牌号简介 About |
---|
Royalcast2505结合了工程塑料的刚性和良好的物理性能平衡。当用MBCA或Ethacure 300固化时,Royalcast 2505生成82-85 Shore D材料,非常适合多种最终用途应用。作为一种可浇铸材料,Royalcast 2505是在通常用于己烷/振动烷(聚氨酯)露天浇铸操作的条件下加工的。这使得铸模工可以使用低成本的模具来生产全系列的刚性零件,包括:体积小、运行大、截面厚或不同的零件,另外,由于Royalcast 2505具有适度的拆卸时间,模具周转率可以很高,从而最大限度地减少模具和直接人工成本。 ROYALCAST 2505 combines the rigidity of an engineering plastic with an excellent balance of physical properties. When cured with MBCA or Ethacure® 300, ROYALCAST 2505 yields an 82-85 Shore D material that is well suited for numerous end use applications. As a castable material, ROYALCAST 2505 is processed under conditions typically used in an Adiprene/Vibrathane (polyurethane) open casting operation. This allows the molder to use low cost tooling to produce a full range of rigid parts, including: Short volume runs Large parts Parts with thick or varied cross-sections Additionally, because ROYALCAST 2505 has a moderate demold time, mold turnabout can be high, thus minimizing tooling and direct labor costs. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.21 | g/cm³ | ASTM D792 |
收缩率 Shrinkage rate |
|||
MD MD |
1.3 | % | 内部方法 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
20℃ 20℃ |
110 | J/m | ASTM D256 |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
20℃ 20℃ |
2700 | J/m | ASTM D256 |
Uncured Properties Uncured Properties |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
颜色 colour |
|||
-- -- 2 |
Clear/Transparent | ||
-- -- 3 |
|||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
ASTM D2240 | ||
邵氏 D,20℃ Shore D, 20 ℃ |
ASTM D2240 | ||
邵氏 D,70℃ Shore D, 70 ℃ |
ASTM D2240 | ||
邵氏 D,100℃ Shore D, 100 ℃ |
ASTM D2240 | ||
洛氏硬度 Rockwell hardness |
|||
R 级,20℃ R-grade, 20 ℃ |
ASTM D785 | ||
拉伸强度 tensile strength |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D638 | |
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
弯曲强度 bending strength |
MPa | ASTM D790 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
热固组件 Thermosetting components |
|||
树脂 resin |
|||
硬化法 Hardening method |
|||
储存稳定性 storage stability |
min | ||
脱模时间 stripping time |
min | ||
后固化时间 Post curing time |
|||
116℃ 116℃ |
hr |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 MBCA Cure |
3 Royalcast 2505 |
【新闻资讯】查看全部
石大胜华拟在日本设立新公司
2021-09-04 搜料网资讯: 近日,石大胜华对外宣布,公司董事会审议通过了《关于成立日本全资孙公司的议案》,为实施公司发展战略,拟用全资子公司石大胜华(香港)有限公司作为投资主体,成 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |