牌号简介 About |
---|
Viton® A-361C是一种固化A族二聚物,设计用于需要更好的金属粘合性的零件的注射和转移成型,以及氟弹性体典型的流体和耐热特性。中等粘度水平Viton® A-361C还允许零件满意的压缩成型。Viton® A-361C的特点是:中等粘度水平(与Viton A-201C/Viton A-401C相比),完全预复合降低固化水平,加入金属粘合促进剂,改进加工,增加模具流动,减少模具污染,更容易脱模,改进脱模“热裂”,与标准工业底漆AP良好的金属粘合。O形圈和垫圈、气门杆和曲轴密封件(以及其他需要Viton A系列流体和耐热性的粘合零件)的压缩、传递和注塑成型 Viton® A-361C is an incorporated cure A-family dipolymer designed for the injection and transfer molding of parts requiring better metal adhesion along with the fluid and heat resistance characteristics typical of fluoroelastomers. The moderate viscosity level of Viton® A-361C also allows for satisfactory compression molding of parts. Features of Viton® A-361C are: Intermediate viscosity level (when compared with Viton® A-201C/Viton® A-401C) Fully precompounded reduced curative level Incorporated metal adhesion promoter Improved processing increased mold flow easier mold release with less mold fouling improved demolding "hot tear" Good metal bonding with standard industrial primers Applications Compression, transfer, and injection molding of: O-rings and gaskets Valve stem and crankshaft seals (and other bonded parts requiring fluid and heat resistance of the A-family of Viton®) |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.82 | g/cm³ | ASTM D792 |
门尼粘度 Mooney viscosity |
|||
ML 1+10,121℃ ML 1+10,121℃ |
63 | MU | ASTM D1646 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
ASTM D2240 | ||
邵氏 A,23℃ Shore A, 23 ℃ |
78 | ASTM D2240 | |
邵氏 A,23℃ Shore A, 23 ℃ 2 |
76 | ASTM D2240 | |
邵氏 A,23℃ Shore A, 23 ℃ 3 |
79 | ASTM D2240 | |
邵氏 A,23℃ Shore A, 23 ℃ 4 |
ASTM D2240 | ||
邵氏 A,23℃ Shore A, 23 ℃ 5 |
ASTM D2240 | ||
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
ASTM D412 | ||
100% 应变,23℃ 100% strain, 23 ℃ 6 |
MPa | ASTM D412 | |
100% 应变,23℃ 100% strain, 23 ℃ 7 |
MPa | ASTM D412 | |
100% 应变,23℃ 100% strain, 23 ℃ 8 |
MPa | ASTM D412 | |
100% 应变,23℃ 100% strain, 23 ℃ 9 |
MPa | ASTM D412 | |
100% 应变,23℃ 100% strain, 23 ℃ 10 |
MPa | ASTM D412 | |
拉伸强度 tensile strength |
ASTM D412 | ||
屈服,23℃ Yield, 23 ℃ 6 |
MPa | ASTM D412 | |
屈服,23℃ Yield, 23 ℃ 7 |
MPa | ASTM D412 | |
屈服,23℃ Yield, 23 ℃ 8 |
MPa | ASTM D412 | |
屈服,23℃ Yield, 23 ℃ 9 |
MPa | ASTM D412 | |
屈服,23℃ Yield, 23 ℃ 10 |
MPa | ASTM D412 | |
拉伸应变 Tensile strain |
ASTM D412 | ||
断裂,23℃ Fracture, 23 ℃ 6 |
% | ASTM D412 | |
断裂,23℃ Fracture, 23 ℃ 7 |
% | ASTM D412 | |
断裂,23℃ Fracture, 23 ℃ 8 |
% | ASTM D412 | |
断裂,23℃ Fracture, 23 ℃ 9 |
% | ASTM D412 | |
断裂,23℃ Fracture, 23 ℃ 10 |
% | ASTM D412 | |
压缩形变 Compression deformation |
|||
23℃,70 hr 23℃,70 hr |
% | ASTM D395B | |
200℃,70 hr 200℃,70 hr |
% | ASTM D395 | |
232℃,70 hr 232℃,70 hr |
% | ASTM D395B |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 20 in/min |
3 20 in/min, 老化 70 hr 在 392°F |
4 20 in/min, 老化 168 hr 在 392°F |
5 20 in/min, 老化 24 hr 在 450°F |
6 20 in/min, 老化 70 hr 在 450°F |
7 老化 70 hr 在 392°F |
8 老化 168 hr 在 392°F |
9 老化 24 hr 在 450°F |
10 老化 70 hr 在 450°F |
【新闻资讯】查看全部
我国研制出可快速降解水中抗生素的新型催化剂
2022-01-08 搜料网资讯: 抗生素滥用导致的生态环境和生物安全问题,已引起广泛关注。近期,中科院合肥物质科学研究院智能机械研究所刘锦淮课题组孔令涛研究团队设计出一种新颖可控的催化 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |