牌号简介 About |
---|
说明BI302是为薄膜应用而设计的高冲击聚丙烯。由于采用乙丙橡胶设计,BI302具有较高的冲击强度。这种级别的薄膜具有优异的机械强度,因此这种级别非常适合于干馏袋薄膜的应用。特性高抗冲击强度耐冲压透明应用耐蒸煮袋,铸膜 Description BI302 is a high impact polypropylene designed for film application. Due to ethylene-propylene rubber design, BI302 shows high impact strength. Films made from this grade provide excellent mechanical strength, thus this grade is highly suited for retort pouch film application. Characteristics High impact strength Punch resistance Transparency Applications Retort pouch, Cast film |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.910 | g/cm³ | ASTM D1505 |
熔体质量流动速率 Melt Flow Rate |
|||
230℃,2.16kg 230℃,2.16kg |
5.0 | g/10min | ASTM D1238 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
200 | J/m | ASTM D256 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
105 | ℃ | ASTM D648 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
洛氏硬度 Rockwell hardness |
|||
R 级 R-level |
60 | ASTM D785 | |
拉伸强度 tensile strength |
|||
屈服 yield |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D638 | |
弯曲模量 Bending modulus |
MPa | ASTM D790 |
备注 | |||
---|---|---|---|
暂无数据 |
【新闻资讯】查看全部
诠世传动全新IROTNECNO加速机退场
2016-04-26 来自意大利的诠世传动,由中国杭州子公司代表,展出全新IRONTECNO铸铁系列产品,以及ATS系列铸铝平行轴式减速机和CM070新型号减速机。 诠世传动全新IROTNECNO |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |