane) 23℃,70 hr,in Reference Fuel A(Isooctane) |
% | ISO 175 | |
23℃,70 hr,甲醇 23 ℃, 70 hr, methanol |
% | ISO 175 | |
23℃,168 hr,in Reference Fuel A(Isooctane) 23℃,168 hr,in Reference Fuel A(Isooctane) |
% | ISO 175 | |
23℃,168 hr,甲醇 23 ℃, 168 hr, methanol |
% | ISO 175 | |
23℃,336 hr,in Reference Fuel A(Isooctane) 23℃,336 hr,in Reference Fuel A(Isooctane) |
% | ISO 175 | |
23℃,336 hr,in Reference Fuel C 23℃,336 hr,in Reference Fuel C |
% | ISO 175 | |
23℃,504 hr,in Reference Fuel A(Isooctane) 23℃,504 hr,in Reference Fuel A(Isooctane) |
% | ISO 175 | |
23℃,504 hr,in Reference Fuel C 23℃,504 hr,in Reference Fuel C |
% | ISO 175 | |
100℃,70 hr,在ASTM #1油中 100 ℃, 70 hr, in ASTM # 1 oil |
% | ISO 175 | |
100℃,70 hr,在ASTM #3油中 100 ℃, 70 hr, in ASTM # 3 oil |
% | ISO 175 | |
100℃,168 hr,in ASTM #1 Oil 100℃,168 hr,in ASTM #1 Oil |
% | ISO 175 | |
100℃,168 hr,in ASTM #3 Oil 100℃,168 hr,in ASTM #3 Oil |
% | ISO 175 | |
100℃,336 hr,in ASTM #1 Oil 100℃,336 hr,in ASTM #1 Oil |
% | ISO 175 | |
100℃,336 hr,in ASTM #3 Oil 100℃,336 hr,in ASTM #3 Oil |
% | ISO 175 | |
100℃,504 hr,in ASTM #1 Oil 100℃,504 hr,in ASTM #1 Oil |
% | ISO 175 | |
100℃,504 hr,in ASTM #3 Oil 100℃,504 hr,in ASTM #3 Oil |
% | ISO 175 | |
邵氏硬度的变化率 The rate of change in Shore hardness 2 |
ASTM D471 | ||
邵氏 D,23℃,70 hr,在基准燃料A(异辛烷)中 Shore D, 23 ℃, 70 hr, in reference fuel A (isooctane) |
ASTM D471 | ||
邵氏 D,23℃,70 hr,在基准燃料C中 Shore D, 23°C, 70 hr, in Reference Fuel C |
ASTM D471 | ||
邵氏 D,23℃,168 hr,在基准燃料A(异辛烷)中 Shore D, 23 ℃, 168 hr, in reference fuel A (isooctane) |
ASTM D471 | ||
邵氏 D,23℃,168 hr,在基准燃料中 Shore D, 23 ℃, 168 hr, in reference fuel |
ASTM D471 | ||
邵氏 D,23℃,336 hr,在基准燃料A(异辛烷)中 Shore D, 23 ℃, 336 hr, in reference fuel A (isooctane) |
ASTM D471 | ||
邵氏 D,23℃,336 hr,在基准燃料C中 Shore D, 23 ℃, 336 hr, in reference fuel C |
ASTM D471 | ||
邵氏 D,23℃,504 hr,在基准燃料A(异辛烷)中 Shore D, 23 ℃, 504 hr, in reference fuel A (isooctane) |
ASTM D471 | ||
邵氏 D,23℃,504 hr,,在基准燃料C中 Shore D, 23 ℃, 504 hr, in reference fuel C |
ASTM D471 | ||
邵氏 D,100℃,70 hr,在ASTM #1油中 Shore D, 100°C, 70 hr, in ASTM #1 Oil |
ASTM D471 | ||
邵氏 D,100℃,70 hr,在ASTM #3油中 Shore D, 100 ℃, 70 hr, in ASTM # 3 oil |
ASTM D471 | ||
邵氏 D,100℃,168 hr,在ASTM #1油中 Shore D, 100°C, 168 hr, in ASTM #1 Oil |
ASTM D471 | ||
邵氏 D,100℃,168 hr,在ASTM #3油中 Shore D, 100 ℃, 168 hr, in ASTM # 3 oil |
ASTM D471 | ||
邵氏 D,100℃,336 hr,在ASTM #1油中 Shore D, 100 ℃, 336 hr, in ASTM # 1 oil |
ASTM D471 | ||
邵氏 D,100℃,336 hr,在ASTM #3油中 Shore D, 100 ℃, 336 hr, in ASTM # 3 oil |
ASTM D471 | ||
邵氏 D,100℃,504 hr,在ASTM #1油中 Shore D, 100 ℃, 504 hr, in ASTM # 1 oil |
ASTM D471 | ||
邵氏 D,100℃,504 hr,在ASTM #3油中 Shore D, 100 ℃, 504 hr, in ASTM # 3 oil |
ASTM D471 | ||
邵氏硬度的变化率 The rate of change in Shore hardness |
ISO 175 | ||
邵氏 D,23℃,70 hr,在基准燃料A(异辛烷)中 Shore D, 23 ℃, 70 hr, in reference fuel A (isooctane) |
ISO 175 | ||
邵氏 D,23℃,70 hr,在基准燃料C中 Shore D, 23°C, 70 hr, in Reference Fuel C |
ISO 175 | ||
邵氏 D,23℃,168 hr,在基准燃料A(异辛烷)中 Shore D, 23 ℃, 168 hr, in reference fuel A (isooctane) |
ISO 175 | ||
邵氏 D,23℃,168 hr,在基准燃料中 Shore D, 23 ℃, 168 hr, in reference fuel |
ISO 175 | ||
邵氏 D,23℃,336 hr,在基准燃料A(异辛烷)中 Shore D, 23 ℃, 336 hr, in reference fuel A (isooctane) |
ISO 175 | ||
邵氏 D,23℃,336 hr,在基准燃料C中 Shore D, 23 ℃, 336 hr, in reference fuel C |
ISO 175 | ||
邵氏 D,23℃,504 hr,在基准燃料A(异辛烷)中 Shore D, 23 ℃, 504 hr, in reference fuel A (isooctane) |
ISO 175 | ||
邵氏 D,23℃,504 hr,,在基准燃料C中 Shore D, 23 ℃, 504 hr, in reference fuel C |
ISO 175 | ||
邵氏 D,100℃,70 hr,在ASTM #1油中 Shore D, 100°C, 70 hr, in ASTM #1 Oil |
ISO 175 | ||
邵氏 D,100℃,70 hr,在ASTM #3油中 Shore D, 100 ℃, 70 hr, in ASTM # 3 oil |
ISO 175 | ||
邵氏 D,100℃,168 hr,在ASTM #1油中 Shore D, 100°C, 168 hr, in ASTM #1 Oil |
ISO 175 | ||
邵氏 D,100℃,168 hr,在ASTM #3油中 Shore D, 100 ℃, 168 hr, in ASTM # 3 oil |
ISO 175 | ||
邵氏 D,100℃,336 hr,在ASTM #1油中 Shore D, 100 ℃, 336 hr, in ASTM # 1 oil |
ISO 175 | ||
邵氏 D,100℃,336 hr,在ASTM #3油中 Shore D, 100 ℃, 336 hr, in ASTM # 3 oil |
ISO 175 | ||
邵氏 D,100℃,504 hr,在ASTM #1油中 Shore D, 100 ℃, 504 hr, in ASTM # 1 oil |
ISO 175 | ||
邵氏 D,100℃,504 hr,在ASTM #3油中 Shore D, 100 ℃, 504 hr, in ASTM # 3 oil |
ISO 175 | ||
体积变化 Volume change |
ASTM D471 | ||
23℃,70 hr,in Reference Fuel A 23℃,70 hr,in Reference Fuel A |
% | ASTM D471 | |
23℃,70 hr,甲醇 23 ℃, 70 hr, methanol |
% | ASTM D471 | |
23℃,168 hr,in Reference Fuel A 23℃,168 hr,in Reference Fuel A |
% | ASTM D471 | |
23℃,168 hr,甲醇 23 ℃, 168 hr, methanol |
% | ASTM D471 | |
23℃,336 hr,in Reference Fuel A 23℃,336 hr,in Reference Fuel A |
% | ASTM D471 | |
23℃,336 hr,in Reference Fuel C 23℃,336 hr,in Reference Fuel C |
% | ASTM D471 | |
23℃,504 hr,in Reference Fuel A 23℃,504 hr,in Reference Fuel A |
% | ASTM D471 | |
23℃,504 hr,in Reference Fuel C 23℃,504 hr,in Reference Fuel C |
% | ASTM D471 | |
100℃,70 hr,在ASTM #1油中 100 ℃, 70 hr, in ASTM # 1 oil |
% | ASTM D471 | |
100℃,70 hr,在ASTM #3油中 100 ℃, 70 hr, in ASTM # 3 oil |
% | ASTM D471 | |
100℃,168 hr,in ASTM #1 Oil 100℃,168 hr,in ASTM #1 Oil |
% | ASTM D471 | |
100℃,168 hr,in ASTM #3 Oil 100℃,168 hr,in ASTM #3 Oil |
% | ASTM D471 | |
100℃,336 hr,in ASTM #1 Oil 100℃,336 hr,in ASTM #1 Oil |
% | ASTM D471 | |
100℃,336 hr,in ASTM #3 Oil 100℃,336 hr,in ASTM #3 Oil |
% | ASTM D471 | |
100℃,504 hr,in ASTM #1 Oil 100℃,504 hr,in ASTM #1 Oil |
% | ASTM D471 | |
100℃,504 hr,in ASTM #3 Oil 100℃,504 hr,in ASTM #3 Oil |
% | ASTM D471 | |
体积变化 Volume change |
ISO 175 | ||
23℃,70 hr,in Reference Fuel A 23℃,70 hr,in Reference Fuel A |
% | ISO 175 | |
23℃,70 hr,甲醇 23 ℃, 70 hr, methanol |
% | ISO 175 | |
23℃,168 hr,in Reference Fuel A 23℃,168 hr,in Reference Fuel A |
% | ISO 175 | |
23℃,168 hr,甲醇 23 ℃, 168 hr, methanol |
% | ISO 175 | |
23℃,336 hr,in Reference Fuel A 23℃,336 hr,in Reference Fuel A |
% | ISO 175 | |
23℃,336 hr,in Reference Fuel C 23℃,336 hr,in Reference Fuel C |
% | ISO 175 | |
23℃,504 hr,in Reference Fuel A 23℃,504 hr,in Reference Fuel A |
% | ISO 175 | |
23℃,504 hr,in Reference Fuel C 23℃,504 hr,in Reference Fuel C |
% | ISO 175 | |
100℃,70 hr,在ASTM #1油中 100 ℃, 70 hr, in ASTM # 1 oil |
% | ISO 175 | |
100℃,70 hr,在ASTM #3油中 100 ℃, 70 hr, in ASTM # 3 oil |
% | ISO 175 | |
100℃,168 hr,in ASTM #1 Oil 100℃,168 hr,in ASTM #1 Oil |
% | ISO 175 | |
100℃,168 hr,in ASTM #3 Oil 100℃,168 hr,in ASTM #3 Oil |
% | ISO 175 | |
100℃,336 hr,in ASTM #1 Oil 100℃,336 hr,in ASTM #1 Oil |
% | ISO 175 | |
100℃,336 hr,in ASTM #3 Oil 100℃,336 hr,in ASTM #3 Oil |
% | ISO 175 | |
100℃,504 hr,in ASTM #1 Oil 100℃,504 hr,in ASTM #1 Oil |
% | ISO 175 | |
100℃,504 hr,in ASTM #3 Oil 100℃,504 hr,in ASTM #3 Oil |
% | ISO 175 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
压缩载荷 Compression load |
ASTM D575 | ||
10% 挠曲 10% deflection |
MPa | ASTM D575 | |
15% 挠曲 15% deflection |
MPa | ASTM D575 | |
2% 挠曲 2% deflection |
MPa | ASTM D575 | |
20% 挠曲 20% deflection |
MPa | ASTM D575 | |
25% 挠曲 25% deflection |
MPa | ASTM D575 | |
5% 挠曲 5% deflection |
MPa | ASTM D575 | |
50% 挠曲 50% deflection |
MPa | ASTM D575 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 C 模具 |
3 Post-cured 16 hr at 230°F |
4 速率 A (50°C/h) |
【新闻资讯】查看全部
科思创Maezio™延续纤维增强热塑性复合资料
2018-08-07 科思创在开发和推广连续纤维增强热塑性复合材料(CFRTP)的道路上又进一步,为其推出全新品牌名称Maezio™。 科思创Maezio™连续纤维增强热塑性复合材料(CFRTP) |
科思创Maezio™延续纤维增强热塑性复合资料 科思创在开发和推广连续纤维增强热塑性复合材料(CFRTP)的道路上又进一步,为其推出全新品牌名称Maezio™。 科思创Maezio™连续纤维增强热塑性复合材料(CFRTP)可以组合制成各种产品,给设计师带来全新的创意空间。 CFRTP复合材料的潜在应用领域之一是为轻型超薄笔记本电脑外壳打造新颖的外观效果。 中国互联网运动品牌必迈采用科思创CFRTP复合材料制造更轻盈更结实的马拉松跑鞋。 海尔推出一款卡萨帝品牌高端空调,主体外壳采用科思创Maezio™ CFRTP复合材料制成。CFRTP轻质、坚固,赋予设计师极大设计自由度。 由于全球对坚固、轻质材料的需求不断增长,该创新材料将大有用武之地,帮助节约资源,提升能效。Maezio™不仅能为交通、电子、消费品和医疗等行业的原始设备制造商和零部件供应商提供先进复合材料的强大性能,还能助其提升成本效益,实现规模化生产。 科思创复合材料业务联席首席执行官David Hartmann表示:“新品牌名称将大大提升我们产品的认知度,进一步增强我们在热塑性复合材料领域的专业度。我们相信,冠以新品牌的复合材料能为各个行业的新一代产品创造实实在在的价值。我们的材料能带来结构轻量化、强度及外观可定制化等方面的综合优势,以目前其他先进材料无法达到的规模进行生产。” 未来材料 这一面向未来的复合材料由连续碳纤或玻纤增强的聚碳酸酯、热塑性聚氨酯或其他热塑性树脂制成。在德国南部的马克特比巴特(Markt Bibart)生产基地,科思创利用这些材料生产复合单向带和片材,然后供应给客户进行深加工。这些材料坚固、轻质且美观,可以组合制成各种产品,给设计师带来全新的创意空间。 目前,由于缺乏兼具成本效益和可规模化生产的工艺,先进复合材料的进一步拓展受阻。除此之外,将其应用到大批量生产产品中也非易事。Maezio™复合材料的出现将打破这一现状。 适用于规模化生产 采用现有的热成型工具对该复合材料进行热成型处理,产出率高,生产周期短。当零部件年产量达到百万件规模时,这些优势尤为关键。此外,注塑成型、自动铺带、自动铺丝等生产技术也可适用于该复合材料。 作为一种热塑性复合材料,Maezio™产品在使用周期结束后可以回收利用,是“规模化和可持续性复合材料解决方案的卓越典范,能够助力各个行业通过材料技术跨越极限。”另一位复合材料业务联席首席执行官施马可博士(Dr. Michael Schmidt)如是说。 广受关注 Maezio™已经引起了不同行业细分市场的广泛关注,比如电子电气、汽车、家电、家具、医疗、体育用品、鞋履和箱包行业。 此前,全球最大的家电品牌海尔推出了一款卡萨帝品牌的高端空调,主体外壳采用Maezio™复合材料制成。在鞋履行业,这一复合材料应用于中国互联网运动品牌必迈的马拉松跑鞋,让广大的运动员和休闲跑步爱好者从中受益。 来源:PUWORLD |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |