牌号简介 About |
---|
滑动改性双向拉伸聚丙烯薄膜非热封双面处理 Slip Modified BIAXIALLY ORIENTED POLYPROPYLENE FILM NON-HEAT SEALABLE, TWO SIDE TREATED |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
尺寸稳定性 dimensional stability 2 |
|||
TD,130℃ TD,130℃ |
< 3.0 | % | |
MD,130℃ MD,130℃ |
< 5.0 | % | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
摩擦系数 friction coefficient |
ASTM D1894 | ||
动态 dynamic |
0.20 | ASTM D1894 | |
静态 static state |
0.25 | ASTM D1894 | |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
25 | µm | |
拉伸强度 tensile strength |
ASTM D882 | ||
MD,屈服 MD, yield |
MPa | ASTM D882 | |
TD,屈服 TD, yield |
MPa | ASTM D882 | |
拉伸应变 Tensile strain |
ASTM D882 | ||
MD,断裂 MD, fracture |
% | ASTM D882 | |
TD,断裂 TD, fracture |
% | ASTM D882 | |
水气透过率 Water vapor transmittance |
|||
38℃,90% RH 38℃,90% RH |
g/m²/24 hr | ASTM F1249 | |
用量 dosage 3 |
m²/kg | ||
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
45° 45° |
ASTM D2457 | ||
雾度 Haze |
% | ASTM D1003 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面能 Surface energy |
ASTM D2578 | ||
-- -- 4 |
dyne/cm | ASTM D2578 | |
-- -- 5 |
dyne/cm | ASTM D2578 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 5 minutes |
3 Internal Method |
4 Corona Side |
5 High Energy Flame Side |
【新闻资讯】查看全部
吉林油田CCUS-EOR方案过审
2022-04-04 3月7日,中国石油吉林油田已编制完成集团公司首个20万吨二氧化碳捕集埋存与提高采收率(CCUS-EOR)开发方案,顺利通过板块专家组审查。 历经30年攻关,吉林油田创新形成了陆相油藏C |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |