牌号简介 About |
---|
PRIMACOR™ 1410共聚物是一种乙烯丙烯酸共聚物,适用于单层或是共挤出吹塑薄膜。 PRIMACOR 1410 共聚物专门用作复合薄膜中的热封层或是粘结剂层。 PRIMACOR 1410共聚物具有以下特性: 优异的热封性能和热粘性能 优异的韧性和强度 优异的耐开裂性能 对水分不敏感 良好的光学性能 应用领域: 特种包装和贴体包装 多层复合材料 符合以下法规要求: 美国食品和药品管理局(U.S. FDA) 21 CFR 177.1310(a)(1) 欧盟(EU) No 10/2011 请查阅法规以获取详尽资料。 PRIMACOR™ 1410 Copolymer is an ethylene acrylic acid copolymer suitable for monolayer or coextrusion blown films. PRIMACOR 1410 Copolymer has been specifically designed for use as a heat seal or adhesive layer in composite films. PRIMACOR 1410 Copolymer exhibits: Excellent hot tack and sealability Excellent toughness and strength Excellent crack resistance Insensitivity to moisture Good optical properties Applications: Speciality and skin packaging Multilayer films Complies with: U.S. FDA 21 CFR 177.1310(a)(1) EU, No 10/2011 Consult the regulations for complete details. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.938 | g/cm³ | ASTM D792 , ISO 1183 |
熔体质量流动速率 Melt Flow Rate 2 |
|||
190℃,2.16kg 190℃,2.16kg 2 |
1.5 | g/10min | ASTM D1238,ISO 1133 |
共聚单体含量 Co monomer content 3 |
9.7 | % | 内部方法 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
屈服,模压成型 Yield, molding 4 |
8.39 | MPa | ASTM D638 |
屈服,模压成型 Yield, molding |
8.39 | MPa | ISO 527-2/508 |
断裂,模压成型 Fracture, molded 4 |
MPa | ASTM D638 | |
断裂,模压成型 Fracture, molded |
MPa | ISO 527-2/508 | |
拉伸应变 Tensile strain |
|||
断裂,模压成型 Fracture, molded 4 |
% | ASTM D638 | |
断裂,模压成型 Fracture, molded |
% | ISO 527-2/508 | |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
MD,屈服,51 µm MD, yield, 51 µ m |
MPa | ASTM D882 | |
TD,屈服,51 µm TD, yield, 51 µ m |
MPa | ASTM D882 | |
MD,屈服,51 µm MD, yield, 51 µ m |
MPa | ISO 527-3 | |
TD,屈服,51 µm TD, yield, 51 µ m |
MPa | ISO 527-3 | |
MD,断裂,51 µm MD, fracture, 51 µ m |
MPa | ASTM D882 , ISO 527-3 | |
TD,断裂,51 µm TD, fracture, 51 µ m |
MPa | ASTM D882 , ISO 527-3 | |
拉伸应变 Tensile strain |
ASTM D882 , ISO 527-3 | ||
MD,断裂,51 µm MD, fracture, 51 µ m |
% | ASTM D882 , ISO 527-3 | |
TD,断裂,51 µm TD, fracture, 51 µ m |
% | ASTM D882 , ISO 527-3 | |
落锤冲击 Drop hammer impact |
|||
51 µm 51 µm |
g | ASTM D1709B , ISO 7765-1/B | |
埃尔曼多夫抗撕强度 Elmandorf tear strength 5 |
|||
MD:51 µm MD:51 µm |
g | ASTM D1922 | |
TD:51 µm TD:51 µm |
g | ASTM D1922 | |
MD:51 µm MD:51 µm |
N | ISO 6383-2 | |
TD:51 µm TD:51 µm |
N | ISO 6383-2 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 , ISO 306 | |
熔融温度 Melting temperature |
|||
DSC DSC |
℃ | 内部方法 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
45°,50.8 µm 45°,50.8 µm |
ASTM D2457 | ||
雾度 Haze |
|||
50.8 µm 50.8 µm |
% | ASTM D1003 | |
50.8 µm 50.8 µm |
% | ISO 14782 |
备注 |
---|
2 如同在生产时测量的一样。 |
3 通过 Dow 属性方法测量的共聚单体含量,和 ASTM D 4094 相比具有相同的精确性。 |
4 510 mm/min |
5 十字头速度为 20 英寸/分。 |
【新闻资讯】查看全部
牙膏里存在聚乙烯制成的小珠子
2018-06-19 牙膏应该是帮助清洁我们的牙齿并摆脱剩下的食物。但对于一些Crest牙膏用户来说,剩下的食物正在被微小的微珠所取代,使得微笑看起来斑点重重,牙龈也有斑点。这些附着在人们牙床上的小块塑料原来是微珠,是由聚乙烯制成的,不能生物降解的小珠子,它们很小,可以通过水过滤系统。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |