柔性,非卤化fr-mppe挤出级,适用于电线绝缘等应用中的评估。阻燃性能能够满足UL 1581规定的VW1和105C温度等级要求。56肖氏硬度。使用标准的挤压设备进行良好的加工。使用0.12 mm x 20绞合铜导线在2.0 mm电线上进行的UL 1581试验。 Flexible, non-halogenated FR mPPE extrusion grade ideal for evaluation in applications such as wire insulation. Flame retardant performance capable of meeting VW1 and 105C temperature rating requirements as defined by UL 1581. 56 Shore D hardness. Excellent processing using standard extrusion equipment. UL 1581 tests conducted on 2.0 mm wire with 0.12 mm x 20 stranded copper conductor. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.03 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
250℃,10.0kg 250℃,10.0kg |
5.1 | g/10min | ASTM D1238 |
吸水率 Water absorption rate |
|||
23℃,48hr 23℃,48hr |
0.10 | % | ASTM D570 |
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
撕裂强度 tear strength |
25 | kN/m | ISO 6383 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火,6.4 mm 0.45 MPa, unannealed, 6.4 mm |
85.0 | ℃ | ASTM D648 |
脆化温度 Embrittlement temperature |
℃ | ASTM D746 | |
维卡软化温度 Vicat Softening Temp |
|||
A50 A50 |
℃ | ISO 306/A50 | |
UL温度额定值 UL temperature rating 7 |
℃ | UL 1581 | |
Heat Deformation(121℃) Heat Deformation(121℃) 8 |
% | UL 1581 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume resistivity |
ohms·cm | IEC 60093 | |
介电强度 Dielectric strength |
|||
2 mm,在油中 2 mm in oil |
kV/mm | IEC 60243-1 | |
相对电容率 Relative permittivity |
|||
50 Hz 50 Hz |
|||
60 Hz 60 Hz |
|||
1 MHz 1 MHz |
|||
耗散因数 Dissipation factor |
|||
50 Hz 50 Hz |
|||
60 Hz 60 Hz |
|||
1 MHz 1 MHz |
|||
相比漏电起痕指数 Compared to the leakage tracing index |
V | IEC 60112 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
灼热丝可燃性指数 Glowing wire flammability index |
|||
3.0 mm 3.0 mm |
℃ | IEC 60695-2-12 | |
灼热丝起燃温度 Igniting temperature of the hot wire |
|||
3 mm 3 mm |
℃ | IEC 60695-2-13 | |
极限氧指数 Extreme oxygen index |
% | ISO 4589-2 | |
VW-1 VW-1 2 |
UL 1581 | ||
烟雾密度 Smoke density 9 |
|||
Flaming,Ds max:500.0 µm Flaming,Ds max:500.0 µm |
|||
Non-Flaming,Ds max:500.0 µm Non-Flaming,Ds max:500.0 µm |
|||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
ISO 868 | ||
拉伸强度 tensile strength |
|||
断裂 fracture 2 |
MPa | UL 1581 | |
断裂 fracture 3 |
MPa | ASTM D638 | |
断裂,136℃ Fracture, 136 ℃ 4 |
MPa | UL 1581 | |
断裂 fracture |
MPa | ISO 527-2/50 | |
拉伸应变 Tensile strain |
|||
断裂 fracture 2 |
% | UL 1581 | |
断裂 fracture 3 |
% | ASTM D638 | |
断裂,136℃ Fracture, 136 ℃ 5 |
% | UL 1581 | |
断裂 fracture |
% | ISO 527-2/50 | |
弯曲模量 Bending modulus 6 |
|||
100 mm跨距 100 mm span |
MPa | ASTM D790 | |
-- -- |
MPa | ISO 178 |
备注 |
---|
2. 2.0 mm wire with 0.12 mm x 20 stranded copper |
3. 类型 1, 50 mm/min |
4. After 7 days. Tested on 2.0 mm wire with 0.12 mm x 20 stranded copper |
5. 6 days, 2.0 mm wire with 0.12 mm x 20 stranded copper |
6. 13 mm/min |
7. 2.0mm wire with 0.12 mm x 20 stranded copper |
8. 250g, 2.0 mm wire with 0.12 mm x 20 stranded copper |
9. Plaque |
【新闻资讯】查看全部
中科炼化10万吨/年EVA装置顺利实现中交
2021-12-06 搜料网资讯; 12月3日,中科炼化一体化项目再传捷报,经石化四建工程项目管理团队湛江中科炼化PMC项目管理部EVA项目组及各参建单位三年多的辛勤奋战,中科炼化10万吨/年EVA装置顺利 |
中科炼化10万吨/年EVA装置顺利实现中交 搜料网资讯;12月3日,中科炼化一体化项目再传捷报,经石化四建工程项目管理团队湛江中科炼化PMC项目管理部EVA项目组及各参建单位三年多的辛勤奋战,中科炼化10万吨/年EVA装置顺利中交! 据介绍,中科炼化10万吨/年EVA装置是以乙烯、醋酸乙烯为原料,以有机过氧化物为引发剂,通过反应釜高效搅拌器的搅拌,在高压状态下生产乙烯-醋酸乙烯共聚EVA产品。该装置主要由乙烯压缩单元、聚合单元、高/低压循环分离单元、挤压造粒单元、风送脱气单元、废气处理单元、醋酸乙烯回收精制单元以及配套的冷冻水机组等辅助设施组成。 为确保中科炼化10万吨/年EVA装置按期中交,石化四建工程项目管理团队湛江中科PMC项目管理部EVA项目组以高压超高压管道系统安装、大机组试车为关键施工线路,精心组织10万吨/年EVA装置的施工管理工作,首先积极督促EPC总包单位加快推进高压、超高压进口管道材料的采购工作,原计划所有进口超高压管道在2020年到货,因突发疫情影响,进口材料到货滞后严重制约着施工进度,经与采购厂商反复沟通协调,第一批进口材料在今年5月份才运抵现场,又经过近两个月的催交催运,7月份所有进口高压管道材料才全部到货,为EVA装置超高压管道系统安装创造了条件;其次,面临超高压管道系统进口材料不能按期到货的困难,EVA项目组及时督促总包调整施工计划,要求施工单位积极抢上低压工艺管道的预制安装,加快电气仪表安装调试步伐,确保10万吨/年EVA装置设备安装、低压管道试压、电气仪表调试按期完成;最后,积极督促施工单位尽快完成压缩机机间管线回装,组织一次压缩机和二次压缩机油运,确保大机组试车工作全面展开。 经石化四建工程项目管理团队湛江中科PMC项目管理部EVA项目组的不懈努力,截至目前,一、二次压缩机单机试车已全部完成,挤压机已完成投料试车,冰机抽真空等工作已圆满结束,预冷器、中冷器、深冷器等设备试压工作已顺利完成,总共714段高压管段已全部安装完,18段调整段已全部安装完,总共1568副法兰已安装完、紧固完,高压管道58个试压包已全部试压完,为EVA装置打通全流程顺利中交打下了坚实的基础。随着10万吨/年EVA装置的顺利中交,将为中科炼化一体化项目画上了一个圆满的句号!
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
价格走势图
抱歉!该牌号暂无认证数据。
抱歉!暂无数据。
抱歉!暂无数据。