PBT+PET，POCAN® DPT7140LDS 000000对比PBT+PET，POCAN® KU 1-7313 000000物性表,价格行情_搜料

牌号信息	POCAN® DPT7140LDS 000000 物性表 PBT+PET & 德国恩骅力指导价格：暂无塑料库存：缺货	POCAN® KU 1-7313 000000 物性表 PBT+PET & 德国恩骅力指导价格：暂无塑料库存：缺货
牌号简介	PET+PBT，44%玻璃纤维/矿物，注塑，LD，高热尺寸稳定性 POCAN® DPT7140LDS 000000 PET+PBT, 44 % glass fibers/mineral, injection molding, LDS, high thermal dimension stability POCAN® DPT7140LDS 000000 PET+PBT, 44 % glass fibers/mineral, injection molding, LDS, high thermal dimension stability POCAN® DPT7140LDS 000000 PET+PBT, 44 % glass fibers/mineral, injection molding, LDS, high thermal dimension stability	Pocan ku 1-7313 000000 PBT+PET，15%玻璃纤维，注塑，改善表面光洁度，增加温度峰值负荷 POCAN® KU1-7313 000000 PBT+PET, 15 % glass fibers, injection molding, improved surface finish, increased temperature peak load POCAN® KU1-7313 000000 PBT+PET, 15 % glass fibers, injection molding, improved surface finish, increased temperature peak load POCAN® KU1-7313 000000 PBT+PET, 15 % glass fibers, injection molding, improved surface finish, increased temperature peak load

产品描述
厂家：	德国恩骅力 Envalior	德国恩骅力 Envalior
类别：	PBT+PET PBT+PET	PBT+PET PBT+PET
填料：	玻璃纤维 44	玻璃纤维 15
用途：
性能特点：	尺寸稳定性好 Good Dimensional Stability	耐高温,表面光泽度好,耐热性好,防火阻燃等级HB High Heat Resistance,Good surface appearance,Heat Resistance, Good,HB
加工条件：	注射成型 Injection Molding	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL POCAN® DPT7140LDS 000000 POCAN® KU 1-7313 000000 单位
UNIT 测试方法
TEST METHOD

吸水率(平衡，23℃，50% RH)
Water Absorption % ISO 62

吸水率(饱和，23℃)
Water Absorption % ISO 62

密度
Density g/cm³ ISO 1183

收缩率(MD：120℃，2.0 mm)
Shrinkage %

收缩率(MD：120℃，2.0 mm，2 hrs)
Shrinkage % ISO 294-4

收缩率(MD：270℃，2.0 mm)
Shrinkage % ISO 294-4

收缩率(MD：280℃，2.0 mm)
Shrinkage %

收缩率(TD：120℃，2.0 mm)
Shrinkage %

收缩率(TD：120℃，2.0 mm，2 hrs)
Shrinkage % ISO 294-4

收缩率(TD：270℃，2.0 mm)
Shrinkage % ISO 294-4

收缩率(TD：280℃，2.0 mm)
Shrinkage %

熔体体积流动速率(260℃，2.16 kg)
Melt Volume Rate cm³/10min ISO 1133

熔体体积流动速率(280℃，2.16 kg)
Melt Volume Rate cm³/10min ISO 1133

粘度值(降低的粘度)
Viscosity value ml/g ISO 1628

表观密度
Apparent density g/cm³ ISO 60

机械性能
MECHANICAL POCAN® DPT7140LDS 000000 POCAN® KU 1-7313 000000 单位
UNIT 测试方法
TEST METHOD

弯曲应变
Flexural Strain %

弯曲应变
Flexural Strain % ISO 178/A

弯曲强度(23℃)
Flexural Strength MPa ISO 178

弯曲强度(23℃)
Flexural Strength MPa ISO 178-A

弯曲强度(3.50% 应变)
Flexural Strength MPa ISO 178-A

弯曲模量(23℃)
Flexural Modulus MPa ISO 178-A

拉伸应变(断裂，23℃)
Tensile strain % ISO 527-2/5

拉伸强度(断裂，23℃)
tensile strength MPa ISO 527-2/5

拉伸模量(23℃)
Tensile modulus MPa ISO 527-1-2

球压硬度
ball-indentation hardness MPa ISO 2039-1

冲击性能
IMPACT POCAN® DPT7140LDS 000000 POCAN® KU 1-7313 000000 单位
UNIT 测试方法
TEST METHOD

悬臂梁无缺口冲击强度(-30℃)
Izod Unnotched Impact strength kJ/m²

悬臂梁无缺口冲击强度(-30℃)
Izod Unnotched Impact strength kJ/m² ISO 180/1U

悬臂梁无缺口冲击强度(23℃)
Izod Unnotched Impact strength kJ/m²

悬臂梁无缺口冲击强度(23℃)
Izod Unnotched Impact strength kJ/m² ISO 180/1U

悬臂梁缺口冲击强度(-30℃)
Izod Notched Impact strength kJ/m²

悬臂梁缺口冲击强度(-30℃)
Izod Notched Impact strength kJ/m² ISO 180-1A

悬臂梁缺口冲击强度(-40℃)
Izod Notched Impact strength kJ/m² ISO 180-1A

悬臂梁缺口冲击强度(23℃)
Izod Notched Impact strength kJ/m²

悬臂梁缺口冲击强度(23℃)
Izod Notched Impact strength kJ/m² ISO 180-1A

简支梁无缺口冲击强度(-30℃)
Charpy Unnotched Impact strength kJ/m²

简支梁无缺口冲击强度(-30℃)
Charpy Unnotched Impact strength kJ/m² ISO 179/1eU

简支梁无缺口冲击强度(23℃)
Charpy Unnotched Impact strength kJ/m²

简支梁无缺口冲击强度(23℃)
Charpy Unnotched Impact strength kJ/m² ISO 179/1eU

简支梁缺口冲击强度(-30℃)
Charpy Notched Impact Strength kJ/m²

简支梁缺口冲击强度(-30℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m²

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

热性能
THERMAL POCAN® DPT7140LDS 000000 POCAN® KU 1-7313 000000 单位
UNIT 测试方法
TEST METHOD

导热系数(23℃)
Thermal Conductivity W/m/K ISO 8302

热变形温度(0.45 MPa，未退火)
HDT ℃ ISO 75-2/B

热变形温度(1.8 MPa，未退火)
HDT ℃ ISO 75-2/A

熔融温度
Melting temperature ℃ ISO 11357-3

球压测试(210℃)
Ball pressure test IEC 60695-10-2

线性热膨胀系数(MD：23~55℃)
Coeff.of linear therm expansion 1/℃

线性热膨胀系数(MD：23~55℃)
Coeff.of linear therm expansion 1/℃ ISO 11359-2

线性热膨胀系数(TD：23~55℃)
Coeff.of linear therm expansion 1/℃

线性热膨胀系数(TD：23~55℃)
Coeff.of linear therm expansion 1/℃ ISO 11359-2

维卡软化温度(B120)
Vicat Softening Temperature ℃ ISO 306/B120

维卡软化温度(B50)
Vicat Softening Temperature ℃ ISO 306

电气性能
ELECTRICAL POCAN® DPT7140LDS 000000 POCAN® KU 1-7313 000000 单位
UNIT 测试方法
TEST METHOD

介电强度(23 ℃，1 mm)
Dielectric strength kV/mm IEC 60243-1

体积电阻率(23℃)
Volume resistivity ohms·cm IEC 60093

相对电容率(23℃，1 MHz)
Relative permittivity

相对电容率(23℃，1 MHz)
Relative permittivity IEC 60250

相对电容率(23℃，100 Hz)
Relative permittivity

相对电容率(23℃，100 Hz)
Relative permittivity IEC 60250

相比漏电起痕指数(解决方案 A)
Comparative Tracking Index V IEC 60112

耗散因数(23℃，1 MHz)
Dissipation factor

耗散因数(23℃，1 MHz)
Dissipation factor IEC 60250

耗散因数(23℃，100 Hz)
Dissipation factor

耗散因数(23℃，100 Hz)
Dissipation factor IEC 60250

表面电阻率
Surface resistivity ohms IEC 60093

阻燃性能
FLAMMABILITY POCAN® DPT7140LDS 000000 POCAN® KU 1-7313 000000 单位
UNIT 测试方法
TEST METHOD

极限氧指数
Oxygen Index % ISO 4589-2

灼热丝可燃性指数(2.0 mm)
Glow Wire Flammability Index(GWFI) ℃ IEC 60695-2-12

阻燃等级
Flame Class Rating UL 94

阻燃等级(0.80 mm)
Flame Class Rating UL 94

阻燃等级(1.60 mm)
Flame Class Rating UL 94

补充信息
POCAN® DPT7140LDS 000000 POCAN® KU 1-7313 000000 单位
UNIT 测试方法
TEST METHOD

ISO Shortname
ISO Shortname

ISO Shortname
ISO Shortname ISO 7792

电解腐蚀
Electrolytic corrosion IEC 60426

加工方式

注射 POCAN® DPT7140LDS 000000 POCAN® KU 1-7313 000000 单位测试方法

Residual Moisture Content %

Residual Moisture Content % Karl Fisher

加工熔体温度 °C

干燥时间 - 除湿干燥剂 hr

干燥温度 - 除湿干燥剂 °C

模具温度 °C

备注

3. 60x60x2mm, 4 hr

4. 60x60x2mm, 110°C MT, 600 bar

5. 2.0 mm/min

6. 2 mm/min

7. 10°C/min

1 一般属性：这些不能被视为规格。

2 60x60x2mm, 90°C MT, 600 bar

3 60x60x2; MT 90°C; 600 Bar

4 60x60x2

5 60x60x2mm

6 0.079 in/min

7 2 mm/min

8 Pull Rate: 2 mm/min; 50% RH

9 10°C/min

10 程序 A


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
电气性能
阻燃性能
补充信息
加工方式
注射
备注
返回顶部