牌号简介 About |
---|
Quadrant EPP Semitron® CMP LL5是一种热塑性聚酯产品,。 它,在北美洲或拉丁美洲有供货。 主要特性为:阻燃/额定火焰。 Quadrant EPP Semitron® CMP LL5 is a Thermoplastic Polyester product. It is available in Latin America or North America. Primary characteristic: flame rated. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.44 | g/cm³ | ASTM D792 |
吸水率 Water absorption rate |
|||
24hr 24hr |
6.0E-4 | % | |
饱和 saturated |
4.7E-3 | % | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
21 | J/m | ASTM D256 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
82.2 | ℃ | ASTM D648 |
熔融峰值温度 Melting peak temperature |
℃ | ASTM D3418 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:-40~300℃ MD:-40~300℃ |
1/℃ | ASTM E831 | |
导热系数 Thermal conductivity coefficient |
W/m/K | ||
最高使用温度 Maximum operating temperature |
|||
Air,Continuous Air,Continuous |
℃ | ||
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | ASTM D257 | |
介电常数 Dielectric constant |
|||
1 MHz 1 MHz |
ESD S11.11 | ||
耗散因数 Dissipation factor |
|||
1 MHz 1 MHz |
ASTM D150 | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
|||
3.20 mm 3.20 mm |
UL 94 | ||
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Collected Volatile Condensable Material Collected Volatile Condensable Material |
% | ||
离子杂质 Ionic impurities |
|||
Fe(Iron) Fe(Iron) |
ppm | ||
K(Potassium) K(Potassium) |
ppm | ||
Na(Sodium) Na(Sodium) |
ppm | ||
|
MPa·m/s | 内部方法 | |
|
% | ASTM E595 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
洛氏硬度 Rockwell hardness |
|||
M 级 M-level |
ASTM D785 | ||
拉伸模量 Tensile modulus |
MPa | ASTM D638 | |
拉伸强度 tensile strength |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D638 | |
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
弯曲强度 bending strength |
MPa | ASTM D790 | |
压缩模量 Compression modulus |
MPa | ASTM D695 | |
压缩强度 compressive strength |
|||
10% 应变 10% strain |
MPa | ASTM D695 | |
剪切强度 shear strength |
MPa | ASTM D732 | |
摩擦系数 friction coefficient |
|||
与钢 - 动态 Steel - Dynamic |
内部方法 | ||
磨损因数 Wear factor |
10^-8 mm³/N·m | 内部方法 |
备注 | |||
---|---|---|---|
暂无数据 |
【新闻资讯】查看全部
塑料净化对环境毁坏力堪比气候变化
2017-07-03 据英国《每日邮报》6月29日报道,近日专家警告,对塑料包装的过度依赖与气候变化一样会对环境造成巨大的破坏。数据显示,全球每分钟售出100万个塑料瓶,这一数字2021年预计将增加20%。据《卫报》透露,去年仅有不到一半的废弃塑料瓶被回收利用。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |