牌号简介 About |
---|
Queo™ 7001LA是一种乙烯基辛烯-1弹性体,使用茂金属催化剂在溶液聚合过程中生产。应用示范的应用包括:在层压低坐密封层和柔性阻隔膜粘膜表面保护膜无卤阻燃化合物降噪,例如汽车应用高强度柔性膜挤压涂层添加剂Queo™ 7001LA含有少量的加工稳定剂。特殊功能Queo™ 7001LA经过优化可提供:在薄膜、挤压和成型应用中与其他聚烯烃多功能混合。高清晰度高柔韧性和表面柔软性塑料与弹性体性能的桥接低熔点 Queo 7001LA is an ethylene based octene-1 elastomer, produced in a solution polymerisation process using a metallocene catalyst. Applications Demonstrated applications include: Low SIT Seal layers in lamination and flexible barrier films Cling film Surface protection film Halogen free flame retardant compounds Noise reduction in e.g. automotive applications High strength flexible films Extrusion coating Additives Queo 7001LA contains a low amount of processing stabilizers. Special Features Queo 7001LA is optimised to deliver: Versatile blending with other polyolefins in film, extrusion and moulding applications. High clarity High flexibility and surface softness Bridging of plastic and elastomeric properties Low peak melting point |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.870 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
1.0 | g/10min | ISO 1133 |
门尼粘度 Mooney viscosity |
|||
ML 1+4,100℃ ML 1+4,100℃ |
30 | MU | DIN 53523 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
始封温度 Initial sealing temperature |
< 60.0 | ℃ | 内部方法 |
落锤冲击 Drop hammer impact |
> 392.3 | kN/m | ISO 7765-1 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
ISO 180 | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
脆化温度 Embrittlement temperature |
℃ | ISO 974 | |
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306/A | |
熔融温度 Melting temperature |
℃ | ISO 11357-3 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
ISO 2813 | ||
雾度 Haze |
% | ASTM D1003 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 A Shaw's A |
|||
邵氏 D Shaw's D |
|||
拉伸强度 tensile strength |
|||
断裂 fracture |
MPa | ISO 527-2 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ISO 527-2 | |
弯曲模量 Bending modulus |
MPa | ISO 178 |
备注 | |||
---|---|---|---|
暂无数据 |
【新闻资讯】查看全部
多地塑料制品运用量不降反增 “限塑令”不能只限不罚
2017-07-13 生活中不仅仅超市和农贸市场是塑料制品的“重灾区”,随着快递行业和外卖行业迅猛发展,塑料包装的消耗也不断增多 塑料袋成本仅仅几分钱,但销售价达到几毛钱,可以给超市带来一笔不小的利润 “要塑料袋吗?”近日,《经济日报》记者在北京西四环某大型超市购物结账时发现,收银员每接待一位顾客的开场白都是这句话。除了采购少量物品,或自带小拖车的顾客没有要塑料袋,大部分顾客都会回答:“来一个。” 大概很多人已经对前几年的“限塑令”没有印象了。2007年12月31 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |