牌号简介 About |
---|
滑动改性双向拉伸聚丙烯薄膜非热封双面处理 Slip Modified BIAXIALLY ORIENTED POLYPROPYLENE FILM NON-HEAT SEALABLE, TWO SIDE TREATED |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
尺寸稳定性 dimensional stability 2 |
|||
TD,130℃ TD,130℃ |
< 3.0 | % | |
MD,130℃ MD,130℃ |
< 5.0 | % | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
摩擦系数 friction coefficient |
ASTM D1894 | ||
动态 dynamic |
0.20 | ASTM D1894 | |
静态 static state |
0.25 | ASTM D1894 | |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
30 | µm | |
拉伸强度 tensile strength |
ASTM D882 | ||
MD,屈服 MD, yield |
MPa | ASTM D882 | |
TD,屈服 TD, yield |
MPa | ASTM D882 | |
拉伸应变 Tensile strain |
ASTM D882 | ||
MD,断裂 MD, fracture |
% | ASTM D882 | |
TD,断裂 TD, fracture |
% | ASTM D882 | |
水气透过率 Water vapor transmittance |
|||
38℃,90% RH 38℃,90% RH |
g/m²/24 hr | ASTM F1249 | |
用量 dosage 3 |
m²/kg | ||
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
45° 45° |
ASTM D2457 | ||
雾度 Haze |
% | ASTM D1003 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面能 Surface energy |
ASTM D2578 | ||
-- -- 4 |
dyne/cm | ASTM D2578 | |
-- -- 5 |
dyne/cm | ASTM D2578 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 5 minutes |
3 Internal Method |
4 Corona Side |
5 High Energy Flame Side |
【新闻资讯】查看全部
数值分析技术及其在注塑模中的使用研讨
2016-01-29 数值分析技术及其在注塑模中的应用研究系统的数学模型,采用混合有限元法、有限差分法求解压力和能量方程,从而实现了成型过程数值分析。 在塑料制品生产中,塑料、模具和加工设备三者密切相关。塑料加工不单纯是物理成型过程,而是控制制品的结构和性能的中心环节。近几年来,发展最快的是利用计算机辅助工程对加工过程进行数值模拟,研究加工条件的变化规律,预测制品的结构和性能,选择制品和模具设计以及工艺条件的最佳方案,使加工成型从一项实用技术变为一门应用科学。如果对塑料在加工过程中的流动、传热, |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |