牌号简介 About |
---|
EMERGE™ PC 8702 高级树脂是一种20%玻璃纤维增强的阻燃聚碳酸酯树脂。这种树脂不含溴、氯或者磷酸盐添加剂。这种树脂可以满足德国标准DIN VDE-0472/第 815部分 (1989) 有关卤素的要求。这是一种带有脱模剂系统的中等流动性的PC树脂,应用于注塑模塑。 应用领域: 信息技术设备 电器零部件 其他结构件/内部零部件 EMERGE™ PC 8702-5 Advanced Resin is an ignition-resistant, 20% glass reinforced, polycarbonate resin. This resin contains no bromine, chlorine, or phosphate additives. The resin is designed to meet the German norm DIN VDE-0472 on halogens. It is a medium flow PC resin with a mold release system, intended for injection molding applications. EMERGE ™ PC 8702-5 has a UL 94 V-0 rating at 1.5 mm, 5VA rating at 3.0 mm and V2 rating at 0.75 mm. Applications: Information technology equipment Electrical parts Other structural/internal parts |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.33 | g/cm³ | ISO 1183/B |
熔体质量流动速率 Melt Flow Rate |
|||
300℃,1.20kg 300℃,1.20kg |
5.0 | g/10min | ISO 1133 |
收缩率 Shrinkage rate |
0.20 到 0.40 | % | ISO 294-4 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
6000 | MPa | ISO 527-2/50 |
拉伸强度 tensile strength |
ISO 527-2/50 | ||
屈服 yield |
100 | MPa | ISO 527-2/50 |
断裂 fracture |
MPa | ISO 527-2/50 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ISO 527-2/50 | |
弯曲模量 Bending modulus |
MPa | ISO 178 | |
弯曲强度 bending strength |
MPa | ISO 178 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
kJ/m² | ISO 180-A | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
0.45 MPa,退火 0.45 MPa, annealed |
℃ | ISO 75-2/B | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
1.8 MPa,退火 1.8 MPa, annealed |
℃ | ISO 75-2/A | |
维卡软化温度 Vicat Softening Temp |
|||
B50 B50 |
℃ | ISO 306 | |
球压温度 Ball pressure temperature |
℃ | IEC 60335-1 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
ISO 11359-2 | ||
MD MD |
1/℃ | ISO 11359-2 | |
TD TD |
1/℃ | ISO 11359-2 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | IEC 60093 | |
体积电阻率 Volume resistivity |
ohms·cm | IEC 60093 | |
介电强度 Dielectric strength |
|||
1.6 mm 1.6 mm |
kV/mm | IEC 60243-1 | |
介电常数 Dielectric constant |
IEC 60250 | ||
1.60 mm,10 Hz 1.60 mm,10 Hz |
IEC 60250 | ||
1.60 mm,1 MHz 1.60 mm,1 MHz |
IEC 60250 | ||
耗散因数 Dissipation factor |
IEC 60250 | ||
10 Hz 10 Hz |
IEC 60250 | ||
100 Hz 100 Hz |
IEC 60250 | ||
1 MHz 1 MHz |
IEC 60250 | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
0.75 mm 0.75 mm 3 |
UL 94 | ||
1.50 mm 1.50 mm 4 |
UL 94 | ||
3.00 mm 3.00 mm 4 |
UL 94 | ||
灼热丝可燃性指数 Glowing wire flammability index |
IEC 60695-2-12 | ||
1.0 mm 1.0 mm 4 |
℃ | IEC 60695-2-12 | |
2.0 mm 2.0 mm 3 |
℃ | IEC 60695-2-12 | |
3.0 mm 3.0 mm 3 |
℃ | IEC 60695-2-12 | |
灼热丝起燃温度 Igniting temperature of the hot wire 3 |
IEC 60695-2-13 | ||
1 mm 1 mm |
℃ | IEC 60695-2-13 | |
2 mm 2 mm |
℃ | IEC 60695-2-13 | |
3 mm 3 mm |
℃ | IEC 60695-2-13 | |
极限氧指数 Extreme oxygen index 3 |
% | ISO 4589-2 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
3 这个额定值并非为了反映这种或任何其他材料在实际起火条件下造成的危险。 |
【新闻资讯】查看全部
杜邦Zytel激光透明无卤尼龙树脂获第56届R&D 100大奖
2018-12-13 近日, 杜邦 交通运输和先进材料事业部生产的无卤尼龙树脂 ZytelHTN LTFR52G30NH BL662 被评为第55届年度RD100大奖。 关于 ZytelHTN 高性能聚酰胺 ZytelHTN LTFR52G30NH BL662 是一种30%玻纤增强,可激光 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |