| 牌号简介 About |
|---|
| 陶氏制造的TYRIL™ 苯乙烯-丙烯腈 (SAN) 树脂具有优异的耐化学品性能、强度、硬度和尺寸稳定性，适用产品范围广阔。与其他的SAN树脂相比，TYRIL 905的主要性能使其优异的水清色透明度以及热稳定性高，这些性能使其能够保持颜色的一致性（减少泛黄）。TYRIL 905用于要求加工性能好、耐化学品性能好和耐热性能好的应用领域。TYRIL 905 在减低痕量颜色方面实现了技术突破。其热稳定性和优异的浅基色使其特别适宜于自着色。加入了紫外线稳定剂的牌号产品具有优异的耐候性能，特别适宜照明装置。 应用领域： 大型电器：冰箱用的透明零部件 照明装置：百叶窗和灯罩 汽车：尾灯和反光镜 化妆品包装：要求水清色透明的、厚壁结构的包装材料 TYRIL* styrene-acrylonitrile (SAN) resins are designed to offer superior chemical resistance, strength, hardness and dimensional stability in a broad range of product applications. The key property of TYRIL 905 is its superior water-clear clarity compared to other SAN resins and a high thermal stability that results in consistent color (reduced yellowing). TYRIL 905 is designed for applications demanding chemical and heat resistance and offers good processability. TYRIL 905 represnts a technology breakthrough in trace-color reduction. Its thermal stability and exceptionally low base color make it a product especially suited for self-coloring. The UV-stabilized version exhibits excellent weather ability, suitable in particular for lighting applications. Applications: Large appliances: transparent refrigerator parts Lighting applications: louvers and covers Automotive: taillight lenses and reflectors Cosmetic packaging: water-clear, thick-wall applications |
产品描述 Product Description
用途：汽车领域的应用;照明应用;包装;电器用具;
颜色：清晰/透明
加工条件：注射成型 Injection Molding
性能特点： 防火阻燃等级HB; 机械强度好; 热稳定性好; 尺寸稳定性好; 耐化学性; 耐高温; 透光性好; 易加工; Good Rigidity,Excellent Processability,Good Clarity,Good Dimensional Stability,High Heat Resistance,Solvent resistance,Heat Stabilized,HB
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.08 | g/cm³ | ASTM D792 |
|
密度 Density |
1.08 | g/cm³ | ISO 1183/B |
|
密度 Density |
1.08 | g/cm³ | ISO 1183-2 |
|
表观密度 Apparent density |
0.69 | g/cm³ | ASTM D1895 |
|
表观密度 Apparent density |
0.69 | g/cm³ | ISO 60 |
|
熔体质量流动速率 Melt Flow Rate |
ASTM D1238 | ||
|
220℃，10.0kg 220℃，10.0kg |
g/10min | ASTM D1238 | |
|
230℃，3.80kg 230℃，3.80kg |
g/10min | ASTM D1238 | |
|
熔体质量流动速率 Melt Flow Rate |
ISO 1133 | ||
|
220℃，10.0kg 220℃，10.0kg |
g/10min | ISO 1133 | |
|
230℃，3.80kg 230℃，3.80kg |
g/10min | ISO 1133 | |
|
熔体体积流动速率 Melt Volume Rate |
|||
|
220℃，10 kg 220℃，10 kg |
cm³/10min | ISO 1133 | |
|
吸水率 Water absorption rate |
|||
|
饱和 saturated |
% | ISO 62-2 | |
|
平衡 balance |
% | ISO 62-2 | |
|
粘度值 Viscosity value |
cm³/g | ISO 307, 1157, 1628 2 | |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
|||
|
23℃ 23℃ |
kJ/m² | ISO 179 | |
|
简支梁冲击强度 Charpy impact strength |
|||
|
23℃ 23℃ |
kJ/m² | ISO 179/1eU 2 | |
|
-30℃ -30℃ |
kJ/m² | ISO 179/1eU 2 | |
|
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
|
23℃ 23℃ |
kJ/m² | ISO 180 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
|||
|
1.8 MPa，退火 1.8 MPa, annealed |
℃ | ASTM D648 | |
|
1.8 MPa，退火 1.8 MPa, annealed |
℃ | ISO 75-2/A | |
|
1.8 MPa 1.8 MPa |
℃ | ISO 75-2 2 | |
|
维卡软化温度 Vicat Softening Temp |
|||
|
B50 B50 |
℃ | ISO 306 2 | |
|
-- -- |
℃ | ISO 306/A120 | |
|
B50 B50 |
℃ | ISO 306 | |
|
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
|
TD TD |
1/℃ | ISO 11359-2 2 | |
|
MD MD |
1/℃ | DIN 53752 | |
|
MD MD |
1/℃ | ISO 11359-2 2 | |
|
比热 specific heat |
J/kg/℃ | ASTM D2766 | |
|
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
表面电阻率 Surface resistivity |
ohms | IEC 60093 2 | |
|
体积电阻率 Volume resistivity |
ohms·cm | IEC 60093 2 | |
|
介电强度 Dielectric strength |
kV/mm | IEC 60243-1 | |
|
相对电容率 Relative permittivity |
|||
|
100 Hz 100 Hz |
IEC 60250 2 | ||
|
1 MHz 1 MHz |
IEC 60250 2 | ||
|
1 MHz 1 MHz |
IEC 60250 | ||
|
耗散因数 Dissipation factor |
|||
|
1 MHz 1 MHz |
IEC 60250 | ||
|
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
1.60 mm 1.60 mm 6 |
UL 94 | ||
|
阻燃等级 Flame retardant level |
|||
|
1.60 mm 1.60 mm |
ISO 1210 2 | ||
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸模量 Tensile modulus |
MPa | ASTM D638 | |
|
拉伸模量 Tensile modulus |
MPa | ISO 527-2 | |
|
拉伸模量 Tensile modulus |
MPa | ISO 527-2 2 | |
|
拉伸强度 tensile strength |
|||
|
断裂 fracture 3 |
MPa | ASTM D638 | |
|
断裂 fracture |
MPa | ISO 527-2/5 | |
|
屈服 yield |
MPa | ISO 527-2 2 | |
|
拉伸应变 Tensile strain |
|||
|
屈服 yield |
% | ISO 527-2 2 | |
|
Nominal strain at break Nominal strain at break |
% | ISO 527-2 2 | |
|
弯曲强度 bending strength |
MPa | ASTM D790 | |
|
弯曲强度 bending strength |
MPa | ISO 178 | |
|
洛氏硬度 Rockwell hardness |
|||
|
M 级 M-level |
ISO 2039-2 | ||
|
M 级 M-level |
ASTM D785 | ||
|
特殊值 |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
-- -- |
℃ | ASTM D1525 4 | |
|
-- -- |
℃ | ASTM D1525 5 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 3 0.20 in/min |
| 4 标准 B (120°C/h), 压 力1 (10N) |
| 5 速率 A (50°C/h), 载荷2 (50N) |
| 6 这个额定值并非为了反映这种或任何其他材料在实际起火条件下造成的危险。 |
|
【新闻资讯】查看全部 
阿科玛计划收购无溶剂水性丙烯酸树脂龙头企业
2022-07-28 阿科玛计划收购墨西哥领先的乳液树脂制造商Polimeros Especiales。收购这家领先的无溶剂水性丙烯酸树脂公司的计划将加强阿科玛在这一快速发展地区的地位。 Polimeros Especiales是一家成熟 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付