| 牌号简介 About |
|---|
| Solanyl® C8101是一种适用于薄膜应用的端部化合物，专门用于包装。Solanyl® C8101可在适合（多层）柔性薄膜的传统吹塑或铸膜挤出生产线上加工。Solanyl® C8101是目前广泛应用的可生物降解塑料和低密度聚乙烯的竞争替代品。Solanyl® C8101拥有自然的感觉和外观。Solanyl® C8101是可生物降解的，生物基或植物源材料含量大于40%。索拉尼龙C8101的应用包括：包装和消费品、农产品 Solanyl® C8101 is an end compound suitable for film applications and is specially developed for packaging. Solanyl® C8101 can be processed on conventional blown or cast film extrusion lines suitable for (multi-layer) flexible films. Solanyl® C8101 is a competitive alternative for currently used biodegradable plastics and LDPE for a wide range of applications. Solanyl® C8101 has a natural feel and look. Solanyl® C8101 is biodegradable and has a biobased or plant derived material content of > 40%. Applications in which Solanyl ® C8101 can be used are: Packaging & Consumer goods Agriculture products |
产品描述 Product Description
用途：包装;流延薄膜;吹膜;农业应用;
加工条件：流延薄膜
性能特点： 可回收; 可堆肥; 食品接触; 生物可降解; 韧性好; Good flexibility,Renewable resources,Biodegradable,Food contact compliance,Compostable
| 技术参数 Technical Data | |||
|---|---|---|---|
|
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
薄膜厚度 film thickness |
|||
|
测试 test |
40 到 200 | µm | |
|
拉伸强度 tensile strength |
|||
|
注塑成型 injection molding |
13.0 到 15.0 | MPa | ISO 527-2 |
|
MD，屈服 MD, yield |
13.0 到 15.0 | MPa | |
|
TD，屈服 TD, yield |
MPa | ||
|
MD MD |
MPa | ||
|
TD TD |
MPa | ||
|
埃尔曼多夫抗撕强度 Elmandorf tear strength |
|||
|
MD MD |
N | ISO 6383-2 | |
|
MD MD 3 |
N | ||
|
TD TD |
N | ISO 6383-2 | |
|
TD TD 3 |
N | ||
|
水气透过率 Water vapor transmittance |
|||
|
23℃，75% RH 23℃，75% RH |
g/m²/24 hr | ||
|
23℃，85% RH 23℃，85% RH |
g/m²/24 hr | ||
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
|
注塑成型 injection molding |
kJ/m² | ISO 179/1eA | |
|
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
|||
|
注塑成型 injection molding |
kJ/m² | ISO 179/1eU | |
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
|
注塑 Injection molding |
kJ/m² | ISO 180-1A | |
|
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
|
注塑 Injection molding |
kJ/m² | ISO 180/1U | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
|||
|
0.45 MPa，未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
|
玻璃化转变温度 Glass transition temperature |
℃ | DSC | |
|
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306/A | |
|
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
Water Activity Water Activity |
内部方法 | ||
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
邵氏硬度 Shore hardness |
|||
|
邵氏 D，注塑成型 Shaw's D, injection molding |
ISO 868 | ||
|
拉伸模量 Tensile modulus |
|||
|
注塑成型 injection molding |
MPa | ||
|
正割，注塑成型 Cutting, injection molding |
MPa | ||
|
拉伸应变 Tensile strain |
|||
|
屈服，注塑成型 Yield, injection molding |
% | ||
|
断裂，注塑成型 Fracture, injection molding |
% | ||
|
弯曲模量 Bending modulus |
|||
|
注塑成型 injection molding |
MPa | ISO 178 | |
|
弯曲强度 bending strength |
|||
|
注塑成型 injection molding |
MPa | ISO 178 | |
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
g/cm³ | ISO 1183 | |
|
表观密度 Apparent density |
g/cm³ | ISO 60 | |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
170℃，5.0kg 170℃，5.0kg |
g/10min | ISO 1133 | |
|
熔体体积流动速率 Melt Volume Rate |
|||
|
190℃，2.16 kg 190℃，2.16 kg |
cm³/10min | ISO 1133 | |
|
螺旋流动长度 Spiral flow length 2 |
cm | ||
|
收缩率 Shrinkage rate |
% | ISO 294-4 | |
|
含水量 water content |
内部方法 | ||
|
灰份含量 Ash Content |
% | 内部方法 | |
|
熔体表观粘度 Apparent viscosity of melt |
|||
|
140℃，10.0 sec^-1 140℃，10.0 sec^-1 |
Pa·s | ||
|
140℃，100 sec^-1 140℃，100 sec^-1 |
Pa·s | ||
|
140℃，1000 sec^-1 140℃，1000 sec^-1 |
Pa·s | ||
|
170℃，10.0 sec^-1 170℃，10.0 sec^-1 |
Pa·s | ||
|
170℃，100 sec^-1 170℃，100 sec^-1 |
Pa·s | ||
|
170℃，1000 sec^-1 170℃，1000 sec^-1 |
Pa·s | ||
|
特殊值 |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
MD MD |
350 到 420 | MPa | |
|
TD TD |
100 到 250 | MPa | |
|
MD，屈服 MD, yield |
% | ||
|
TD，屈服 TD, yield |
% | ||
|
MD，断裂 MD, fracture |
% | ||
|
TD，断裂 TD, fracture |
% | ||
| 备注 |
|---|
| 2、模具温度: 25°C |
| 3、DIN 53514 |
|
【新闻资讯】查看全部
十建中化泉州项目设备装置工程正式拉开尾声
2019-01-03 2018年12月24日，炼化工程十建公司承建的中化泉州100万吨/年乙烯及炼油改扩建项目乙烯装置1号丙烯精馏塔顺利吊装就位，标志着该项目设备安装工程正式拉开序幕。 据了解，1号丙烯塔是中化泉州乙烯项目到场的首台大型受限设备，设备到场前，项目部提前策划，持续与业主、总承包单位沟通，跟踪设计图纸、材料，设备到货时间，确保了设备到货前完成了附塔平台、附塔管线的预制工作。 该设备于11月28日抵达码头，29日现场摆放到位。12月3日完成附塔平台的安装，12月14日完 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |