牌号简介 About |
---|
UmaPET COMH的主要特点是高阻隔金属化薄膜,在平面上用等离子体进行金属化处理,另一面进行电晕处理。它表现出良好的阻隔性能以及良好的金属与薄膜的粘合强度/粘合力。它具有优良的机械性能、抗曲裂性和光泽。应用UmaPET COMH在软包装应用中用作夹层阻挡层,要求层压板具有良好的阻挡层和良好的粘合强度。在糖果、奶粉、谷类食品、零食、薯条、挤压食品、茶等的层压板中用作阻挡层的典型用途。 |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
收缩率 Shrinkage rate |
ASTM D1204 | ||
MD:150℃,0.01 mm,30 min MD:150℃,0.01 mm,30 min |
2.5 | % | |
MD:150℃,0.012 mm,30 min MD:150℃,0.012 mm,30 min |
2.5 | % | |
MD:150℃,0.015 mm,30 min MD:150℃,0.015 mm,30 min |
2.5 | % | |
MD:150℃,0.023 mm,30 min MD:150℃,0.023 mm,30 min |
2.5 | % | |
TD:150℃,0.01 mm,30 min TD:150℃,0.01 mm,30 min |
0.40 | % | |
TD:150℃,0.012 mm,30 min TD:150℃,0.012 mm,30 min |
% | ||
TD:150℃,0.015 mm,30 min TD:150℃,0.015 mm,30 min |
% | ||
TD:150℃,0.023 mm,30 min TD:150℃,0.023 mm,30 min |
% | ||
表面张力 surface tension |
ASTM D2578 | ||
Corona Side:10.0 µm Corona Side:10.0 µm |
mN/m | ||
Corona Side:12.0 µm Corona Side:12.0 µm |
mN/m | ||
Corona Side:15.0 µm Corona Side:15.0 µm |
mN/m | ||
Corona Side:23.0 µm Corona Side:23.0 µm |
mN/m | ||
Metallized side:10.0 µm Metallized side:10.0 µm |
mN/m | ||
Metallized side:12.0 µm Metallized side:12.0 µm |
mN/m | ||
Metallized side:15.0 µm Metallized side:15.0 µm |
mN/m | ||
Metallized side:23.0 µm Metallized side:23.0 µm |
mN/m | ||
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
µm | ||
薄膜厚度 film thickness |
|||
拉伸强度 tensile strength |
ASTM D882 | ||
MD,断裂,10 µm MD, fracture, 10 µ m |
MPa | ||
MD,断裂,12 µm MD, fracture, 12 µ m |
MPa | ||
MD,断裂,15 µm MD, fracture, 15 µ m |
MPa | ||
MD,断裂,23 µm MD, fracture, 23 µ m |
MPa | ||
TD,断裂,10 µm TD, fracture, 10 µ m |
MPa | ||
TD,断裂,12 µm TD, fracture, 12 µ m |
MPa | ||
TD,断裂,15 µm TD, fracture, 15 µ m |
MPa | ||
TD,断裂,23 µm TD, fracture, 23 µ m |
MPa | ||
拉伸应变 Tensile strain |
ASTM D882 | ||
MD,断裂,10 µm MD, fracture, 10 µ m |
% | ||
MD,断裂,12 µm MD, fracture, 12 µ m |
% | ||
MD,断裂,15 µm MD, fracture, 15 µ m |
% | ||
MD,断裂,23 µm MD, fracture, 23 µ m |
% | ||
TD,断裂,10 µm TD, fracture, 10 µ m |
% | ||
TD,断裂,12 µm TD, fracture, 12 µ m |
% | ||
TD,断裂,15 µm TD, fracture, 15 µ m |
% | ||
TD,断裂,23 µm TD, fracture, 23 µ m |
% | ||
透氧率 Oxygen permeability 1 |
ASTM D3985 | ||
23℃,10 µm 23℃,10 µm |
cm³/m²/24 hr | ||
23℃,12 µm 23℃,12 µm |
cm³/m²/24 hr | ||
23℃,15 µm 23℃,15 µm |
cm³/m²/24 hr | ||
23℃,23 µm 23℃,23 µm |
cm³/m²/24 hr | ||
水蒸气透过性 Water vapor permeability |
ASTM F1249 | ||
-- -- 2 |
g/m²/24 hr | ||
-- -- 3 |
g/m²/24 hr | ||
-- -- 4 |
g/m²/24 hr | ||
-- -- 5 |
g/m²/24 hr | ||
用量 dosage |
内部方法 | ||
10.0 µm 10.0 µm |
m²/kg | ||
12.0 µm 12.0 µm |
m²/kg | ||
15.0 µm 15.0 µm |
m²/kg | ||
23.0 µm 23.0 µm |
m²/kg | ||
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Optical Density Optical Density |
内部方法 | ||
10.0 µm 10.0 µm |
% | ||
12.0 µm 12.0 µm |
% | ||
15.0 µm 15.0 µm |
% | ||
23.0 µm 23.0 µm |
% |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 0%RH |
3 37.8°C, 90%RH, 15 µm |
4 37.8°C, 90%RH, 23 µm |
5 37.8°C, 90%RH, 10 µm |
6 37.8°C, 90%RH, 12 µm |
【新闻资讯】查看全部
持续下跌1个半月 BOPP价格仍有下调空间
2021-12-08 搜料网资讯: 自10月14日起,双向拉伸聚丙烯薄膜(BOPP)已持续下跌1个半月之久。截至12月1日,BOPP厚光膜华东市场成交价格为1.12万~1.15万元(吨价,下同),累计下滑3150元,跌幅达21.72%,局 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |