牌号简介 About |
---|
LNP* Lubricomp* Compound PFL34是基于含有玻璃纤维和PETF的尼龙6树脂的化合物。此材料的突出性能是自润滑性。 |
技术参数 Technical Data | |||
---|---|---|---|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
断裂,I型,5 mm/min Fracture, Type I, 5 mm/min |
140 | MPa | ASTM D638 |
断裂,5 mm/min Fracture, 5 mm/min |
138 | MPa | ISO 527 |
断裂 fracture |
130 | MPa | ASTM D638 |
拉伸应变 Tensile strain |
|||
断裂,I型,5 mm/min Fracture, Type I, 5 mm/min |
3.2 | % | ASTM D638 |
断裂,5 mm/min Fracture, 5 mm/min |
3.2 | % | ISO 527 |
断裂 fracture |
% | ASTM D638 | |
弯曲强度 bending strength |
kgf/cm² | ASTM D 790 | |
断裂,1.30 mm/min,50 mm跨度 Fracture, 1.30 mm/min, 50 mm span |
MPa | ASTM D790 | |
屈服,1.30 mm/min,50 mm跨度 Yield, 1.30 mm/min, 50 mm span |
MPa | ASTM D790 | |
弯曲模量 Bending modulus |
kgf/cm² | ASTM D 790 | |
2 mm/mim 2 mm/mim |
MPa | ISO 178 | |
1.30 mm/min,50 mm跨距 1.3 mm/min,50mm跨距 |
MPa | ASTM D790 | |
拉伸模量 Tensile modulus |
|||
5 mm/min 5 mm/min |
MPa | ASTM D638 | |
50 mm/min 50 mm/min |
MPa | ASTM D638 | |
1 mm/min 1 mm/min |
MPa | ISO 527 | |
弯曲强度 bending strength |
MPa | ISO 178 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
23℃ 23℃ |
J/m | ASTM D4812 | |
23℃ 23℃ |
J/m | ASTM D4812 | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
J/m | ASTM D256 | |
23℃ 23℃ |
J/m | ASTM D256 | |
仪表冲击总能量 Total energy of instrument impact |
cm-kgf | ASTM D 3763 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火,3.2 mm 1.8 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
1.8 MPa,未退火,3.2 mm 1.8 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
0.45 MPa,未退火,3.2 mm 0.45 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
TD:-30~30℃ TD:-30~30℃ |
1/℃ | ASTM D696 | |
MD:-30~30℃ MD:-30~30℃ |
1/℃ | ASTM D696 | |
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
g/cm³ | ASTM D792 | |
吸水率 Water absorption rate |
|||
24hr,50% RH 24hr,50% RH |
% | ASTM D570 | |
收缩率 Shrinkage rate |
|||
MD:24 hrs MD:24 hrs |
% | ASTM D955 | |
MD:24 hrs MD:24 hrs |
% | ASTM D955 | |
MD:24 hrs MD:24 hrs |
% | ASTM D955 | |
垫圈磨损因素 Factors of gasket wear |
10^-10 in^5-min/ft-lb-hr | ASTM D 3702 Modified | |
环磨损因素 Environmental wear factors |
10^-10 in^5-min/ft-lb-hr | ASTM D 3702 Modified | |
动摩擦因数 Dynamic friction coefficient |
- | ASTM D 3702 Modified | |
静摩擦因数 Static friction coefficient |
- | ASTM D 3702 Modified |
备注 | |||
---|---|---|---|
暂无数据 |
【新闻资讯】查看全部
大连商品交易所3日PVC行情表
2021-11-03 搜料网资讯: 大连商品交易所 日行情表 查询日期: 20 21 年 11 月 3 日 本月第 3 个交易日 本年第 201 个交易日 商品 交割月份 开盘价 最高价 最低价 收盘价 前结算价 结算价 涨跌 涨跌 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |