PA6，Durethan® DPBKV60EFW1 000000对比PA6，Durethan® DPBKV60EF 000000物性表,价格行情_搜料

牌号信息	Durethan® DPBKV60EFW1 000000 物性表 PA6 & 德国朗盛指导价格：暂无塑料库存：缺货	Durethan® DPBKV60EF 000000 物性表 PA6 & 德国朗盛指导价格：暂无塑料库存：缺货
牌号简介	PA 6，60%玻璃纤维，注塑成型，改善流动性，天气稳定 Durethan® DPBKV60EFW1 000000 (Dry) PA 6, 60 % glass fibers, injection molding, improved flowability, weather stabilized Durethan® DPBKV60EFW1 000000 PA 6, 60 % glass fibers, injection molding, improved flowability, weather stabilized Durethan® DPBKV60EFW1 000000 PA 6, 60 % glass fibers, injection molding, improved flowability, weather stabilized	PA 6，60%玻璃纤维，注塑成型，提高流动性 Durethan® DPBKV60EF 000000 (Dry) PA 6, 60 % glass fibers, injection molding, improved flowability Durethan® DPBKV60EF 000000 PA 6, 60 % glass fibers, injection molding, improved flowability Durethan® DPBKV60EF 000000 PA 6, 60 % glass fibers, injection molding, improved flowability

产品描述
厂家：	德国朗盛 LANXESS	德国朗盛 LANXESS
类别：	PA6 PA6	PA6 PA6
填料：	玻璃纤维 60	玻璃纤维 60
用途：
性能特点：	耐候抗UV,易流动 Weather resistance is good,Good liquidity	易流动 Good liquidity
加工条件：	注射成型 Injection Molding	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL Durethan® DPBKV60EFW1 000000 Durethan® DPBKV60EF 000000 单位
UNIT 测试方法
TEST METHOD

密度
Density g/cm³

收缩率(MD：120℃，2.0 mm)
Shrinkage rate %

收缩率(MD：280℃，2.0 mm)
Shrinkage rate %

收缩率(TD：120℃，2.0 mm)
Shrinkage rate %

收缩率(TD：280℃，2.0 mm)
Shrinkage rate %

机械性能
MECHANICAL Durethan® DPBKV60EFW1 000000 Durethan® DPBKV60EF 000000 单位
UNIT 测试方法
TEST METHOD

弯曲应变
Bending strain %

弯曲强度(23℃)
bending strength MPa

弯曲模量(23℃)
Bending modulus MPa

拉伸应变(断裂，23℃)
Tensile strain %

拉伸强度(断裂，23℃)
tensile strength MPa

拉伸模量(23℃)
Tensile modulus MPa

冲击性能
IMPACT Durethan® DPBKV60EFW1 000000 Durethan® DPBKV60EF 000000 单位
UNIT 测试方法
TEST METHOD

多轴向仪器化冲击力峰值(-30℃)
Multi axial instrumented peak impact force N

多轴向仪器化冲击力峰值(23℃)
Multi axial instrumented peak impact force N

多轴向仪器化冲击能量(-30℃，冲击总贯穿能量)
Multi axial instrumented impact energy J

多轴向仪器化冲击能量(23℃，冲击总贯穿能量)
Multi axial instrumented impact energy J

悬臂梁无缺口冲击强度(-30℃)
Notched impact strength of cantilever beam kJ/m²

悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam kJ/m²

悬臂梁缺口冲击强度(-30℃)
Impact strength of cantilever beam notch kJ/m²

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m²

简支梁无缺口冲击强度(-30℃)
Charpy Unnotch Impact strength kJ/m²

简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength kJ/m²

简支梁缺口冲击强度(-30℃)
Charpy Notched Impact Strength kJ/m²

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m²

热性能
THERMAL Durethan® DPBKV60EFW1 000000 Durethan® DPBKV60EF 000000 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃

熔融温度
Melting temperature ℃

线性热膨胀系数(MD：23~55℃)
Linear coefficient of thermal expansion 1/℃

线性热膨胀系数(TD：23~55℃)
Linear coefficient of thermal expansion 1/℃

补充信息
Durethan® DPBKV60EFW1 000000 Durethan® DPBKV60EF 000000 单位
UNIT 测试方法
TEST METHOD

ISO Shortname
ISO Shortname

电气性能
ELECTRICAL Durethan® DPBKV60EFW1 000000 Durethan® DPBKV60EF 000000 单位
UNIT 测试方法
TEST METHOD

相比漏电起痕指数(解决方案 A)
Compared to the leakage tracing index V

阻燃性能
FLAMMABILITY Durethan® DPBKV60EFW1 000000 Durethan® DPBKV60EF 000000 单位
UNIT 测试方法
TEST METHOD

阻燃等级(0.75 mm)
Flame retardant level

阻燃等级(1.50 mm)
Flame retardant level

加工方式

注射 Durethan® DPBKV60EFW1 000000 Durethan® DPBKV60EF 000000 单位测试方法

Residual Moisture Content % Karl Fisher

加工熔体温度 °C

干燥时间 - Dry Air Dryer hr

干燥温度 - Dry Air Dryer °C

模具温度 °C

备注

2. 60x60x2mm, 4 hr

3. 60x60x2mm, 80°C MT, 600 bar

4. 2.0 mm/min

5. 2 mm/min

6. 10°C/min

3. 60x60x2mm, 4 hr

4. 60x60x2mm, 80°C MT, 600 bar

5. 2.0 mm/min

6. 2 mm/min

7. 10°C/min


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
补充信息
电气性能
阻燃性能
加工方式
注射
备注
返回顶部