牌号简介 About |
---|
Amodel® AT-1002 HS是一种整洁、增韧、热稳定的聚邻苯二甲酰胺(ppa)树脂,在湿热老化后具有优异的保持性能;在低温下具有高冲击性,比许多未增强的热塑性聚酯和尼龙树脂具有更好的机械性能。这种材料专门设计用于汽车电气/电子应用,如连接器、插座和传感器。自然:AT-1002 hs nt Amodel® AT-1002 HS is a neat, toughened, heat stabilized polyphthalamide (PPA) resin that offers superior retention of properties after humid thermal aging; high impact at low temperature and better mechanical properties than many unreinforced thermoplastic polyester and nylon resins. This material was specifically designed for automotive electrical/electronic applications such as connectors, sockets and sensors. Natural: AT-1002 HS NT |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.13 | g/cm³ | ISO 1183/A |
收缩率 Shrinkage rate |
|||
TD TD |
2.1 | % | ASTM D955 |
MD MD |
2.0 | % | ASTM D955 |
吸水率 Water absorption rate |
|||
24hr 24hr |
0.50 | % | ASTM D570 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
2760 | MPa | ASTM D638 |
拉伸模量 Tensile modulus |
ISO 527-2 | ||
23℃ 23℃ |
MPa | ISO 527-2 | |
100℃ 100℃ |
MPa | ISO 527-2 | |
拉伸强度 tensile strength |
MPa | ASTM D638 | |
断裂,23℃ Fracture, 23 ℃ |
MPa | ISO 527-2 | |
拉伸强度 tensile strength |
ISO 527-2 | ||
屈服,23℃ Yield, 23 ℃ |
MPa | ISO 527-2 | |
屈服,100℃ Yield, 100 ℃ |
MPa | ISO 527-2 | |
拉伸应变 Tensile strain |
ISO 527-2 | ||
断裂,23℃ Fracture, 23 ℃ |
% | ISO 527-2 | |
断裂 fracture 2 |
% | ASTM D638 | |
屈服,23℃ Yield, 23 ℃ |
% | ISO 527-2 | |
屈服,100℃ Yield, 100 ℃ |
% | ISO 527-2 | |
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
弯曲模量 Bending modulus |
ISO 178 | ||
23℃ 23℃ |
MPa | ISO 178 | |
100℃ 100℃ |
MPa | ISO 178 | |
弯曲强度 bending strength |
MPa | ASTM D790 | |
弯曲强度 bending strength |
ISO 178 | ||
23℃ 23℃ |
MPa | ISO 178 | |
100℃ 100℃ |
MPa | ISO 178 | |
剪切强度 shear strength |
MPa | ASTM D732 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
|||
23℃ 23℃ |
ISO 179/1eU | ||
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
J/m | ASTM D256 | |
23℃ 23℃ |
kJ/m² | ISO 180-1A | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
23℃ 23℃ |
ISO 180/1U | ||
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments |
|||
Total Energy Total Energy |
J | ASTM D3763 | |
Penetration Impact Penetration Impact 3 |
N | ASTM D3763 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,退火 1.8 MPa, annealed |
℃ | ASTM D648 | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/Af | |
0.45 MPa,退火 0.45 MPa, annealed |
℃ | ASTM D648 | |
熔融峰值温度 Melting peak temperature |
℃ | ASTM D3418 | |
熔融温度 Melting temperature |
℃ | ISO 11357-3 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
TD TD |
ASTM E831 | ||
0 到 100℃ 0 to 100 ℃ |
cm/cm/℃ | ASTM E831 | |
100 到 200℃ 100 to 200 ℃ |
cm/cm/℃ | ASTM E831 | |
MD MD |
ASTM E831 | ||
0 到 100℃ 0 to 100 ℃ |
cm/cm/℃ | ASTM E831 | |
100 到 200℃ 100 to 200 ℃ |
cm/cm/℃ | ASTM E831 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | ASTM D257 | |
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257 | |
介电强度 Dielectric strength |
kV/mm | ASTM D149 | |
介电常数 Dielectric constant |
ASTM D150 | ||
60 Hz 60 Hz |
ASTM D150 | ||
1 MHz 1 MHz |
ASTM D150 | ||
耗散因数 Dissipation factor |
ASTM D150 | ||
60 Hz 60 Hz |
ASTM D150 | ||
1 MHz 1 MHz |
ASTM D150 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
V | ASTM D3638 | |
高电压电弧起痕速率 High voltage arc marking rate |
|||
HVTR HVTR |
mm/min | UL 746 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level 5 |
UL 94 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 类型 4 |
3 Maximum Load |
4 最大负荷 |
5 这些可燃性等级不代表这些材料或任何其他材料在实际着火灾情况下的危险性。 |
【新闻资讯】查看全部
陶氏在印度推出完全可回收聚乙烯包装处置方案
2018-02-01 陶氏化学公司旗下陶氏包装与特种塑料事业部开发出创新的聚乙烯 (PE) 树脂配方,为印度带来一种新型、可持续、全 PE 复合软包装的解决方案。 目前的软包装解决方案是不同的聚合物和添加剂的多层结构,它们在回收过程中不相容,需要复杂的过程分解。陶氏的革命性全PE复合软包装解决方案,在不影响美感、品牌认知和性能的同时,能够让包装在用完之后实现100%可回收。 陶氏包装与特种塑料业务部亚太区商务副总裁李明壮(Bambang Candra)表示:“陶氏鼓励负责任地生产 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |