牌号简介 About |
---|
Polycasa压克力是Polycasa热塑性模塑料的商品名。Polycasa丙烯腈是一种基于聚甲基丙烯酸甲酯(PMMA)的高度透明、无定形热塑性塑料,而Polycasa丙烯腈KR产品是一种具有一系列熔融粘度的高冲击改性产品。有许多透明和不透明的颜色。出色的透明度和亮度。无与伦比的抗老化性能。表面硬度高。耐刮擦性。可回收性好。高光学质量。玻璃外观清晰。户外性能好。符合所有现行的欧洲食品接触法规,可用于接触食品。汽车应用。建筑物。照明。食物。标志。电的。卫生的。海军陆战队。医学。 Polycasa Acryl is the trade name for thermoplastic moulding compounds from Polycasa. Polycasa Acryl is a highly transparent, amorphous thermoplastic based on polymethylmethacrylate (PMMA), whilst Polycasa Acryl KR products are high-impact modified products with a range of melt viscosities. CHARACTERISTICS Available in many transparent and opaque shades. Excellent transparency and brilliance. Unsurpassed resistance to ageing. High surface hardness. Scratch resistance. Good recyclability. High optical quality. Glass-clear appearance. Good outdoor performance. Meets all current European food contact legislation and can be used in contact with foodstuffs. APPLICATIONS Automotive. Building. Lighting. Food. Signs. Electrical. Sanitary. Marine. Medical. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.14 | g/cm³ | ISO 1183 |
表观密度 Apparent density |
0.67 | g/cm³ | DIN 53466 |
熔体体积流动速率 Melt Volume Rate |
|||
230℃,3.8 kg 230℃,3.8 kg |
3.50 | cm³/10min | ISO 1133 |
收缩率 Shrinkage rate |
0.50 到 0.80 | % | |
吸水率 Water absorption rate |
|||
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
0.40 | % | |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
水蒸气渗透性 water vapor permeability |
g/m²/24 hr | DIN 53122 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
23℃ 23℃ |
kJ/m² | ISO 179/1e | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
|||
23℃ 23℃ |
kJ/m² | ISO 179/1eU | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/Af | |
维卡软化温度 Vicat Softening Temp |
|||
B50 B50 |
℃ | ISO 306 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:23~80℃ MD:23~80℃ |
1/℃ | DIN 53752 | |
比热 specific heat |
J/kg/℃ | IEC 1006 | |
导热系数 Thermal conductivity coefficient |
W/m/K | DIN 52612 | |
最高使用温度 Maximum operating temperature |
|||
short cycle operation short cycle operation |
℃ | ||
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | IEC 60093 | |
体积电阻率 Volume resistivity |
ohms·cm | IEC 60093 | |
介电强度 Dielectric strength 2 |
kV/mm | IEC 60243-1 | |
介电常数 Dielectric constant |
IEC 60250 | ||
100 Hz 100 Hz |
IEC 60250 | ||
1 MHz 1 MHz |
IEC 60250 | ||
耗散因数 Dissipation factor |
IEC 60250 | ||
100 Hz 100 Hz |
IEC 60250 | ||
1 MHz 1 MHz |
IEC 60250 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
|||
解决方案 B Solution B |
V | IEC 60112 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
折射率 Refractive index |
ISO 489 | ||
透光率 Transmittance |
|||
3000 µm 3000 µm |
% | DIN 5036-3 | |
雾度 Haze |
% | DIN 5036-3 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
球压硬度 Ball hardness |
|||
H358/30 H358/30 |
MPa | ISO 2039-1 | |
拉伸模量 Tensile modulus |
MPa | ISO 527-2 | |
拉伸强度 tensile strength |
|||
断裂 fracture |
MPa | ISO 527-2 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ISO 527-2 | |
弯曲强度 bending strength |
MPa | ISO 178 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 K20/P50 |
【新闻资讯】查看全部
全球半导体市场增长26%,环氧塑封料企业德高化成利润增长120%
2022-03-22 3月18日,新三板上市企业天津德高化成新材料股份有限公司发布2021年业绩公告;全年营业收入8304万元,同比增长58%;扣非净利润1063万元,同比增长121%。 德高化成成立于2008年,是一家 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |