牌号简介 About |
---|
D/W 213是一种从原始PTFE中剥离的薄膜,它已经在一侧用萘钠(D/W212)蚀刻,之后底漆被应用于增强与弹性体和压敏粘合剂的结合。这种表面处理可以使聚四氟乙烯(PTFE)与其他材料的粘合力非常差。底漆可由最终用户指定,也可由Dewal推荐用于特定用途。钠蚀聚四氟乙烯的主要应用包括与弹性体粘合以产生叠层隔膜,以及在聚四氟乙烯压敏带生产中应用压敏粘合剂。 D/W 213 is a film skived from virgin PTFE, that has been etched on one side with Sodium Naphthalene (D/W212) after which a primer has been applied to enhance bonding to elastomers and pressure sensitive adhesives. This surface treatment allows the PTFE which normally exhibits very poor adhesion to be bonded to other materials. The primer may be specified by the end user or may be recommended by DeWAL for specific applications. The primary applications for sodium etched PTFE involve bonding to elastomers to produce laminated diaphragms, as well as the applicaton of pressure sensitive adhesives in the production of PTFE pressure sensitive tapes. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Thickness Thickness |
50.8 到 1020 | nm | |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
MD,屈服 MD, yield |
27.6 | MPa | ASTM D882 |
拉伸应变 Tensile strain |
|||
MD,断裂 MD, fracture |
300 | % | ASTM D882 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
连续使用温度 Continuous use temperature |
260 | ℃ | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Core ID Core ID |
7.62 | cm | |
Maximum Roll OD Maximum Roll OD |
mm | ||
Width Width |
mm |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
我国快递包装实践回收率不到10%
2017-03-14 2016年,我国快递业务量突破300亿件、同比增长53%,继续稳居世界第一,预计到2020年中国快递业务量将达到700亿件。与之相对应的一项数据则令人担忧,有关调查显示,快递业中快递包装实际回收率不到10%,绝大部分被直接送进垃圾场填埋。 “我国作为世界第一快递大国,提高快递包装回收率,推广和使用绿色包装,推进快递企业向绿色物流转变,十分必要且迫在眉睫。”黑龙江省齐齐哈尔市龙江县环卫处工人王月清代表从事环卫工作16年。因每天和各种各样的垃圾打交道,此次参会,她带来了“关于实 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |