牌号简介 About |
---|
CALIBRE™ 603-3 是一种接枝聚碳酸酯树脂,专用于异型材、波纹板和非常复杂的多壁层片材的挤出加工。CALIBRE™ 603-3 具有非常高的熔体强度,可以有效地对具有高达7层或者更多层的最复杂的多壁层结构进行定型,也可以有效地对复杂的异型材和波纹板进行定型。CALIBRE™ 603-3 含有紫外线吸收剂,但是请注意室外用板材还需要一层吸收紫外线的保护层。在这里推荐使用CALIBRE™ 320UV 与其共挤出,制造出一个厚度为50 µm的保护层。 主要特性: 熔体强度非常高 抗冲击性能好 应用领域: 复杂的多壁层片材 异型材 CALIBRE™ 603-3 is a branched polycarbonate resin specially designed for extrusion of profiles, corrugated sheet and very complex multi-wall sheet. CALIBRE™ 603-3 offers a very high melt strength to calibrate effectively the most complex multi-wall sheet structures, such as a seven wall sheet or more, and to calibrate effectively complex profiles and corrugated sheet. CALIBRE™ 603-3 contains a UV absorber additive, but note that sheets for outdoor applications also require a protective UV-absorbing cap layer. It is recommended to coextrude a 50 µm thick cap layer, using CALIBRE™ 320UV. Main Characteristics: Very high melt strength Good impact resistance Applications: Complex multi-wall sheet Profiles |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.20 | g/cm³ | ASTM D792 |
收缩率 Shrinkage rate |
|||
MD MD |
0.60 | % | ASTM D995 |
吸水率 Water absorption rate |
|||
23℃,24hr 23℃,24hr |
0.15 | % | ASTM D570 |
23℃,50% RH 23℃,50% RH |
0.32 | % | ASTM D570 |
熔体质量流动速率 Melt Flow Rate |
|||
300℃,1.20kg 300℃,1.20kg |
3.0 | g/10min | ASTM D1238 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
23℃ 23℃ |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂,23℃ Fracture, 23 ℃ |
% | ASTM D638 | |
拉伸模量 Tensile modulus |
|||
23℃ 23℃ |
MPa | ASTM D638 | |
弯曲强度 bending strength |
|||
23℃ 23℃ |
MPa | ASTM D790 | |
弯曲模量 Bending modulus |
|||
23℃ 23℃ |
MPa | ASTM D790 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
折射率 Refractive index |
ASTM D542 | ||
透光率 Transmittance |
% | ASTM D1003 | |
雾 度 μm Haze μ M |
% | ASTM D1003 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,退火 0.45 MPa, annealed |
℃ | ASTM D648 | |
1.8 MPa,退火 1.8 MPa, annealed |
℃ | ASTM D648 | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
维卡软化温度 Vicat Softening Temp |
|||
|
℃ | ASTM D1525 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻 Volumetric resistance |
Ω.cm | ASTM D257 | |
绝缘强度 Insulation strength |
|||
|
KV/mm | ASTM D149 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
|||
1.50mm 1.50mm |
UL-94 | ||
3.00mm 3.00mm |
UL-94 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 0.079 in/min |
3 这个额定值并非为了反映这种或任何其他材料在实际起火条件下造成的危险。 |
4 This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
【新闻资讯】查看全部
无机硅化物分会部署明年工作
2021-12-26 搜料网资讯: 近日,2021中国无机盐工业协会无机硅化物分会分会长和专家委员会(扩大)工作会议暨碳达峰碳中和发展论坛在江苏无锡举行,会上明确了2022年专家委员会工作内容。 一是 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |