牌号简介 About |
---|
SABIC LLDPE 218B SABIC® LLDPE 218B是一种丁烯线性低密度聚乙烯树脂,通常设计用于易于加工,并专门配制用于铸膜挤出高温下的最佳热稳定性。SABIC® LLDPE 218B铸膜具有良好的光学性能、韧性、抗穿刺性和撕裂强度。应用SABIC® LLDPE 218B树脂通常用于手和托盘拉伸包装。本产品不适用于任何医药/医疗应用,也不得用于任何医药/医疗应用。SABIC LLDPE 218B产品说明218B是线性低密度聚乙烯级产品,旨在提供易于加工的性能,并专门配制,以在生产铸膜过程中使用的高加工温度下实现最佳热稳定性。使用该树脂生产的薄膜具有优良的光学性能、良好的抗穿刺性和撕裂强度。典型应用:粘膜、手动和颗粒包裹用拉伸膜、熔融压花膜和其他通用应用。 SABIC® LLDPE 218B SABIC® LLDPE 218B is a butene linear low density polyethylene resin typically designed for easy processing and specially formulated for optimum thermal stability at high temperatures used in cast film extrusion. Cast films produced from SABIC® LLDPE 218B exhibit good optical properties, improved toughness, puncture resistance and tear strength. Application SABIC® LLDPE 218B resin is typically used for hand and pallet stretch wrap. This product is not intended for and must not be used in any pharmaceutical/medical applications. SABIC® LLDPE 218B Product Description 218B is Linear Low Density Polyethylene grade designed to provide easy processability and specially formulated for optimum thermal stability at high processing temperatures used during production of Cast films. Films produced using this resin gives excellent optical properties, good puncture resistance and tear strength. Typical Applications Cling film, Stretch films for manual and pellet wrap, melt embossed films and other general purpose applications. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.918 | g/cm³ | ISO 1183/A |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
2.0 | g/10min | ISO 1133 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Elastic Recovery(铸造薄膜,20.0 µm) Elastic Recovery (cast film, 20.0 µ m) |
53 | % | ASTM D5459 |
Protrusion Puncture Resistance - 铸造薄膜(20.0 µm) Corrosion Function Resistance - Cast thin film (20.0 µ m) |
2.20 | J | ASTM D5748 |
Retention Force(60 sec,20.0 µm) Retention Force(60 sec,20.0 µm) 1 |
970 | g | |
Stress Retention(铸造薄膜,20.0 µm) Stress Retention (cast film, 20.0 µ m) |
% | ASTM D5459 | |
Ultimate Pre(stretch Level 铸造薄膜,20.0 µm) Ultimate Pre-stretch Level - Cast Film (20.0 µm) |
% | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306/A | |
熔融温度 Melting temperature |
|||
DSC DSC |
℃ | 内部方法 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
45°,20 µm,铸造薄膜 45 °, 20 µ m, cast thin film |
ASTM D2457 | ||
雾度 Haze |
|||
20.0 µm,铸造薄膜 20.0 µ m, cast thin film |
% | ASTM D1003A | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
落锤冲击 Drop hammer impact |
|||
20.0 µm,铸造薄膜 20.0 µ m, cast thin film |
J/cm | ISO 7765-2 | |
Peel Cling Peel Cling 2 |
ASTM D5458 | ||
0% pre-stretch:20.0 µm 0% pre-stretch:20.0 µm |
g/2.5 cm | ||
200% pre-stretch:20.0 µm 200% pre-stretch:20.0 µm |
g/2.5 cm | ||
撕裂强度 tear strength 3 |
|||
TD,20 µm TD,20 µm 3 |
kN/m | ISO 6383-2 | |
memo_intro memo_intro |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Cast Film |
【新闻资讯】查看全部
万华化学上半年净利暴增近四倍,主要产品量价齐升推动业绩大增
2021-07-30 搜料网资讯: 7月29日,万华化学发布半年报称,上半年实现营业收入676.57亿元,同比增118.91%;营业利润161.41亿元,同比增382.54%;净利润135.30亿元,同比增377.21%。 公司报告称,上半年烟 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |