牌号简介 About |
---|
中粘度阻燃聚酰胺6级(V-2);无PBDE SCHULAMID® 6 MV 14 FR 4 K1681 (Dry) Medium viscosity flame-retardant Polyamide 6 grade (V-2); without PBDE SCHULAMID® 6 MV 14 FR 4 K1681 Nylon Unfilled PBDE-Free, GWIT |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.26 | g/cm³ | ISO 1183/A |
粘数 Viscosity number |
145 | cm³/g | ISO 307 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179/1eA | ||
-30℃ -30℃ |
3.0 | kJ/m² | ISO 179/1eA |
23℃ 23℃ |
4.0 | kJ/m² | ISO 179/1eA |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
ISO 179/1eU | ||
-30℃ -30℃ |
48 | kJ/m² | ISO 179/1eU |
23℃ 23℃ |
kJ/m² | ISO 179/1eU | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/Af | |
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/Bf | |
维卡软化温度 Vicat Softening Temp |
|||
A50 A50 |
℃ | ISO 306/A50 | |
B50 B50 |
℃ | ISO 306 | |
球压测试 Ball pressure test |
|||
200℃ 200℃ |
IEC 60695-10-2 | ||
相对温度指数 Relative temperature index |
|||
电气性能 Electrical performance |
UL 746 | ||
阻燃等级(0.38 mm) Flame retardant grade (0.38 mm) |
℃ | UL 746 | |
0.75 mm 0.75 mm |
℃ | UL 746 | |
1.5 mm 1.5 mm |
℃ | UL 746 | |
3.0 mm 3.0 mm |
℃ | UL 746 | |
强度机械性能 Strength mechanical performance |
UL 746 | ||
阻燃等级(0.38 mm) Flame retardant grade (0.38 mm) |
℃ | UL 746 | |
0.75 mm 0.75 mm |
℃ | UL 746 | |
1.5 mm 1.5 mm |
℃ | UL 746 | |
3.0 mm 3.0 mm |
℃ | UL 746 | |
冲击机械性能 Impact mechanical performance |
UL 746 | ||
阻燃等级(0.38 mm) Flame retardant grade (0.38 mm) |
℃ | UL 746 | |
0.75 mm 0.75 mm |
℃ | UL 746 | |
1.5 mm 1.5 mm |
℃ | UL 746 | |
3.0 mm 3.0 mm |
℃ | UL 746 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
相比漏电起痕指数 Compared to the leakage tracing index |
V | IEC 60112 | |
高电弧燃烧指数(HAI) High Arc Burning Index (HAI) |
UL 746 | ||
阻燃等级(0.38 mm) Flame retardant grade (0.38 mm) |
UL 746 | ||
0.75 mm 0.75 mm |
UL 746 | ||
1.5 mm 1.5 mm |
UL 746 | ||
3.0 mm 3.0 mm |
UL 746 | ||
热丝引燃 Hot wire ignition |
|||
HWI HWI |
UL 746 | ||
阻燃等级(0.38 mm) Flame retardant grade (0.38 mm) |
UL 746 | ||
0.75 mm 0.75 mm |
UL 746 | ||
1.5 mm 1.5 mm |
UL 746 | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
燃烧速率 Burning rate |
ISO 3795 | ||
0.38 mm,自动灭火 0.380 mm, Self-Extinguishing |
mm/min | ISO 3795 | |
0.75 mm,自动灭火 0.75 mm, automatic fire extinguishing |
mm/min | ISO 3795 | |
1.5 mm,自动灭火 1.5mm, automatic fire extinguishing |
mm/min | ISO 3795 | |
3.0 mm,自动灭火 3.0 mm, automatic fire extinguishing |
mm/min | ISO 3795 | |
阻燃等级 Flame retardant level |
UL 94 | ||
0.38 mm 0.38 mm |
UL 94 | ||
0.75 mm 0.75 mm |
UL 94 | ||
1.50 mm 1.50 mm |
UL 94 | ||
3.00 mm 3.00 mm |
UL 94 | ||
可燃性等级 Flammability level |
IEC 60695-11-10, -20 | ||
阻燃等级(0.38 mm) Flame retardant grade (0.38 mm) |
IEC 60695-11-10, -20 | ||
0.75 mm 0.75 mm |
IEC 60695-11-10, -20 | ||
1.5 mm 1.5 mm |
IEC 60695-11-10, -20 | ||
3.0 mm 3.0 mm |
IEC 60695-11-10, -20 | ||
灼热丝可燃性指数 Glowing wire flammability index |
IEC 60695-2-12 | ||
0.38 mm 0.38 mm |
℃ | IEC 60695-2-12 | |
0.75 mm 0.75 mm |
℃ | IEC 60695-2-12 | |
1.5 mm 1.5 mm |
℃ | IEC 60695-2-12 | |
3.0 mm 3.0 mm |
℃ | IEC 60695-2-12 | |
灼热丝起燃温度 Igniting temperature of the hot wire |
IEC 60695-2-13 | ||
0.38 mm 0.38 mm |
℃ | IEC 60695-2-13 | |
0.75 mm 0.75 mm |
℃ | IEC 60695-2-13 | |
1.5 mm 1.5 mm |
℃ | IEC 60695-2-13 | |
3 mm 3 mm |
℃ | IEC 60695-2-13 | |
极限氧指数 Extreme oxygen index |
% | ISO 4589-2 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
MPa | ISO 527-2/1A/1 | |
拉伸强度 tensile strength |
|||
屈服 yield |
MPa | ISO 527-2/1A/50 | |
拉伸应变 Tensile strain |
|||
屈服 yield |
% | ISO 527-2/1A/50 | |
球压硬度 Ball hardness |
|||
H358/30 H358/30 |
MPa | ISO 2039-1 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
模具构造的设计,这些特点无视不得哟~
2017-05-11 ⑴抽气孔的设计: 抽真空成型的抽气孔设计是模具设计的关键,抽气孔应位于片材最后贴模的地方,如凹模成型时在凹模底部四周及有凹陷的地方,凸模成型时在凸模的底部四周等,具体情况视成型塑件的形状和大小而定。 对于轮廓复杂的塑件,抽气孔应集中,对于大的平面塑件,抽气孔需要均布。孔间距可视塑件大小而定,对于小型塑件,孔间距可在20~30mm之是选取,大型塑件应适当增加距离。 通常成型塑料流动性好,成型温度高,则抽气孔小些;坏料板材厚度大,则抽气孔大些;坯 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |