牌号简介 About |
---|
LNP*COLORCOMP*325C是一种通用的无增强PBT树脂。这一级别的附加功能包括改进的处理。适用于喷洒器、喷嘴、泵、门把手、油箱盖、笔和铅笔等。又名:lnp*colorcomp*化合物325产品再订购名称:325C LNP* COLORCOMP* 325C is a general purpose, unreinforced PBT resin. Added features of this grade include improved processing. Good for applications such as sprinklers, nozzles, pumps, door handles, tank covers, pens and pencils. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.31 | g/cm³ | ASTM D792 |
特定体积 Specific volume |
0.770 | cm³/g | ASTM D792 |
收缩率 Shrinkage rate |
内部方法 | ||
MD MD 3 |
1.5 到 2.3 | % | 内部方法 |
MD MD 4 |
0.90 到 1.6 | % | 内部方法 |
TD TD 4 |
1.0 到 1.7 | % | 内部方法 |
TD TD 3 |
% | 内部方法 | |
吸水率 Water absorption rate |
ASTM D570 | ||
24hr 24hr |
% | ASTM D570 | |
平衡,23℃ Equilibrium, 23 ℃ |
% | ASTM D570 | |
耐候性 Weathering resistance |
UL 746C | ||
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
J/m | ASTM D256 | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
23℃ 23℃ |
J/m | ASTM D4812 | |
落锤冲击 Drop hammer impact 7 |
|||
23℃ 23℃ 7 |
J | ASTM D3029 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
ASTM D648 | ||
0.45 MPa,未退火,6.4 mm 0.45 MPa, unannealed, 6.4 mm |
℃ | ASTM D648 | |
1.8 MPa,未退火,6.4 mm 1.8 MPa, unannealed, 6.4 mm |
℃ | ASTM D648 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD MD |
ASTM E831 | ||
-40 到 40℃ -40 to 40 ℃ |
cm/cm/℃ | ASTM E831 | |
60 到 138℃ 60 to 138 ℃ |
cm/cm/℃ | ASTM E831 | |
相对温度指数 Relative temperature index |
℃ | UL 746 | |
电气性能 Electrical performance |
℃ | UL 746 | |
冲击机械性能 Impact mechanical performance |
℃ | UL 746 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257 | |
介电强度 Dielectric strength |
ASTM D149 | ||
1.6 mm,在油中 1.6 mm in oil |
kV/mm | ASTM D149 | |
3.2 mm,在空气中 3.2 mm in air |
kV/mm | ASTM D149 | |
3.2 mm,在油中 3.2 mm in oil |
kV/mm | ASTM D149 | |
介电常数 Dielectric constant |
ASTM D150 | ||
100 Hz 100 Hz |
ASTM D150 | ||
1 MHz 1 MHz |
ASTM D150 | ||
耗散因数 Dissipation factor |
ASTM D150 | ||
100 Hz 100 Hz |
ASTM D150 | ||
1 MHz 1 MHz |
ASTM D150 | ||
耐电弧性 Arc resistance 8 |
ASTM D495 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
UL 746 | ||
高电弧燃烧指数(HAI) High Arc Burning Index (HAI) |
UL 746 | ||
高电压电弧起痕速率 High voltage arc marking rate |
|||
HVTR HVTR |
UL 746 | ||
热丝引燃 Hot wire ignition |
|||
HWI HWI |
UL 746 | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
0.80 mm 0.80 mm |
UL 94 | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
洛氏硬度 Rockwell hardness |
|||
R 级 R-level |
ASTM D785 | ||
拉伸强度 tensile strength 5 |
|||
屈服 yield 5 |
MPa | ASTM D638 | |
拉伸应变 Tensile strain 5 |
|||
断裂 fracture 5 |
% | ASTM D638 | |
弯曲模量 Bending modulus 6 |
|||
50 mm跨距 50 mm span 6 |
MPa | ASTM D790 | |
弯曲强度 bending strength 6 |
|||
屈服,50 mm跨度 Yield, 50 mm span 6 |
MPa | ASTM D790 |
备注 |
---|
3 2.3 to 4.6 mm |
4 0.75 to 2.3 mm |
5 类型 1, 50 mm/min |
6 1.3 mm/min |
7 Modified |
8 钨电极 |
【新闻资讯】查看全部
东营 千亿石化城喷薄渤海湾
2018-01-05 石油和化学工业是国民经济的基础产业,也是重要的支柱产业。东营市因油而建、因油而兴的城市,伴随着胜利油田的开发建设,该市在短短30多年的时间里迅速崛起为全国举足轻重的石油石化城。经济日报-中国经济网记者通过参访近距离透视东营市石化产业逆势发展的背后乾坤。 转型:敢为人先领立潮头 山东省东营市,一座因油而建、因油而兴的城市,伴随着胜利油田的开发建设,该市在短短30多年的时间里迅速崛起为全国举足轻重的石油石化城。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |