牌号简介 About |
---|
优质CoEx热封双向取向聚丙烯薄膜 Premium CoEx Heat Sealable BIAXIALLY ORIENTED POLYPROPYLENE FILM TWO SIDE SEALABLE FOR FOOD PACKAGING |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
尺寸稳定性 dimensional stability |
|||
TD,130℃ TD,130℃ 2 |
< 3.0 | % | |
MD,130℃ MD,130℃ 3 |
< 5.0 | % | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
摩擦系数 friction coefficient |
|||
动态 dynamic |
0.20 | ASTM D1894 | |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
20 | µm | |
拉伸强度 tensile strength |
ASTM D882 | ||
MD,屈服 MD, yield |
11.7 | MPa | ASTM D882 |
TD,屈服 TD, yield |
MPa | ASTM D882 | |
拉伸应变 Tensile strain |
ASTM D882 | ||
MD,断裂 MD, fracture |
% | ASTM D882 | |
TD,断裂 TD, fracture |
% | ASTM D882 | |
水气透过率 Water vapor transmittance |
|||
38℃,90% RH 38℃,90% RH |
g/m²/24 hr | ASTM F1249 | |
用量 dosage 4 |
m²/kg | ||
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
45° 45° |
ASTM D2457 | ||
雾度 Haze |
% | ASTM D1003 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Heat Seal Temperature Heat Seal Temperature 5 |
|||
Treated Side Treated Side |
℃ | ||
Untreated side Untreated side |
℃ | ||
表面能 Surface energy |
dyne/cm | ASTM D2578 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 5 minuites |
3 5 minutes |
4 Internal Method |
5 1/2 sec, 30 PSI |
【新闻资讯】查看全部
三井化学将在亚太地域投资消费α甲基苯乙烯和异丙醇产品
2018-05-15 日本三井化学公司将在亚太地区投资生产α甲基苯乙烯 (AMS) 和异丙醇 (IPA)产品。 公司预计在2018年中期开始投资建厂, 预计工厂将在2020到2021年之间开始正式投入使用。 目前,三井公司正在评估AMS在新加坡的业务潜力以及IPA在新加坡与泰国的需求量。以此来规划公司未来的市场战略。这两种产品都是苯酚的副产品,而苯酚是三井化工公司基础素材业务的支柱。 通过对于苯酚的充分利用, 三井公司希望可以进一步增强酚醛链的盈利能力。 α-甲基苯乙烯可用于生产 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |