牌号简介 About |
---|
Amodel A- 1933 HSL是一种33 %玻纤增强聚邻苯二甲酰胺(PPA)树脂。该牌号主要是为了改善产品在50/50乙二醇和水环境中的性能。在130 ℃(266 ° F )的温度下, 采用苛刻的汽车冷却剂系统、含有机酸稳定剂的乙二醇进行测试。结果表明,其性能超出了汽车行业对暴露在高温防冻液环境下,高分子材料所需的性能要求。 潜在应用包括各种汽车零部件,如节温器壳体、加热器核心端盖、加热器软管接头和进水口、插座、阀门。 黑色:A-1933 HSL BK 328 Amodel® A-1933 HSL is a 33% glass reinforced grade of polyphthalamide (PPA) resin. This grade was developed specifically for improved performance in a 50/50 ethylene glycol and water environment. This material was tested using the aggressive automotive coolant system, ethylene glycol with organic acid stabilizer, at 130°C (266°F). It exceeds the performance required by the automotive industry for polymeric materials exposed to high-temperature antifreeze solutions. Potential applications include a variety of automotive components such as thermostat housings, heater core endcaps, heater hose connectors, and water inlets, outlets, and valves. Black: A-1933 HSL BK 328 |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.49 | g/cm³ | ISO 1183/A |
收缩率 Shrinkage rate |
ISO 294-4 | ||
TD TD 2 |
1.0 | % | ASTM D955 |
MD MD 2 |
0.20 | % | ASTM D955 |
TD TD |
1.0 | % | ISO 294-4 |
MD MD |
0.20 | % | ISO 294-4 |
吸水率 Water absorption rate |
|||
24hr 24hr |
% | ASTM D570 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
MPa | ISO 527-2 | |
拉伸强度 tensile strength |
|||
屈服 yield |
MPa | ISO 527-2 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ISO 527-2 | |
弯曲模量 Bending modulus |
MPa | ISO 178 | |
弯曲强度 bending strength |
MPa | ISO 178 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
kJ/m² | ISO 179-1eA | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
kJ/m² | ISO 180-1A | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
熔融温度 Melting temperature |
℃ | ISO 11357-3 | |
老化性能 Aging performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
弯曲模量的保留率 Retention rate of bending modulus |
|||
1000 hr,in Glycol,130℃ 1000 hr,in Glycol,130℃ |
% | ISO 178 | |
弯曲强度的保留率 Retention rate of bending strength |
|||
1000 hr,in Glycol,130℃ 1000 hr,in Glycol,130℃ |
% | ISO 178 | |
Retention of Tensile Modulus(1000 hr,in Glycol,130℃) Retention of Tensile Modulus(1000 hr,in Glycol,130℃) |
% | ISO 527-2 | |
拉伸强度的保留率 Retention rate of tensile strength |
|||
1000 hr,in Glycol,130℃ 1000 hr,in Glycol,130℃ |
% | ISO 527-2 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 D2类型 |
【新闻资讯】查看全部
陶熙™将于2月6日正式在中国市场启用!
2018-01-24 1月23日,陶氏宣布道康宁并入陶氏后推出的新品牌――陶熙™将于2月6日在中国市场正式启用! 陶氏新品牌――陶熙™ 陶氏消费品解决方案全球商务副总裁 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |