牌号简介 About |
---|
Amodel® AT-1125 HS聚邻苯二甲酰胺(ppa)是一种钢化、热稳定的25%玻璃纤维增强树脂,设计用于需要硬度、良好尺寸稳定性、耐化学性和延展性的应用。该树脂具有较高的热变形温度和较高的弯曲模量,比未经强化的玻璃纤维增强聚甲基丙烯酸甲酯具有更大的拉伸延伸率。典型应用包括轴承、轴承保持架/保持架、轴承座、化学加工设备部件、电机架、运动设备、草坪和花园设备以及需要压配合或卡配合装配的部件。黑色:AT-1125 HS BK 324 Amodel® AT-1125 HS polyphthalamide (PPA) is a toughened, heat stabilized 25% glass reinforced resin, designed as a cost effective solution for applications requiring stiffness, good dimensional stability, chemical resistance and ductility. This resin has a high heat deflection temperature and a high flexural modulus, with greater tensile elongation than untoughened glass-reinforced PPA. Typical applications include bearings, bearing retainers/cages, housings, chemical processing equipment components, motor frames, sporting equipment, lawn and garden equipment and components that require press-fit or snap-fit assembly. Black: AT-1125 HS BK 324 |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.35 | g/cm³ | ISO 1183/A |
收缩率 Shrinkage rate |
|||
TD TD |
0.60 | % | ASTM D955 |
MD MD |
0.40 | % | ASTM D955 |
吸水率 Water absorption rate |
|||
24hr 24hr |
0.20 | % | ASTM D570 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
8480 | MPa | ASTM D638 |
拉伸模量 Tensile modulus |
MPa | ISO 527-2 | |
拉伸强度 tensile strength |
|||
断裂 fracture |
MPa | ISO 527-2 | |
断裂 fracture |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ISO 527-2 | |
断裂 fracture |
% | ASTM D638 | |
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
弯曲模量 Bending modulus |
MPa | ISO 178 | |
弯曲强度 bending strength |
MPa | ISO 178 | |
屈服 yield |
MPa | ASTM D790 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
kJ/m² | ISO 179-1eA | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
J/m | ASTM D256 | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
kJ/m² | ISO 180-1A | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
J/m | ASTM D256 | |
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments |
ASTM D3763 | ||
Energy as Maximum Load Energy as Maximum Load 2 |
J | ASTM D3763 | |
Energy at Maximum Load Energy at Maximum Load 3 |
J | ASTM D3763 | |
Total Energy Total Energy |
J | ASTM D3763 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ASTM D648 | |
熔融峰值温度 Melting peak temperature |
℃ | ASTM D3418 | |
熔融温度 Melting temperature |
℃ | ISO 11357-3 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Maximum Load: 230 lb (1020 N) |
3 最大负载:280 lb (1240 N) |
【新闻资讯】查看全部
安徽省公示第二批化工园区名单
2022-09-22 扫描上图二维码,可以免费下载 搜料 APP 9月18日,据报道, 安徽省发改委官网发布了安徽省化工园区名单(第二批)公示,申报的园区为临泉经济开发区化工产业集中区、宁国港口产业 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |