SABIC® SUPEER™ 8118L是一种通过nexlene技术生产的乙烯-辛烯共聚物。它在广泛的通用和高性能LLDPE吹膜应用中表现良好,具有良好的加工性能。SABIC® SUPEER™ 8118L的典型应用包括层压膜、冷冻袋、液体袋、重型袋、工业衬垫、农业薄膜、拉伸罩、表面保护膜。本产品不适用于任何医药/医疗应用,也不得用于任何医药/医疗应用。 SABIC® SUPEER™ 8118L is an ethylene-octene copolymer produced via Nexlene™ Technology. It performs well in a wide range of general purpose and high performance LLDPE blown film applications and has good processablity. Application Typical applications for SABIC® SUPEER™ 8118L are lamination film, frozen bags, liquid pouches, heavy duty bags, industrial liner, agriculture film, stretch hood, surface protective film. This product is not intended for and must not be used in any pharmaceutical/medical applications. |
产品描述 Product Description
厂家:沙特沙伯基础 SABIC
类别:mLLDPE mLLDPE
用途:重包装袋;衬里;工业应用;袋子;通用;层压板;吹膜;拉伸缠绕;农业应用;
加工条件:吹塑薄膜
性能特点: 抗结块性; 共聚物; 高光滑性; 辛烯共聚单体; 低密度; 易加工; Excellent Processability,Smoothness,High anti-blocking,Low density,Octene copolymer,Copolymer
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.918 | g/cm³ | ASTM D1505 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
1.1 | g/10min | ASTM D1238 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
50 | µm | |
割线模量 Secant modulus |
|||
1% 正割,MD:50 µm,吹塑薄膜 1% secant, MD: 50 µ m, blow molded film |
140 | MPa | |
1% 正割,TD:50 µm,吹塑薄膜 1% secant, TD: 50 µ m, blow molded film |
156 | MPa | |
拉伸强度 tensile strength |
|||
MD,屈服,50 µm,吹塑薄膜 MD, yield, 50 µ m, blow molded film |
MPa | ||
TD,屈服,50 µm,吹塑薄膜 TD, yield, 50 µ m, blow molded film |
MPa | ||
MD,断裂,50 µm,吹塑薄膜 MD, fracture, 50 µ m, blow molded film |
MPa | ||
TD,断裂,50 µm,吹塑薄膜 TD, fracture, 50 µ m, blow molded film |
MPa | ||
拉伸应变 Tensile strain |
|||
MD,断裂,50 µm,吹塑薄膜 MD, fracture, 50 µ m, blow molded film |
% | ||
TD,断裂,50 µm,吹塑薄膜 TD, fracture, 50 µ m, blow molded film |
% | ||
落锤冲击 Drop hammer impact 2 |
|||
50 µm,吹塑薄膜 50 µ m, blow molded film 2 |
g | ASTM D1709 | |
埃尔曼多夫抗撕强度 Elmandorf tear strength |
|||
MD:50 µm,吹塑薄膜 MD: 50 µ m, blow molded film |
g | ||
TD:50 µm,吹塑薄膜 TD: 50 µ m, blow molded film |
g | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
熔融温度 Melting temperature |
℃ | 内部方法 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
雾度 Haze |
|||
50 µm,吹塑薄膜 50 µ m, blow molded film |
% | ASTM D1003 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Blown Film Melt Temperature Blown Film Melt Temperature |
℃ | ||
Blow(up Ratio) Blow(up Ratio) |
|||
|
备注 |
---|
2、F50 |
【新闻资讯】查看全部
榆能化完成年方案的75.45%
2018-11-26 图为施工现场 截至10月底,榆能化公司一期填平补齐工程项目今年投资9.05亿元,完成年计划的75.45%。该项目以煤、天然气为原料,建设年产180万 |
榆能化完成年方案的75.45% 图为施工现场 截至10月底,榆能化公司一期填平补齐工程项目今年投资9.05亿元,完成年计划的75.45%。该项目以煤、天然气为原料,建设年产180万吨甲醇、60万吨甲醇制烯烃、40万吨聚丙烯和30万吨低密度聚乙烯/乙烯-醋酸乙烯聚酯(LDPE/EVA)一体化装置,计划2020年建成试车。 来源:中国化工报 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
价格走势图
开始时间:
结束时间:
材料厂家:
【牌号齐全,内容全面】
全网共2500+项牌号+上游原料单体+原油价格,最长可追溯近20年价格行情
【精准,及时,权威!】
专业团队挖掘行情信息,第一时间发布行情
抱歉!该牌号暂无认证数据。
免责声明:参考价格是搜料网根据网络大数据拟合分析的结果,仅供参考。实际成交价取决但不限于以下因素:下单时间,付款方式,交货方式,数量,税费,色号,产地,项目信息。
抱歉!暂无数据。
抱歉!暂无数据。