PC，LEXAN™ Copolymer CXT19EX对比PC，LEXAN™ HPB3144 resin物性表,价格行情_搜料

牌号信息	LEXAN™ Copolymer CXT19EX 物性表 PC & 沙特沙伯基础指导价格：暂无塑料库存：缺货	LEXAN™ HPB3144 resin 物性表 PC & 沙特沙伯基础指导价格：暂无塑料库存：缺货
牌号简介	Lexan CXT19EX树脂是一种高温聚碳酸酯共聚物树脂，VICAT为190°C，透明透明。这种树脂是为片材和薄膜挤出应用而优化的，具有较低的压盘和较宽的加工窗口，并且黄变程度有限。它的透明色有限。 LEXAN™ CXT19EX resin is a High Heat Polycarbonate Copolymer Resin with Vicat of 190°C and crystal clear transparency. This resin is optimized for sheet and film extrusion applications, has a low plateout and a broad processing window with limited yellowing. It is available in limited transparent colors.	标准流量，透明，高纯度聚碳酸酯共聚物树脂，降低氧气渗透性和水蒸气透过率。用于医疗设备和医药应用。卫生保健变更管理，生物相容性（ISO 10993或USP六级），符合食品接触。 Standard flow, transparent, high purity polycarbonate copolymer resin with reduced oxygen permeability and water vapor transmission rate. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO 10993 or USP Class VI), food contact compliant.

产品描述
厂家：	沙特沙伯基础 SABIC	沙特沙伯基础 SABIC
类别：	PC Polycarbonate	PC Polycarbonate
填料：
用途：	汽车内部零件,电器用具,照明应用,Automotive Lighting,电子显示器	药物,医疗器械
性能特点：		高纯度,生物兼容性,食品接触,透湿性差,共聚物 High purity,Biocompatible,Food contact compliance,Poor moisture permeability,Copolymer
加工条件：		注射成型 Injection Molding

技术参数

物理性能
PHYSICAL LEXAN™ Copolymer CXT19EX LEXAN™ HPB3144 resin 单位
UNIT 测试方法
TEST METHOD

吸水率(24hr)
Water Absorption % ASTM D570

吸水率(24hr，50% RH)
Water Absorption % ASTM D570

吸水率(平衡，23℃)
Water Absorption % ASTM D570

吸水率(平衡，23℃，50% RH)
Water Absorption %

吸水率(平衡，23℃，50% RH)
Water Absorption % ISO 62

吸水率(平衡，50% RH)
Water Absorption % ASTM D570

吸水率(饱和，23℃)
Water Absorption %

吸水率(饱和，23℃)
Water Absorption % ISO 62

密度
Density g/cm³ ASTM D792

密度(--)
Density g/cm³ ASTM D792

密度(--)
Density g/cm³ ISO 1183，ASTM D792

收缩率(MD：3.2 mm)
Shrinkage %

收缩率(MD：3.2 mm)
Shrinkage % 内部方法

收缩率(TD：3.2 mm)
Shrinkage %

熔体体积流动速率(300℃，1.2 kg)
Melt Volume Rate cm³/10min ISO 1133

熔体体积流动速率(330℃，2.16 kg)
Melt Volume Rate cm³/10min ISO 1133

熔体质量流动速率(300℃，1.20kg)
Melt Flow Rate g/10min ASTM D1238

熔体质量流动速率(330℃，2.16kg)
Melt Flow Rate g/10min ASTM D1238

特定体积
Specific volume cm³/g ASTM D792

机械性能
MECHANICAL LEXAN™ Copolymer CXT19EX LEXAN™ HPB3144 resin 单位
UNIT 测试方法
TEST METHOD

Erichson Scratch Depth(6N)
Erichson Scratch Depth（6N） µm 内部方法

弯曲强度(--)
Flexural Strength MPa ISO 178

弯曲强度(屈服，50 mm跨度)
Flexural Strength MPa ASTM D790

弯曲模量(--)
Flexural Modulus MPa ISO 178

弯曲模量(50 mm跨距)
Flexural Modulus MPa ASTM D790

拉伸应变(屈服)
Tensile strain % ASTM D638

拉伸应变(屈服)
Tensile strain % ISO 527-2/50

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸应变(断裂)
Tensile strain % ISO 527-2/50

拉伸强度(屈服)
tensile strength MPa ASTM D638

拉伸强度(屈服)
tensile strength MPa ISO 527-2/50

拉伸强度(断裂)
tensile strength MPa ASTM D638

拉伸强度(断裂)
tensile strength MPa ISO 527-2/50

拉伸模量(--)
Tensile modulus MPa ASTM D638

拉伸模量(--)
Tensile modulus MPa ISO 527-1-2

泰伯耐磨性(1000 周期，1000 g，CS-17 转轮)
Taber Abrasion mg ASTM D1044

泰伯耐磨性(1000 周期，1000 g，CS-17 转轮)
Taber Abrasion mg 内部方法

洛氏硬度(L 级)
Rockwell hardness

洛氏硬度(M 级)
Rockwell hardness

球压硬度(H358/30)
ball-indentation hardness MPa ISO 2039-1

铅笔硬度
Pencil hardness ASTM D3363

冲击性能
IMPACT LEXAN™ Copolymer CXT19EX LEXAN™ HPB3144 resin 单位
UNIT 测试方法
TEST METHOD

悬臂梁无缺口冲击强度(-30℃)
Izod Unnotched Impact strength kJ/m² ISO 180/1U

悬臂梁无缺口冲击强度(23℃)
Izod Unnotched Impact strength ASTM D4812, ISO 180/1U

悬臂梁无缺口冲击强度(23℃)
Izod Unnotched Impact strength ISO 180/1U

悬臂梁缺口冲击强度(-30℃)
Izod Notched Impact strength J/m ASTM D256

悬臂梁缺口冲击强度(-30℃)
Izod Notched Impact strength kJ/m² ISO 180-1A

悬臂梁缺口冲击强度(23℃)
Izod Notched Impact strength J/m ASTM D256

悬臂梁缺口冲击强度(23℃)
Izod Notched Impact strength kJ/m² ISO 180-1A

简支梁无缺口冲击强度(-30℃)
Charpy Unnotched Impact strength kJ/m²

简支梁无缺口冲击强度(23℃)
Charpy Unnotched Impact strength

简支梁无缺口冲击强度(23℃)
Charpy Unnotched Impact strength ISO 179/1eU

简支梁缺口冲击强度(-30℃)
Charpy Notched Impact Strength kJ/m²

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m²

装有测量仪表的落镖冲击(23℃，Total Energy)
Dart impact equipped with measuring instruments J ASTM D3763

热性能
THERMAL LEXAN™ Copolymer CXT19EX LEXAN™ HPB3144 resin 单位
UNIT 测试方法
TEST METHOD

导热系数
Thermal Conductivity W/m/K ASTM C177, ISO 8302

导热系数
Thermal Conductivity W/m/K ISO 8302

比热
specific heat J/kg/℃ ASTM C351

热变形温度(0.45 MPa，未退火，100 mm跨距)
HDT ℃ ISO 75-2/Be

热变形温度(0.45 MPa，未退火，3.2 mm)
HDT ℃ ASTM D648

热变形温度(0.45 MPa，未退火，4.0 mm，64 mm跨距)
HDT ℃ ISO 75-2/Bf

热变形温度(1.8 MPa，未退火，100 mm跨距)
HDT ℃ ISO 75-2/Ae

热变形温度(1.8 MPa，未退火，3.2 mm)
HDT ℃ ASTM D648

热变形温度(1.8 MPa，未退火，4.0 mm，64 mm跨距)
HDT ℃ ISO 75-2/Af

玻璃化转变温度(一半的宽度)
Glass transition temperature ℃ 内部方法

球压测试(125℃)
Ball pressure test

球压测试(140℃)
Ball pressure test

线性热膨胀系数(MD：-40~40℃)
Coeff.of linear therm expansion 1/℃

线性热膨胀系数(MD：-40~95℃)
Coeff.of linear therm expansion 1/℃ ASTM E831

线性热膨胀系数(MD：23~80℃)
Coeff.of linear therm expansion 1/℃ ISO 11359-2

线性热膨胀系数(TD：-40~95℃)
Coeff.of linear therm expansion 1/℃ ASTM E831

线性热膨胀系数(TD：-40℃)
Coeff.of linear therm expansion 1/℃

线性热膨胀系数(TD：23~80℃)
Coeff.of linear therm expansion 1/℃ ISO 11359-2

维卡软化温度(--)
Vicat Softening Temperature ℃ ASTM D1525 18

维卡软化温度(B120)
Vicat Softening Temperature ℃ ISO 306/B120

维卡软化温度(B50)
Vicat Softening Temperature ℃ ISO 306

光学性能
OPTICAL LEXAN™ Copolymer CXT19EX LEXAN™ HPB3144 resin 单位
UNIT 测试方法
TEST METHOD

折射率
Refractive index ASTM D542，ISO 489

折射率
Refractive index ISO 489

色散系数
Dispersion coefficient ISO 489

透光率(1000 µm)
Light Transmission %

透光率(2000 µm)
Light Transmission %

透光率(2540 µm)
Light Transmission % ASTM D1003

透光率(3000 µm)
Light Transmission %

雾度(2540 µm)
Haze % ASTM D1003

电气性能
ELECTRICAL LEXAN™ Copolymer CXT19EX LEXAN™ HPB3144 resin 单位
UNIT 测试方法
TEST METHOD

介电常数(1 MHz)
Dielectric constant

介电常数(50 Hz)
Dielectric constant

介电常数(60 Hz)
Dielectric constant

体积电阻率
Volume resistivity ohms·cm ASTM D257

相比漏电起痕指数
Comparative Tracking Index UL 746

加工方式

挤压说明 LEXAN™ Copolymer CXT19EX LEXAN™ HPB3144 resin 单位测试方法

注射 LEXAN™ Copolymer CXT19EX LEXAN™ HPB3144 resin 单位测试方法

加工熔体温度 °C

射嘴温度 °C

干燥时间 hr

干燥温度 °C

建议的最大水分含量 %

料斗温度 °C

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

备注

2. 5.0 mm/min

3. 类型 1, 50 mm/min

4. 1.3 mm/min

5. 2.0 mm/min

6. at Yield

7. 80*10*3 sp=62mm

8. 80*10*3 mm

9. 80*10*4 mm

10. 标准 B (120°C/h), 载荷2 (50N)

1 一般属性：这些不能被视为规格。

2 0.20 in/min

3 类型 1, 2.0 in/min

4 0.051 in/min

5 0.079 in/min

6 Yield

7 80*10*3 sp=62mm

8 80*10*3

9 1 kgf

10 120*10*4 mm

11 标准 B (120°C/h), 载荷2 (50N)

12 Approximate maximum


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
光学性能
电气性能
加工方式
挤压说明
注射
备注