牌号简介 About |
---|
12熔融阻燃聚碳酸酯释放,非氯非溴应用/用途:电气设备、通信外壳、商业设备、计算机。关键词:聚合物;热塑性塑料;聚碳酸酯(PC);聚碳酸酯,未增强,阻燃,UL 746H,UL 746R,RoHS,无氯无溴 12 Melt Flame Retardant Polycarbonate with Release, Non-Chlorine Non-Bromine Application/Use: Electircal Devices, Communications enclosures, Business Equipment, Computers. Key Words: Polymer; Thermoplastic; Polycarbonate (PC); Polycarbonate, Unreinforced, Flame Retardant, UL 746H, UL 746R, RoHS, Non-Chlorine Non-Bromine |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.23 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
300℃,1.20kg 300℃,1.20kg |
12 | g/10min | ASTM D1238 |
收缩率 Shrinkage rate |
|||
MD MD |
0.50 到 0.70 | % | ASTM D955 |
室外适用性 Outdoor applicability |
f1 | UL 746C | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
3.2mm 3.2mm |
640 | J/m | ASTM D256 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:-40~95℃ MD:-40~95℃ |
1/℃ | ||
TD:-40~95℃ TD:-40~95℃ |
1/℃ | ||
相对温度指数 Relative temperature index |
℃ | UL 746 | |
电气性能 Electrical performance |
℃ | UL 746 | |
冲击机械性能 Impact mechanical performance |
℃ | UL 746 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
耐电弧性 Arc resistance |
ASTM D495 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
UL 746 | ||
高电弧燃烧指数(HAI) High Arc Burning Index (HAI) |
|||
1.5 mm 1.5 mm |
|||
3.0 mm 3.0 mm |
|||
高电压电弧起痕速率 High voltage arc marking rate |
|||
HVTR HVTR |
UL 746 | ||
热丝引燃 Hot wire ignition |
|||
HWI HWI |
|||
1.5 mm 1.5 mm |
|||
3.0 mm 3.0 mm |
|||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
|||
1.50 mm 1.50 mm |
|||
3.00 mm 3.00 mm |
|||
灼热丝可燃性指数 Glowing wire flammability index |
℃ | IEC 60695-2-12 | |
灼热丝起燃温度 Igniting temperature of the hot wire |
℃ | IEC 60695-2-13 | |
极限氧指数 Extreme oxygen index |
% | ASTM D2863 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
UL Rating UL Rating |
|||
Non-bromine,Non-chlorine Non-bromine,Non-chlorine |
UL 746H | ||
RoHS Compliance RoHS Compliance |
UL 746R | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
洛氏硬度 Rockwell hardness |
|||
R 级 R-level |
ASTM D785 | ||
拉伸强度 tensile strength |
|||
屈服,3.17 mm Yield, 3.17 mm |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂,3.17 mm Fracture, 3.17 mm |
% | ASTM D638 | |
弯曲模量 Bending modulus |
|||
3.17 mm 3.17 mm |
MPa | ASTM D790 | |
弯曲强度 bending strength |
|||
屈服,3.17 mm Yield, 3.17 mm |
MPa | ASTM D790 |
备注 | |||
---|---|---|---|
暂无数据 |
【新闻资讯】查看全部
塑料在通讯工程与家用电器工业中的运用
2017-09-11 通讯工程中的应用 属于高科技领域的现代通讯产业缺少不了轻质,透明,坚韧,又绝缘的塑料,可以说新型的绝缘线缆,通讯电缆和光缆,光盘等光记录材料以及诸如移动电话,传真机,复印机,电脑打印机等通讯用办公设备的迅速发展,是在近年来各国对通用塑料,工程塑料及其合金塑料进行了大量深入的研究,开发出一系列能满足不同通讯器材上所要求的特殊性能之塑料之后才实现的。 家用电器工业中的应用 家用电器是耐用消费品的主要领域,中国的家 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |