四氟乙烯/丙烯(TFE/P)橡胶,90-98°IRHD。四氟乙烯和丙烯的共聚物。使用AFLAS FA-100H配制。AFLAS是旭化成玻璃的注册商标。对酸、蒸汽、热水、盐水、油、润滑剂和酸性油气(H2S)具有优异的抵抗力。可抵抗所有类型的液压流体(包括烷基芳基磷酸酯)、所有制动流体(乙二醇、矿物和硅酮基)、胺腐蚀抑制剂和添加剂包装。抗爆炸性减压、高压和气体(即二氧化碳)起泡。 Tetrafluoroethylene/Propylene (TFE/P) Rubber, 90-98°IRHD. Copolymer of tetrafluoroethylene and propylene. Formulated using Aflas® FA-100H. Aflas® is a registered trademark of Asahi Glass. Excellent resistance to acids, steam, hot water, brine, oils, lubricants and sour oil and gas (H2S). Resistant to all types of hydraulic fluids (including alkyl-aryl phosphate esters), all brake fluids (glycol, mineral and silicone base), amine corrosion inhibitors and additive packages. Resistant to explosive decompression, high pressure and gas (i.e. CO2 ) blistering. |
技术参数 Technical Data | |||
---|---|---|---|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
IRHD 硬度 IRHD hardness |
93 | ASTM D1415 , ISO 48 | |
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
屈服 yield |
17.6 | MPa | ASTM D412 , ISO 37 |
拉伸应变 Tensile strain |
|||
断裂 fracture |
120 | % | ASTM D412,ISO 37 |
压缩形变 Compression deformation |
|||
200℃,24 hr 200℃,24 hr |
24 | % | ASTM D395B |
200℃,24 hr 200℃,24 hr 2 |
24 | % | ISO 815 |
老化性能 Aging performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
空气中拉伸强度的变化率 The rate of change in tensile strength in air |
|||
200℃,72 hr 200℃,72 hr |
% | ASTM D412 , ISO 37 | |
空气中极限伸长率的变化率 The rate of change in ultimate elongation in air |
|||
200℃,72 hr 200℃,72 hr |
% | ASTM D412 , ISO 37 | |
空气中 IRHD 硬度的变化率 The change rate of IRHD hardness in the air |
|||
200℃,72 hr 200℃,72 hr |
ASTM D573 , ISO 188 | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
最高工作温度 Maximum operating temperature |
|||
-- -- |
℃ | ||
Intermittent,short term Intermittent,short term |
℃ | ||
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Low Temperature Resistance Low Temperature Resistance |
|||
Non-brittle for 3 minutes Non-brittle for 3 minutes |
℃ | ASTM D2137 | |
Non-brittle for 3 minutes Non-brittle for 3 minutes |
℃ | ISO R812 | |
TR10 TR10 |
℃ | ASTM D1329 | |
TR10 TR10 |
℃ | ISO 2921 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 类型 B |
【新闻资讯】查看全部
Science Advance:旧瓶新酒催化剂新用处
2016-06-23 垃圾是放错位置的资源,如何将大量废弃而且不易降解的聚乙烯塑料利用起来是摆在人类面前的重大环境课题。利用现有催化剂,科学家找到了一条聚乙烯变废为宝的新途径…… 牛奶盒,玩具,食品杂货袋,泡沫包装,机械零件,甚至是人工髋关节……每年,人类使用聚乙烯制品的重量达1亿吨左右,比任何其他塑料都多。与此同时造成的废弃物也很多,据统计,废弃聚乙烯约占全球垃圾填埋场中塑料总量的60%,并且难以分解。 近日,中科院上海有机所与美国加利福尼亚大学的研究者将已知的催化剂重新改造, |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |