牌号简介 About |
---|
EMERGE™ PC 8600ECO-10高级树脂含有50%的消费后回收(PCR)聚碳酸酯,符合由T_V Rheinland认证的IEEE 1680:2006。它是一种半透明的阻燃聚碳酸酯,不含氯、溴或磷酸盐添加剂,符合全球环境标准。该树脂具有良好的机械、热和化学性能,同时保持了良好的加工性能。应用电子和电器充电和适配器外壳信息技术设备 EMERGE™ PC 8600ECO-10 Advanced Resin contains 50% post consumer recycled (PCR) polycarbonate complying with IEEE 1680:2006 certified by TÜV Rheinland. It is a translucent and ignition resistant polycarbonate that does not contain chlorine, bromine, or phosphate additives to comply with global environmental standards. This resin combines good mechanical, thermal, and chemical properties while retaining excellent processability. Applications Electronics and electrical appliances Charges and adaptors enclosures Information technology equipment |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.20 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
300℃,1.20kg 300℃,1.20kg |
10 | g/10min | ASTM D1238 |
收缩率 Shrinkage rate |
|||
MD MD |
0.50 到 0.70 | % | ASTM D955 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
3.20 mm,注塑成型 3.20 mm, injection molded |
2800 | MPa | ASTM D638 |
拉伸强度 tensile strength |
|||
屈服,3.20 mm,注塑成型 Yield, 3.20 mm, injection molding |
61.0 | MPa | |
断裂,3.20 mm,注塑成型 Fracture, 3.20 mm, injection molded |
MPa | ||
拉伸应变 Tensile strain |
|||
屈服,3.20 mm,注塑成型 Yield, 3.20 mm, injection molding |
% | ||
断裂,3.20 mm,注塑成型 Fracture, 3.20 mm, injection molded |
% | ||
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃,3.2mm,注塑成型 23 ℃, 3.2mm, injection molding |
J/m | ASTM D256 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
维卡软化温度 Vicat Softening Temp |
|||
-- -- |
℃ | ASTM D1525 2 | |
-- -- |
℃ | ISO 306/A120 | |
球压温度 Ball pressure temperature |
℃ | IEC 60335-1 | |
相对温度指数 Relative temperature index |
℃ | UL 746 | |
电气性能 Electrical performance |
℃ | UL 746 | |
冲击机械性能 Impact mechanical performance |
℃ | UL 746 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
|||
0.55 mm 0.55 mm |
|||
1.50 mm 1.50 mm |
|||
2.50 mm 2.50 mm |
备注 |
---|
2、标准 B (120°C/h), 压 力1 (10N) |