牌号简介 About |
---|
Vibrathane B875是一种MDI端接的聚醚基预聚物。预聚物是室温下的液体。当用1,4丁二醇固化时,Vibrathane B875生成95肖氏硬度的聚氨酯。 VIBRATHANE B875 is an MDI-terminated, polyether based prepolymer. The prepolymer is a liquid at room temperature. VIBRATHANE B875 yields a 95 Shore hardness urethane when cured with 1,4 Butanediol. |
技术参数 Technical Data | |||
---|---|---|---|
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
ASTM D412 | ||
100% 应变 100% strain |
8.69 | MPa | ASTM D412 |
200% 应变 200% strain |
10.3 | MPa | ASTM D412 |
300% 应变 300% strain |
11.8 | MPa | ASTM D412 |
拉伸强度 tensile strength |
16.5 | MPa | ASTM D412 |
拉伸应变 Tensile strain |
|||
断裂 fracture |
480 | % | ASTM D412 |
撕裂强度 tear strength |
|||
-- -- 2 |
kN/m | ASTM D624 | |
开裂 cracking |
kN/m | ASTM D470 | |
压缩形变 Compression deformation |
|||
80℃,22 hr 80℃,22 hr |
% | ASTM D395 | |
巴肖氏弹性 Basho's elasticity |
% | ASTM D2632 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
储存稳定性 storage stability |
min | ||
后固化时间 Post curing time |
|||
115℃ 115℃ |
hr | ||
Uncured Properties Uncured Properties |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
固化时间 Curing time |
|||
82℃ 82℃ |
hr | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 A Shaw's A |
ASTM D2240 | ||
压缩强度 compressive strength |
ASTM D695 | ||
5% 应变 5% strain |
MPa | ASTM D695 | |
10% 应变 10% strain |
MPa | ASTM D695 | |
15% 应变 15% strain |
MPa | ASTM D695 | |
20% 应变 20% strain |
MPa | ASTM D695 | |
25% 应变 25% strain |
MPa | ASTM D695 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 C 模具 |
【新闻资讯】查看全部
Dymax戴马斯首发用于可穿戴医疗设备的结构胶粘剂
2021-11-05 搜料网资讯: Dymax戴马斯,快速光固化材料和设备的制造商,为迎合高速发展的医疗可穿戴设备市场,及满足需要控制皮肤致敏性潜在风险的制造商需求,近期推出2000-MW系列可穿戴医疗 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |