牌号简介 About |
---|
WONDERLITE® PC-175是一种聚碳酸酯(PC)产品,。 它,在亚太地区、北美洲、拉丁美洲、欧洲或非洲和中东有供货。 典型应用领域为:电气/电子应用。 主要特性为:通过 rohs 认证。 WONDERLITE® PC-175 is a Polycarbonate (PC) product. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Typical application: Electrical/Electronic Applications. Primary characteristic: rohs compliant. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density 2 |
1.20 | g/cm³ | ASTM D792 |
密度 Density |
1.20 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
300℃,1.20kg 300℃,1.20kg |
62 | g/10min | ASTM D1238 |
熔体体积流动速率 Melt Volume Rate |
|||
300℃,1.2 kg 300℃,1.2 kg |
65.0 | cm³/10min | ISO 1133 |
收缩率 Shrinkage rate |
0.50 to 0.70 | % | ISO 294-4 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
23℃ 23℃ |
kJ/m² | ISO 179 | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
kJ/m² | ISO 180-1A | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,退火 1.8 MPa, annealed |
℃ | ISO 75-2/A | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 6 | |
维卡软化温度 Vicat Softening Temp |
|||
A50 A50 |
℃ | ISO 306/A50 | |
B50 B50 |
℃ | ISO 306 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD MD |
1/℃ | ISO 11359-2 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
断裂 fracture |
MPa | ISO 527-2/50 | |
屈服 yield 3 |
MPa | ASTM D638 | |
屈服 yield |
MPa | ISO 527-2/50 | |
拉伸应变 Tensile strain |
|||
断裂 fracture 4 |
% | ASTM D638 | |
断裂 fracture |
% | ISO 527-2/50 | |
弯曲模量 Bending modulus 4 |
MPa | ASTM D790 | |
弯曲模量 Bending modulus 5 |
MPa | ISO 178 | |
弯曲强度 bending strength 4 |
MPa | ASTM D790 | |
弯曲强度 bending strength 5 |
MPa | ISO 178 | |
洛氏硬度 Rockwell hardness |
|||
M 级 M-level |
ASTM D785 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 23°C |
3 0,24 in/min |
4 0,051 in/min |
5 0,079 in/min |
6 速率 A (50°C/h), 压 力1 (10N) |
【新闻资讯】查看全部
中国蓝星与日本旭化成协作改性PPE树脂产销
2017-02-16 2月13日,中国蓝星(集团)股份有限公司与日本旭化成集团签署合作协议,双方将在中国国内正式生产和销售改性PPE(聚苯醚)树脂。 改性PPE树脂具有出色的耐热性、阻燃性、尺寸稳定性和机械特性,能够在车载电池零部件和太阳能发电零部件等环境能源领域发挥重要作用。中国蓝星是国内唯一的PPE单体及聚合物生产销售企业。根据该协议,本次合作中,双方将利用中国蓝星在PPE单体和聚合物方面的技术及成本优势,以及旭化成在改性PPE树脂上的加工及技术优势,共同开展PPE单体、聚合物、改性PPE树 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |