牌号简介 About |
---|
AOC的Vipel F701系列树脂是高分子量、两段间苯二甲酸、不饱和聚酯树脂,具有湿润、固化和处理通用树脂的特点。他们有极好的保质期,是理想的纤维缠绕和喷涂。下面列出了几种选定的树脂,包括高粘度基础树脂,Vipel F701-FHG-00。耐腐蚀AOC的Vipel F701系列树脂在与无机和有机酸接触时提供优异的耐腐蚀性。许多石油产品,如煤油、加热油和原油,耐溶剂性已得到现场验证。请参阅AOC的“耐腐蚀树脂指南”,了解耐腐蚀信息或关于树脂是否适合任何特定化学环境的问题。用途广泛,适用于手工制作、喷涂、纤维缠绕等多种制造方法。 AOC's Vipel F701 Series resins are high molecular weight, two-stage isophthalic, unsaturated polyester resin with the wet out, cure and handling characteristics of general purpose resins. They have an excellent shelf life and are ideal for filament winding and spray-up. A few selected resins are listed below including the high viscosity base resin, Vipel F701-FHG-00. BENEFITS Corrosion resistance AOC's Vipel F701 series resins provide excellent corrosion resistance when used in contact with inorganic and organic acids. Solvent resistance is field-proven for many petroleum products such as kerosene, heating oil and crude oils. Refer to AOC's "Corrosion Resistant Resin Guide" for corrosion resistance information or for questions regarding suitability of a resin to any particular chemical environment contact AOC. Versatile Suitable for various fabricating methods such as hand lay-up, spray-up and filament winding. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
苯乙烯含量 styrene content |
47 | % | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
107 | ℃ | ASTM D648 |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Gel to Peak Gel to Peak |
37.0 | min | |
放热峰值 exothermic peak |
82 | ℃ | |
触变指数 Thixotropic index 2 |
2.00 | ||
Uncured Properties Uncured Properties |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
g/cm³ | ||
粘度 viscosity |
|||
布络克菲尔德 LV Brookfield LV |
Pa·s | ||
胶凝时间 Gelation time |
min | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
巴氏硬度 Babbitt hardness |
ASTM D2583 | ||
拉伸模量 Tensile modulus |
MPa | ASTM D638 | |
拉伸强度 tensile strength |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D638 | |
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
弯曲强度 bending strength |
MPa | ASTM D790 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 6/60 rpm |
【新闻资讯】查看全部
巴陵石化3月启动厂区内卸车站台优化改造
2018-11-23 巴陵石化炼油部苯乙烯装置2012年建成投产,苯乙烯产品主要内供并有部分外销。原产品充装站台在厂区外依山修建,经多年使用,出现地面鼓包、龙门架轻微移位等现象,存在山体滑坡隐患,而且站台充装产品类别单一,不利于出厂产品集中管理,采用敞开式装车设施也不能满足新的环保标准。 对此,该部今年3月启动厂区内装车站台优化改造,使之具备充装苯乙烯产品的条件。改造中,该部运用持续改进工具进行分析统筹,对改造过程全面把关。该部制定苯乙烯装车设施投用详细方案,严格检查苯乙烯产品的进料管线、储罐、 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |