牌号简介 About |
---|
乐泰EA E-40exp是一种双组分自流平环氧树脂,专为封装电机而设计。一旦混合,双组分环氧树脂在室温下固化。它可以被封装成水平体积,并将流动以填充空隙。典型应用包括封装电线导管,以将电机与周围环境隔离。 Loctite® EA E-40EXP™ is a two component, self-leveling epoxy designed for potting electric motors. Once mixed, the two component epoxy cures at room temperature. It can be potted into horizontal volumes and will flow to fill the voids. Typical applications include the potting of wire conduits to isolate the electrical motor from the surrounding environment. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
吸水率 Water absorption rate |
|||
23℃,24hr 23℃,24hr |
0.23 | % | ISO 62 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
玻璃化转变温度 Glass transition temperature |
52.0 | ℃ | ASTM E1640 |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD MD |
|||
< 52℃ < 52℃ |
2.6E-5 | cm/cm/℃ | |
> 52℃ > 52℃ |
1.5E-4 | cm/cm/℃ | |
导热系数 Thermal conductivity coefficient |
0.25 | W/m/K | ASTM E1530 |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
介电强度 Dielectric strength |
kV/mm | IEC 60243-1 | |
介电常数 Dielectric constant |
|||
1 kHz 1 kHz |
|||
10 kHz 10 kHz |
|||
100 kHz 100 kHz |
|||
1 MHz 1 MHz |
|||
耗散因数 Dissipation factor |
|||
1 kHz 1 kHz |
|||
10 kHz 10 kHz |
|||
100 kHz 100 kHz |
|||
1 MHz 1 MHz |
|||
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积收缩 Volume contraction |
% | ISO 1675 | |
Uncured Properties Uncured Properties |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
颜色 colour |
|||
-- -- 2 |
|||
-- -- 3 |
|||
重量混合比(PBW) Weight Mix Ratio (PBW) |
|||
Resin Resin |
|||
Hardener Hardener |
|||
体积混合比(PBV) Volume Mixing Ratio (PBV) |
|||
Resin Resin |
|||
Hardener Hardener |
|||
密度 Density |
|||
25℃ 25℃ 2 |
g/cm³ | ||
25℃ 25℃ 4 |
g/cm³ | ||
粘度 viscosity |
|||
布络克菲尔德 RVT,25℃ 25°C, Brookfield RVT 5 5 |
Pa·s | ||
布络克菲尔德,25℃ Brookfield, 25 ℃ 6 |
Pa·s | ||
胶凝时间 Gelation time |
|||
22℃ 22℃ |
min | ||
Tack Free Time Tack Free Time |
min | ||
Cured Properties Cured Properties |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
搭接剪切强度 lap shear strength |
MPa | ISO 4587 | |
Linear Shrinkage Linear Shrinkage |
% | ISO 1675 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
ISO 868 | ||
拉伸模量 Tensile modulus |
MPa | ISO 527-2 | |
拉伸强度 tensile strength |
MPa | ISO 527-2 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ISO 527-2 |
备注 |
---|
2、Hardener |
3、Resin |
4、Mixed |
5、Hardener, Spindle 14, speed 10 rpm |
6、Resin, Spindle 14, speed 10 rpm |
【新闻资讯】查看全部
卫星化学2#40万吨/年聚乙烯装置计划三季度投产
2022-03-11 3月9日晚,卫星化学发布了旗下子公司连云港石化有限公司在建项目最新进展。 C2项目二期:预计2022年中期试生产 2017年,卫星化学股份有限公司(以下简称公司)在国家规划的七大石 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |