牌号简介 About |
---|
不热封胶带基膜无涂层再生纤维素膜(RCF),机械强度高。已开发出400/450/500支,用作制造胶带的基础。 Non Heat-Sealable Tape Base Films Uncoated regenerated cellulose film (RCF) with high mechanical strength. 400/450/500PUT have been developed for use as a base for the manufacture of adhesive tapes. |
技术参数 Technical Data | |||
---|---|---|---|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
摩擦系数 friction coefficient |
ASTM D1894 | ||
与自身 - 动态 With oneself - dynamic |
0.50 | ASTM D1894 | |
与自身 - 静态 With oneself - static |
0.70 | ASTM D1894 | |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
28 | µm | |
割线模量 Secant modulus |
ASTM D882 | ||
1% 正割,MD:28 µm 1% secant, MD: 28 µ m |
> 3000 | MPa | ASTM D882 |
1% 正割,TD:28 µm 1% secant, TD: 28 µ m |
> 1500 | MPa | ASTM D882 |
拉伸强度 tensile strength |
ASTM D882 | ||
MD,屈服,28 µm MD, yield, 28 µ m |
MPa | ASTM D882 | |
TD,屈服,28 µm TD, yield, 28 µ m |
MPa | ASTM D882 | |
拉伸应变 Tensile strain |
ASTM D882 | ||
MD,断裂,28 µm MD, fracture, 28 µ m |
% | ASTM D882 | |
TD,断裂,28 µm TD, fracture, 28 µ m |
% | ASTM D882 | |
透氧度(湿)(23℃,28 µm,0.0% RH) Oxygen permeability (wet) (23 ℃, 28 µ m, 0.0% RH) |
cm³/m²/24 hr | ASTM F1927 | |
用量 dosage |
|||
27.7 µm 27.7 µm |
m²/kg | 内部方法 |
备注 | |||
---|---|---|---|
暂无数据 |
【新闻资讯】查看全部
宏观视角下PE价格走势浅析
2021-04-19 搜料网资讯: 宏观分析方法是大宗商品价格分析方法之一。由于宏观是微观的集合,宏观指标中譬如GDP等具有滞后性,非及时性的特点,因此GDP只能是作为长期参考。宏观分析更多从宏 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |