牌号简介 About |
---|
VITAMIDE® AI13BK8503是一种聚酰胺66(尼龙66)产品,。 它,在欧洲有供货。 特性包括: 阻燃/额定火焰 冲击改性 Chemically reinforced with 15% glass fibre, suitable for mouldings with high strength and toughness also at minus temperatures. Used in the automotive, engineering and electrical industry. With the increasing content of FG also the toughness, tensile and bending strength increase, the shrinkage decreases and the heat application increases up to 250°C. It achieves higher rates of tensile strength and modulus of elasticity also in conditioning state when compared with PA 6 GF. PA 66 GF50 achieves modulus 16000MPa - of the aluminium alloy rates. Application: hobby tools, covers of electrotools, electromotors, cooling screws of blowers, gear wheels, carrying parts in the automotive industry like eg. brake cables. Delivered in natural mode and in the full RAL colour scale. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.23 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
275℃,0.325kg 275℃,0.325kg |
3.0 | g/10min | ISO 1133 |
收缩率 Shrinkage rate |
STM 64 0808 | ||
TD TD |
1.2 | % | STM 64 0808 |
MD MD |
0.80 | % | STM 64 0808 |
含水量 water content |
0.15 | % | ISO 960 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
MPa | ISO 527-2 | |
拉伸强度 tensile strength |
|||
屈服 yield |
MPa | ISO 527-2 | |
拉伸应变 Tensile strain |
|||
屈服 yield |
% | ISO 527-2 | |
弯曲模量 Bending modulus |
MPa | ISO 178 | |
弯曲强度 bending strength |
MPa | ISO 178 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179 | ||
-20℃ -20℃ |
kJ/m² | ISO 179 | |
23℃ 23℃ |
kJ/m² | ISO 179 | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
ISO 179 | ||
-20℃ -20℃ |
kJ/m² | ISO 179 | |
23℃ 23℃ |
kJ/m² | ISO 179 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306/B | |
熔融温度 Melting temperature |
|||
DSC DSC |
℃ | ISO 3146 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | IEC 60093 | |
体积电阻率 Volume resistivity |
ohms·cm | IEC 60093 | |
介电强度 Dielectric strength |
kV/mm | IEC 60243-1 | |
相比漏电起痕指数 Compared to the leakage tracing index |
V | IEC 60112 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
灼热丝起燃温度 Igniting temperature of the hot wire |
℃ | IEC 60695-2-13 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
路博润发布两种新型TPU树脂
2018-03-08 路博润公司的特种聚合物业务推出了两种用于热熔胶的新型热塑性聚氨酯树脂。 路博润表示,新型树脂属于不含增塑剂的Pearlbond 300 TPU系列,这是一种柔软的聚合物系列产品,具有低活化温度和对各种基材的优异粘合性能。 “新型树脂可用于技术纺织品,衬布,服装(接缝带和热转印标签),传送带,鞋类和其他应用,”路博润称。新的Pearlbond 360和960 TPU树脂在室外应用中表现非常好,这要归功于耐湿剂和微生物等外部因素。 “Pearlb |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |