牌号简介 About |
---|
12X01是HP-LLDPE吹塑薄膜级,具有优异的加工性能和良好的薄膜强度,与低凝胶相结合。特点超丁烯优良的加工性能良好的薄膜强度低凝胶应用吹塑薄膜等级 12X01 is a HP-LLDPE blown film grade of excellent processability and good film strength combined with low gels. Features Superbutene Excellent processability Good film strength Low gels Application Blown film grade |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.912 | g/cm³ | ASTM D1505 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
0.95 | g/10min | ASTM D1238 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
25.0 到 180 | µm | |
测试 test |
25 | µm | |
割线模量 Secant modulus |
|||
2% 正割,MD:25 µm,吹塑薄膜 2% secant, MD: 25 µ m, blow molded film |
190 | MPa | |
2% 正割,TD:25 µm,吹塑薄膜 2% secant, TD: 25 µ m, blow molded film |
MPa | ||
拉伸强度 tensile strength |
|||
MD,屈服,25 µm,吹塑薄膜 MD, yield, 25 µ m, blow molded film |
MPa | ||
TD,屈服,25 µm,吹塑薄膜 TD, yield, 25 µ m, blow molded film |
MPa | ||
MD,断裂,25 µm,吹塑薄膜 MD, fracture, 25 µ m, blow molded film |
MPa | ||
TD,断裂,25 µm,吹塑薄膜 TD, fracture, 25 µ m, blow molded film |
MPa | ||
拉伸应变 Tensile strain |
|||
MD,断裂,25 µm,吹塑薄膜 MD, fracture, 25 µ m, blow molded film |
% | ||
TD,断裂,25 µm,吹塑薄膜 TD, fracture, 25 µ m, blow molded film |
% | ||
落锤冲击 Drop hammer impact |
|||
25 µm,吹塑薄膜 25 µ m, blow molded film |
g | ASTM D1709 | |
埃尔曼多夫抗撕强度 Elmandorf tear strength |
|||
MD:25 µm,吹塑薄膜 MD: 25 µ m, blow molded film |
g | ||
TD:25 µm,吹塑薄膜 TD: 25 µ m, blow molded film |
g | ||
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
45°,25 µm,吹塑薄膜 45 °, 25 µ m, blow molded film |
ASTM D2457 | ||
雾度 Haze |
|||
25 µm,吹塑薄膜 25 µ m, blow molded film |
% | ASTM D1003 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Blow(up Ratio) Blow(up Ratio) |
备注 | |||
---|---|---|---|
暂无数据 |
【新闻资讯】查看全部
万华北京车用聚氨酯零碎料成功使用于日系豪华SUV
2016-03-14 万华化学(北京)有限公司汽车研发平台积极致力于车用聚氨酯材料的开发和应用研究,目前,最新开发的聚氨酯声学系统料Waneflex® 531D/Wannate® 8223成功应用于日系高端SUV车型。 日系高端品牌最新推出的豪华SUV车型,追求卓越的驾乘感受,将至臻品质与豪华品位延伸到每一处精深细节之中。这与万华北京“从PU开始,创造美好生活”的理念不谋而合。全新的技术突破,优质的聚氨酯泡沫解决方案,实现了优良的吸音、减震、降噪效果,为驾乘者提供安静舒适的车内空间。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |