牌号简介 About |
---|
符合ISO 1043-1的材料规范:聚丙烯热稳定聚丙烯,用40%重量%长的玻璃纤维加固。纤维与聚丙烯基体发生化学耦合。冲击性能得到增强。球是圆柱形的,通常也包括10 mm长的嵌入纤维。Celstran成型件具有高强度、高刚度、高热变形等优异的力学性能。由于部件中内置了纤维骨架,因此在高温和低温下缺口冲击强度会增加。长纤维增强能显著降低蠕变。模制品的各向同性收缩使翘曲最小化。通过注射成型,可以制造出具有高再现性的复杂零件。应用领域:汽车功能/结构件 Material code according to ISO 1043-1: PP Heat stabilized polypropylene reinforced with 40 weight percent long glass fibers. The fibers are chemically coupled to the polypropylene matrix. The impact properties are enhanced. The pellets are cylindrical and normally as well as the embedded fibers 10 mm long. Parts molded of CELSTRAN have outstanding mechanical properties such as high strength and stiffness combined with high heat deflection. The notched impact strength is increased at elevated and low temperatures due to the fiber skeleton built in the parts. The long fiber reinforcement reduces creep significantly. The very isotropic shrinkage in the molded parts minimizes the warpage. Complex parts can be manufactured with high reproducibility by injection molding. Application field: Functional/structural parts for automotive |
产品描述 Product Description
厂家:美国塞拉尼斯 Celanese
类别:PP PP not specified
用途:汽车领域的应用;
颜色:黑色
加工条件:注射成型 Injection Molding
性能特点: 热稳定性好; 化学耦合; 机械强度好; 耐低温冲击; 低翘曲性; 冲击性能好; 韧性好; Good Rigidity,Low warping,Good flexibility,High impact resistance,Chemical coupling,low-temperature impact resistance,Heat Stabilized
填料:玻璃纤维 40
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.22 | g/cm³ | ISO 1183 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
-- -- |
8200 | MPa | ISO 527-2/1A/1 |
80℃ 80℃ |
5200 | MPa | ISO 527-2/1A |
拉伸强度 tensile strength |
|||
断裂 fracture |
110 | MPa | ISO 527-2/1A/5 |
80℃ 80℃ |
60.0 | MPa | ISO 527-2/1A |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ISO 527-2/1A/5 | |
断裂,80℃ Fracture, 80 ℃ |
% | ISO 527-2/1A | |
弯曲模量 Bending modulus |
ISO 178 | ||
23℃ 23℃ |
MPa | ISO 178 | |
80℃ 80℃ |
MPa | ISO 178 | |
弯曲强度 bending strength |
ISO 178 | ||
23℃ 23℃ |
MPa | ISO 178 | |
80℃ 80℃ |
MPa | ISO 178 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179/1eA | ||
-30℃ -30℃ |
kJ/m² | ISO 179/1eA | |
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
ISO 179/1eU | ||
-30℃ -30℃ |
kJ/m² | ISO 179/1eU | |
23℃ 23℃ |
kJ/m² | ISO 179/1eU | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
8.0 MPa,未退火 8.0 MPa, unannealed |
℃ | ISO 75-2/C | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
熔融温度 Melting temperature 2 |
℃ | ISO 11357-3 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 10°C/min |
【新闻资讯】查看全部
中国石化:预计2021年上半年净利润为365亿元~385亿元
2021-07-02 搜料网资讯: 7月1日,中国石化发布2021年半年度业绩预告:2021年上半年归属于母公司股东的净利润预计人民币365亿元到385亿元,较2020年同期实现扭亏为盈,增长约人民币594亿元到614亿 |
中国石化:预计2021年上半年净利润为365亿元~385亿元 搜料网资讯:7月1日,中国石化发布2021年半年度业绩预告:2021年上半年归属于母公司股东的净利润预计人民币365亿元到385亿元,较2020年同期实现扭亏为盈,增长约人民币594亿元到614亿元,较2019年同期预计将增加16.6%到23%。 公告显示,2020年年初,受新冠肺炎疫情和油价暴跌的双重影响,全球石油石化产品消费大幅萎缩,中国石化生产经营受到较大冲击,2020年上半年经营亏损。 2021年上半年,中国石化经营业绩同比大幅改善,较2019年同期也实现较好增长,主要是由于:今年以来,全球疫情形势整体好转,国际原油价格震荡上行,国内统筹疫情防控和经济社会发展的成果持续巩固,石油石化产品市场需求较快恢复。公司抓住机遇,降低采购成本,优化生产经营,大力拓市扩销,推进产业链整体增效,各业务板块经营状况均有较大改善,取得良好的经营业绩。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
价格走势图
开始时间:
结束时间:
材料厂家:
【牌号齐全,内容全面】
全网共2500+项牌号+上游原料单体+原油价格,最长可追溯近20年价格行情
【精准,及时,权威!】
专业团队挖掘行情信息,第一时间发布行情
抱歉!该牌号暂无认证数据。
免责声明:参考价格是搜料网根据网络大数据拟合分析的结果,仅供参考。实际成交价取决但不限于以下因素:下单时间,付款方式,交货方式,数量,税费,色号,产地,项目信息。
抱歉!暂无数据。
抱歉!暂无数据。