牌号简介 About |
---|
235G是一种35%玻璃纤维增强尼龙6,在机械性能、表面光洁度和模具释放特性之间提供平衡。 235G is a 35% glass fibre reinforced nylon 6 that offers a balance between mechanical performance, surface finish and mould release characteristics. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density Density |
1.41 | g/cm³ | ISO 1183 |
成型收缩率 Molding Shrinkage Molding shrinkage |
0.7-1.2 | % | ISO 294-4 |
吸水率 Water Absorption Water Absorption |
|||
平衡 equilibrium,23℃,50%r.h. Equilibrium equilibrium, 23 ℃, 50% r. h |
1.9 | % | ISO 62 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile Modulus Tensile Modulus |
|||
干燥 dry Dry |
10005 | MPa | ISO 527 |
湿润 cond. Wet Cond |
8004 | MPa | ISO 527 |
拉伸强度 Tensile Strength Tensile Strength |
|||
干燥 dry Dry |
MPa | ISO 527-2 | |
湿润 cond. Wet Cond |
MPa | ISO 527-2 | |
拉伸应变 Tensile Strain Tensile Strain |
|||
断裂 brk,干燥 dry Broken BRK, dry dry |
% | ISO 527 | |
断裂 brk,湿润 cond. Broken BRK, wet Cond |
% | ISO 527 | |
弯曲模量 Flexural Modulus Flexural Modulus |
|||
干燥 dry Dry |
MPa | ISO 178 | |
湿润 cond. Wet Cond |
MPa | ISO 178 | |
弯曲强度 Flexural Strength Flexural Strength |
|||
干燥 dry Dry |
MPa | ISO 178 | |
湿润 cond. Wet Cond |
MPa | ISO 178 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy notched Impact strength Charpy Notched Impact Strength |
|||
干燥 dry Dry |
kJ/m² | ISO 179/1eA | |
湿润 cond. Wet Cond |
kJ/m² | ISO 179/1eA | |
简支梁无缺口冲击强度 Charpy Unnotched Impact strength Charpy Unnotch Impact strength |
kJ/m² | ISO 179/1eU | |
悬臂梁缺口冲击强度 Izod Notched Impact strength Izod Notched Impact strength |
KJ/m² | ISO 180/1A | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 HDT Hot deformation temperature HDT |
|||
0.45 MPa 0.45 MPa |
℃ | ISO 75-1/-2 | |
1.82 MPa 1.82 MPa |
℃ | ISO 75-1/-2 | |
电气性能 ELECTRICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface Resistivity Surface Resistivity |
|||
干燥 dry Dry |
ohms | IEC 60093 | |
湿润 cond. Wet Cond |
ohms | IEC 60093 | |
体积电阻率 Volume Resistivity Volume Resistance |
|||
干燥 dry Dry |
ohms·cm | IEC 60093 | |
湿润 cond. Wet Cond |
ohms·cm | IEC 60093 | |
耐电强度 Electric strength Electric strength |
|||
干燥 dry Dry |
V/mil | IEC 60243-1 | |
湿润 cond. Wet Cond |
V/mil | IEC 60243-1 | |
相对电容率 Relative Permittivity Relative permittivity |
|||
干燥 dry Dry |
IEC 60250 | ||
湿润 cond. Wet Cond |
IEC 60250 | ||
相比漏电起痕指数 Comparative Tracking Index Compared Tracking Index |
V | IEC 60112 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame Class Rating Flame Class Rating |
|||
0.16 mm 0.16 mm |
calss | UL 94 | |
极限氧指数 Oxygen Index Oxygen Index |
% | ISO 4589-2 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Mould shrinkage is significantly influenced by many factors including wall thickness, gating, moulding shape and processing conditions. The range values given are determined from specimen bar mouldings of 1.5mm to 4mm wall thickness. They are provided as a guide for comparison purposes only and no guarantee should be inferred from their inclusion. (Specimens measured in the dry state, 24 hours after moulding). |
【新闻资讯】查看全部 ![]()
道达尔牵头对HYZON Motors进行战略投资
2020-11-22 搜料网资讯:2020年10月10日,氢能移动和清洁能源公司HYZON Motors和欧洲能源巨头道达尔SE旗下风险投资部门Total Carbon Neutrality Ventures宣布了一项由道达尔和其他专业氢能源投资机构牵头的 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |