牌号简介 About |
---|
NANCAR® 3345是一种中高丙烯腈-丁二烯共聚物,具有良好的耐油性。它在低温下聚合,并含有足够的抗氧化剂,以满足正常老化条件。它具有较低的门尼粘度、优良的加工特性、快速的固化速度、较低的霉菌污染、优良的回弹性能和优越的流动性。NANCAR® 3345是一种优良的多用途丁腈弹性体。它可以与乙烯树脂混合,产生光滑的挤压和无神经的片材。建议的应用包括燃油软管、填料、垫圈、油封、其他汽车零件、耐油皮带、鞋、辊盖和海绵产品。 NANCAR® 3345 is a medium high acrylonitrile butadiene copolymer with good oil resistance. It is polymerized at low temperature and contains sufficient antioxidant for normal aging conditions. It has low Mooney viscosity, superior processing characteristics, fast curing rate, low mold fouling, superior resilience properties and superior flowability. NANCAR® 3345 is an excellent multi-purpose nitrile elastomer. It may be blended with vinyl resins to produce smooth extrusions and nerve-free sheets. Suggested applications include those in fuel hoses, packings, gaskets, oil seals, other car parts, oil resistant belts, footwear, roll covers and sponge products. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.980 | g/cm³ | |
门尼粘度 Mooney viscosity |
|||
ML 1+4,100℃ ML 1+4,100℃ |
45 | MU | ASTM D1646 |
丙烯腈含量(Bound) Acrylonitrile content (Bound) |
33.0 | % | 内部方法 |
Stabilizer Stabilizer |
Non-staining | ||
可溶性 solubility |
|||
in MEK in MEK |
100 | % | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
ASTM D2240 | ||
邵氏 A Shaw's A 2 |
ASTM D2240 | ||
邵氏 A Shaw's A 3 |
ASTM D2240 | ||
邵氏 A Shaw's A 4 |
ASTM D2240 | ||
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
ASTM D412 | ||
300% 应变 300% strain 5 |
MPa | ASTM D412 | |
300% 应变 300% strain 6 |
MPa | ASTM D412 | |
300% 应变 300% strain 7 |
MPa | ASTM D412 | |
拉伸强度 tensile strength |
ASTM D412 | ||
屈服 yield 2 |
MPa | ASTM D412 | |
屈服 yield 3 |
MPa | ASTM D412 | |
屈服 yield 4 |
MPa | ASTM D412 | |
拉伸应变 Tensile strain |
ASTM D412 | ||
断裂 fracture 5 |
% | ASTM D412 | |
断裂 fracture 6 |
% | ASTM D412 | |
断裂 fracture 7 |
% | ASTM D412 | |
撕裂强度 tear strength 8 , 3 |
kN/m | ASTM D624 | |
压缩形变 Compression deformation 4 |
|||
100℃,70 hr 100℃,70 hr 4 |
% | ASTM D395 | |
老化性能 Aging performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
空气中拉伸强度的变化率 The rate of change in tensile strength in air 3 |
|||
100℃,70 hr 100℃,70 hr 3 |
% | ASTM D865 | |
空气中极限伸长率的变化率 The rate of change in ultimate elongation in air 3 |
|||
100℃,70 hr 100℃,70 hr 3 |
% | ASTM D865 | |
空气中硬度计硬度的变化率 The rate of change in hardness of a hardness tester in the air 3 |
|||
邵氏 A,100℃,70 hr Shore A, 100 ℃, 70 hr 3 |
ASTM D865 | ||
拉伸强度的变化率 The rate of change in tensile strength 3 |
ASTM D471 | ||
100℃,70 hr,在ASTM #1油中 100 ℃, 70 hr, in ASTM # 1 oil |
% | ASTM D471 | |
100℃,70 hr,在ASTM #3油中 100 ℃, 70 hr, in ASTM # 3 oil |
% | ASTM D471 | |
极限伸长率的变化率 Change rate of ultimate elongation 3 |
ASTM D471 | ||
100℃,70 hr,在ASTM #1油中 100 ℃, 70 hr, in ASTM # 1 oil |
% | ASTM D471 | |
100℃,70 hr,在ASTM #3油中 100 ℃, 70 hr, in ASTM # 3 oil |
% | ASTM D471 | |
邵氏硬度的变化率 The rate of change in Shore hardness 3 |
ASTM D471 | ||
支撐 A,100℃,70 hr,在ASTM #1油中 Support A, 100 ℃, 70 hr, in ASTM # 1 oil |
ASTM D471 | ||
支撐 A,100℃,70 hr,在ASTM #3油中 Support A, 100 ℃, 70 hr, in ASTM # 3 oil |
ASTM D471 | ||
体积变化 Volume change 3 |
ASTM D471 | ||
100℃,70 hr,ASTM 标准油(1号) 100 ℃, 70 hr, ASTM standard oil (No.1) |
% | ASTM D471 | |
100℃,70 hr,ASTM 标准油(3号) 100 ℃, 70 hr, ASTM standard oil (No.3) |
% | ASTM D471 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热损耗 Heat loss |
% | ASTM D5688 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 硫化 20.0 min 在 302°F |
3 硫化 40.0 min 在 302°F |
4 硫化 60.0 min 在 302°F |
5 Cured for 60.0 min at 150°C |
6 Cured for 40.0 min at 150°C |
7 Cured for 20.0 min at 150°C |
8 C 模具 |
【新闻资讯】查看全部
我国首创无氯氟聚氨酯发泡剂
2018-04-19 4月15日,山东理工大学和补天新材料技术有限公司共同完成的新型无氯氟聚氨酯化学发泡剂创制项目,在北京通过中国石油和化学工业联合会组织的科技成果鉴定。由中国科学院段雪院士、中国工程院苏义脑院士领衔的鉴定委员会认为,该技术成果属国内外首创,居国际领先水平,将对我国氯氟烃发泡剂替代产生重大的推动作用。 鉴定意见显示,该技术成果具有四大创新点:一是设计合成了两类新结构无氯氟聚氨酯化学发泡剂。这两类发泡剂为化学新物质,已完成毒理实验和新物质注册,安全绿色。二是提出了新结构发泡剂的开发 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |