牌号简介 About |
---|
DAI-EL G-671 DAI-EL™ G-671是一种中等粘度固化的三元共聚物,适用于转移、压缩和注射成型应用。G-671在低温柔韧性和耐化学性之间提供了良好的平衡。DAI-EL G-671 DAI-EL™ G-671是一种含氟弹性体,包含偏二氟乙烯/四氟乙烯/六氟丙烯的三元共聚物,含有固化剂(双酚AF)和固化促进剂。该材料的TR10为-20°C,多元醇固化型氟弹性体具有最大的低温密封性能。 DAI-EL® G-671 DAI-EL® G-671 is a bisphenol cure incorporated terpolymer designed for transfer and compression molding applications. G-671 combines good chemical and solvent resistance with good low temperature properties. Typical Applications: O-rings, gaskets, seals DAI-EL® G-671 DAI-EL G-671 is a fluoroelastomer comprising terpolymer of vinylidenefluoride/tetrafluoroethylene/hexafluoropropylene, contains a curing agent (bisphenol AF) and cure accelerator. The TR10 of this material is -20°C and the maximum low-temperature sealing performance is available among polyol cure based fluoroelastomers. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.80 到 1.84 | g/cm³ | |
门尼粘度 Mooney viscosity |
|||
ML 1+10,121℃ ML 1+10,121℃ |
35 | MU | |
氟含量 Fluorine content |
67 | % | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 A,25℃ Shore A, 25 ℃ |
71 | ||
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
屈服,25℃ Yield, 25 ℃ |
16.0 | MPa | |
100% 应变,25℃ 100% strain, 25 ℃ |
MPa | ||
拉伸应变 Tensile strain |
|||
断裂,25℃ Fracture, 25 ℃ |
% | ||
撕裂强度 tear strength |
|||
25℃ 25℃ |
kN/m | ||
压缩形变 Compression deformation |
|||
25℃,70 hr 25℃,70 hr |
% | ||
100℃,70 hr 100℃,70 hr |
% | ||
175℃,70 hr 175℃,70 hr |
% | ||
200℃,70 hr 200℃,70 hr |
% | ||
老化性能 Aging performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
空气中拉伸强度的变化率 The rate of change in tensile strength in air |
|||
230℃,70 hr 230℃,70 hr |
% | ||
空气中极限伸长率的变化率 The rate of change in ultimate elongation in air |
|||
230℃,70 hr 230℃,70 hr |
% | ||
空气中硬度计硬度的变化率 The rate of change in hardness of a hardness tester in the air |
|||
邵氏 A,230℃,70 hr Shore A, 230 ℃, 70 hr |
|||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
脆化温度 Embrittlement temperature |
℃ | ||
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
固化温度 curing temperature |
℃ | ||
固化时间 Curing time |
|||
Curelastometer Curelastometer |
min | ||
Gehman Torsion Test Gehman Torsion Test |
|||
T10 T10 |
℃ | ||
T2 T2 |
℃ | ||
TR Test TR Test |
|||
TR10 TR10 |
℃ | ||
TR70 TR70 |
℃ |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 23°C |
3 25% compression |
【新闻资讯】查看全部
美军拟开发3D打印无人机技术 行业使用获打破
2016-02-26 据媒体报道,美国陆军打算开发一项新技术,用3D打印方式在战场现场制造小型无人驾驶飞行器,旨在以最短时间响应前线士兵的不同需求,同时降低装备成本。战地无人机制造系统包括设计单元和制造单元,使用计算机辅助设计软件,按照士兵的任务需求个性化定制多种无人机。从士兵发出请求至无人机投入使用,整个过程不超过24小时。 业内人士认为,技术的改变让3D打印成为了目前世界上最令人关注的技术之一。市场研究公司IDC的数据显示,2015年全球3D打印支出接近110亿美元。IDC预测,到2019年 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |