牌号简介 About |
---|
永久植入物用可植入级聚醚醚酮树脂VESTAKEEP® i5 G是一种天然有色、高粘度聚醚醚酮(PEEK),专门为长期植入医疗器械设计。经验证的生物相容性,超高纯度和扩展的质量措施使Vestakeep I级材料成为永久性植入物的最佳选择。对于VESTAKEEP® i5 G,根据ISO 10993-1关于永久性组织/骨接触的建议和USP第六类,对生物相容性进行了测试。VESTAKEEP® i5 G符合ASTM F2026“外科植入物应用的聚醚醚酮(PEEK)聚合物的标准规范”。 Implantable grade polyether ether ketone resin for permanent implants VESTAKEEP® i5 G is a natural colored, very high viscosity polyether ether ketone (PEEK) that is especially designed for long term implantable medical devices. Proven biocompatibility The extra high purity and extended quality measures make VESTAKEEP® i-grade materials an excellent choice for permanent implants. For VESTAKEEP® i5 G, biocompatibility has been tested following ISO 10993-1 recommendations for permanent tissue/bone contact and USP Class VI. VESTAKEEP® i5 G complies to ASTM F2026 "Standard Specification for Polyetheretherketone (PEEK) Polymers for Surgical Implant Applications". |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.30 | g/cm³ | ISO 1183 |
熔体体积流动速率 Melt Volume Rate |
|||
380℃,5 kg 380℃,5 kg |
7.00 | cm³/10min | ISO 1133 |
吸水率 Water absorption rate |
|||
饱和,23℃ Saturation, 23 ℃ |
0.40 | % | |
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
0.12 | % | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
3400 | MPa | ISO 527-2 |
拉伸强度 tensile strength |
|||
屈服 yield |
MPa | ||
断裂 fracture |
MPa | ||
拉伸应变 Tensile strain |
|||
屈服 yield |
% | ||
断裂 fracture |
% | ||
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
-30℃,完全断裂 -30 ℃, completely fractured |
kJ/m² | ||
23℃,完全断裂 23 ℃, completely fractured |
kJ/m² | ||
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
|||
-30℃ -30℃ |
|||
23℃ 23℃ |
|||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
玻璃化转变温度 Glass transition temperature |
|||
-- -- 2 |
℃ | ||
-- -- 3 |
℃ | ||
维卡软化温度 Vicat Softening Temp |
|||
-- -- |
℃ | ISO 306/A | |
-- -- |
℃ | ISO 306/B | |
熔融温度 Melting temperature 4 |
℃ | ISO 11357-3 | |
结晶点 Crystallization point |
℃ | ISO 11357 |
备注 |
---|
2、2nd heating, onset |
3、2nd heating, midpoint |
4、2nd heating |
【新闻资讯】查看全部 ![]()
油价一度触及两年新高!美油收盘微跌0.1%,终结二连涨走势
2021-05-06 搜料网资讯: 国际油价周三收盘涨跌不一,其中美国原油期货价格小幅下跌,终结了此前两个交易日的连续上涨走势,盘中一度触及两年新高,原因是欧洲和美国重新开放经济促使原油 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |