牌号简介 About |
---|
材料规范符合ISO 1043-1:PA66尼龙66/6共聚物,由40%重量的长玻璃纤维增强。球是圆柱形的,通常也包括10 mm长的嵌入纤维。Celstran成型件具有高强度、高刚度、高热变形等优异的力学性能。由于部件中内置了纤维骨架,因此在高温和低温下缺口冲击强度会增加。长纤维增强能显著降低蠕变。模制品的各向同性收缩使翘曲最小化。通过注射成型,可以制造出具有高再现性的复杂零件。可代替压铸金属,重量轻,无腐蚀问题,无后处理。 Material code according to ISO 1043-1: PA66 Nylon 66/6 Copolymer reinforced by 40 weight percent long glass fibers. The pellets are cylindrical and normally as well as the embedded fibers 10 mm long. Parts molded of CELSTRAN have outstanding mechanical properties such as high strength and stiffness combined with high heat deflection. The notched impact strength is increased at elevated and low temperatures due to the fiber skeleton built in the parts. The long fiber reinforcement reduces creep significantly. The very isotropic shrinkage in the molded parts minimizes the warpage. Complex parts can be manufactured with high reproducibility by injection molding. Can be used for substituting die cast metal with the advantage of Weight reduction, no corrosion problems, no post treatment. |
产品描述 Product Description
厂家:美国塞拉尼斯 Celanese
类别:PA66/6 PA66/6
用途:金属取代;
加工条件:注射成型 Injection Molding
性能特点: 耐腐蚀; 机械强度好; 各向同性好; 耐低温冲击; 低翘曲性; 韧性好; Good Rigidity,Low warping,Good flexibility,Corrosion Resistant,low-temperature impact resistance,Good Isotropy
填料:玻璃纤维 40
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.46 | g/cm³ | |
吸水率 Water absorption rate |
|||
饱和,23℃ Saturation, 23 ℃ |
1.2 | % | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
12800 | MPa | |
拉伸强度 tensile strength |
|||
断裂 fracture |
240 | MPa | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
2.3 | % | |
弯曲模量 Bending modulus |
|||
23℃ 23℃ |
MPa | ||
80℃ 80℃ |
MPa | ||
弯曲强度 bending strength |
|||
23℃ 23℃ |
MPa | ||
80℃ 80℃ |
MPa | ||
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
-30℃ -30℃ |
kJ/m² | ||
23℃ 23℃ |
kJ/m² | ||
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
|||
-30℃ -30℃ |
kJ/m² | ||
23℃ 23℃ |
kJ/m² | ||
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
-30℃ -30℃ |
kJ/m² | ||
23℃ 23℃ |
kJ/m² | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ||
8.0 MPa,未退火 8.0 MPa, unannealed |
℃ | ||
熔融温度 Melting temperature 2 |
℃ |
备注 |
---|
2. 10°C/min |
【新闻资讯】查看全部
上海赛科:打通物流大动脉 带动下游企业复工复产
2022-05-30 上海赛科严抓疫情防控,以路运转铁路、路运转水路等多种方式,成功打通物流大动脉,有效带动下游企业复工复产。目前,566名员工驻厂值守,生产运行处于安全可控状态。 图为丙烯 |
上海赛科:打通物流大动脉 带动下游企业复工复产 上海赛科严抓疫情防控,以路运转铁路、路运转水路等多种方式,成功打通物流“大动脉”,有效带动下游企业复工复产。目前,566名员工驻厂值守,生产运行处于安全可控状态。
图为丙烯腈1号装置内操紧张有序地进行反应器投料
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
价格走势图
开始时间:
结束时间:
材料厂家:
【牌号齐全,内容全面】
全网共2500+项牌号+上游原料单体+原油价格,最长可追溯近20年价格行情
【精准,及时,权威!】
专业团队挖掘行情信息,第一时间发布行情
抱歉!该牌号暂无认证数据。
免责声明:参考价格是搜料网根据网络大数据拟合分析的结果,仅供参考。实际成交价取决但不限于以下因素:下单时间,付款方式,交货方式,数量,税费,色号,产地,项目信息。
抱歉!暂无数据。
抱歉!暂无数据。