SABIC PP化合物37T1020 SABIC® PPcompound 37T1020是一种含20%滑石的高流动性共聚物,在硬度和抗冲击性之间提供了极好的平衡。它是专门为汽车内部零件,如柱包层和门板开发的。SABIC® PPcompound 37T1020是指定的汽车级。SABIC PP化合物37T1020 SABIC PP化合物37T1020是一种通用的滑石填充热稳定共聚物聚丙烯化合物。该化合物具有高冲击性和高流动性,适用于注塑应用。IMDS ID是16161338。 SABIC® PPcompound 37T1020 is a high flow copolymer with 20% talc, offering an excellent balance between stiffness and impact resistance. It has been specially developed for automotive interior parts such as column cladding and door panels. SABIC® PPcompound 37T1020 is a designated automotive grade. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.05 | g/cm³ | ASTM D792 |
密度 Density |
1.04 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
230℃,2.16kg 230℃,2.16kg |
13 | g/10min | ISO 1133 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
71 | ISO 868 | |
拉伸模量 Tensile modulus 2 |
2450 | MPa | ASTM D638 |
拉伸模量 Tensile modulus |
MPa | ISO 527-1-2 | |
拉伸强度 tensile strength 3 |
|||
断裂 fracture |
MPa | ISO 527-2/1A/50 | |
断裂 fracture 3 |
MPa | ASTM D638 | |
屈服 yield |
MPa | ISO 527-2/50 | |
屈服 yield 3 |
MPa | ASTM D638 | |
拉伸应变 Tensile strain 3 |
|||
断裂 fracture |
% | ISO 527-2/50 | |
断裂 fracture 4 |
% | ASTM D638 | |
屈服 yield |
% | ISO 527-2/50 | |
屈服 yield 3 |
% | ASTM D638 | |
弯曲模量 Bending modulus |
|||
50 mm跨距 50 mm span 4 |
MPa | ISO 178 | |
50 mm跨距 50 mm span 5 |
MPa | ASTM D790 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179/1eA | ||
-30℃ -30℃ 6 |
kJ/m² | ISO 179/1eA | |
23℃ 23℃ 7 |
kJ/m² | ISO 179/1eA | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch 6 |
ISO 180/1A | ||
23℃,3.2mm 23℃,3.2mm 8 |
J/m | ASTM D256 | |
-30℃ -30℃ |
kJ/m² | ISO 180-1A | |
0℃ 0℃ |
kJ/m² | ISO 180-1A | |
23℃ 23℃ |
kJ/m² | ISO 180-1A | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam 8 |
|||
23℃,3.2 mm 23℃,3.2 mm 8 |
J/m | ASTM D4812 | |
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments 9 |
|||
23℃,Energy at Peak Load 23℃,Energy at Peak Load 9 |
J | ASTM D3763 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature 6 |
|||
1.8 MPa,未退火,3.2 mm 1.8 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
1.8 MPa,未退火 1.8 MPa, unannealed 6 |
℃ | ISO 75-2/A | |
0.45 MPa,未退火,3.2 mm 0.45 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
0.45 MPa,未退火 0.45 MPa, unannealed 6 |
℃ | ISO 75-2/B | |
维卡软化温度 Vicat Softening Temp |
|||
A50 A50 |
℃ | ISO 306/A50 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
TD:-30~100℃ TD:-30~100℃ |
1/℃ | ISO 11359-2 | |
MD:-30~100℃ MD:-30~100℃ |
1/℃ | ISO 11359-2 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 2.0 in/min |
3 类型 1, 2.0 in/min |
4 0.079 in/min |
5 0.051 in/min |
6 方法 I (三点负荷) |
7 80*10*4mm, Cut |
8 80*10*4 mm, Cut |
9 63.5*12.7*3.2mm, Cut |
10 7.22 ft/sec |
【新闻资讯】查看全部
靖边县陕北首家塑料薄膜厂投产
2016-01-04 近日,陕北地区首家塑料薄膜企业――靖边华伟塑业有限公司在靖边县中小企业创业园内成功投产运营,填补了靖边县乃至陕北地区的塑料薄膜生产空白。 该项目占地20亩,概算投资4500万元,采用国内先进的塑料薄膜吹塑成型工艺,可年产3万吨农用聚乙烯大棚膜、地膜、滴灌带、水龙带等塑料产品,年可实现销售收入2亿元以上。该项目的投产对促进靖边现代农业发展和带动就业将起到积极的推动作用。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |