牌号简介 About |
---|
Technylexten D 219WFC V30黑色是一种聚酰胺6.10,用30%的玻璃纤维增强,有机稳定,用于注塑成型。水和食物接触认证。本产品有黑色可选。 TECHNYL eXten® D 219WFC V30 Black is a polyamide 6.10, reinforced with 30% of glass fibre, heat stabilized with organic stabilizers, for injection moulding. This grade offers lower water uptake, higher dimensional stability and enhanced chlorine resistance versus standard PA 6.6. It offers too an enhanced corrosion resistance, a reduction in lead levels versus standard metal solutions and an increase in ease of processing and part design freedom versus metal solutions and other plastics. It is used for cold and warm water plumbing components including, but not limited to, components in contact with drinking water systems globally where elevated levels of chlorine could be present. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.31 | g/cm³ | ISO 1183/A |
吸水率 Water absorption rate |
ISO 62 | ||
23℃,24hr 23℃,24hr |
0.36 | % | ISO 62 |
饱和,23℃ Saturation, 23 ℃ |
2.4 | % | ISO 62 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
23℃ 23℃ |
9200 | MPa | ISO 527-2/1A |
拉伸强度 tensile strength |
|||
断裂,23℃ Fracture, 23 ℃ |
150 | MPa | ISO 527-2/1A |
拉伸应变 Tensile strain |
|||
断裂,23℃ Fracture, 23 ℃ |
% | ISO 527-2 | |
弯曲模量 Bending modulus |
|||
23℃ 23℃ |
MPa | ASTM D790 | |
23℃ 23℃ |
MPa | ISO 178 | |
弯曲强度 bending strength |
|||
23℃ 23℃ |
MPa | ASTM D790 | |
23℃ 23℃ |
MPa | ISO 178 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
kJ/m² | ISO 180 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/Af | |
熔融温度 Melting temperature |
℃ | ISO 11357-3 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | IEC 60093 | |
体积电阻率 Volume resistivity |
ohms·cm | IEC 60093 | |
介电强度 Dielectric strength |
|||
2 mm 2 mm |
kV/mm | IEC 60243-1 | |
相对电容率 Relative permittivity |
IEC 60250 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
|||
解决方案 A Solution A |
V | IEC 60112 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
1.60 mm 1.60 mm |
UL 94 | ||
3.20 mm 3.20 mm |
UL 94 | ||
灼热丝可燃性指数 Glowing wire flammability index |
|||
1.6 mm 1.6 mm |
℃ | IEC 60695-2-12 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
博禄化工将在2020年恢复中国聚合物工厂的消费
2018-08-27 8月20日,博禄化工市场和销售公司CEO Wim Roels在2018届亚洲石化工业会议上透露,博禄化工预计在2020年恢复中国聚合物工厂的生产。 据 Wim Roels介绍,博禄化工上海工厂正在进行一项“去瓶颈”工程,目前已经进行到前端工程和设计阶段。该项目完成后,上海工厂的产能将从目前的3.5万吨/年上升至12.5万吨/年。 据了解,博禄化工上海工厂的产品主要服务于中国的汽车市场,特别是电动汽车。 Wim Roels表示:“目前汽车行业正 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |