LNP*Thermocomp*RF008H是一种基于尼龙66的化合物,含有40%的玻璃纤维。这个级别的附加功能是:医疗保健。 LNP* THERMOCOMP* RF008H is a compound based on Nylon 66 containing 40% Glass Fiber. Added feature of this grade is: Healthcare.
Plaslube® PA6/6 GF40 TL10是一种聚酰胺66(尼龙66)产品,含有的填充物为40% 玻璃纤维增强材料。 它可以通过注射成型进行加工,在北美洲有供货。 特性包括: 阻燃/额定火焰 热稳定剂 润滑 Plaslube® PA6/6 GF40 TL10 is a Polyamide 66 (Nylon 66) product filled with 40% glass fiber. It can be processed by injection molding and is available in North America. Characteristics include: Flame Rated Heat Stabilizer Lubricated
产品描述
厂家:
沙特沙伯基础 SABIC
美国Techmer
类别:
PA66 PA66
PA66 PA66
填料:
玻璃纤维 40
玻璃纤维 40
用途:
医疗/护理用品
性能特点:
润滑性,热稳定性好,防火阻燃等级HB Lubricating,Heat Stabilized,HB
加工条件:
注射成型 Injection Molding
注射成型 Injection Molding
技术参数
物理性能 PHYSICAL
LNP™ THERMOCOMP™ Compound RF008H
Plaslube® PA6/6 GF40 TL10
单位 UNIT 测试方法 TEST METHOD
吸水率(24hr)
Water absorption rate
%ASTM D570
吸水率(24hr,50% RH)
Water absorption rate
%ASTM D570
吸水率(平衡,23℃,50% RH)
Water absorption rate
%ISO 62
密度
Density
g/cm³ASTM D792
密度(--)
Density
g/cm³ASTM D792
密度(--)
Density
g/cm³ISO 1183
收缩率(MD:24 hrs)
Shrinkage rate
%ASTM D955
收缩率(MD:3.2 mm)
Shrinkage rate
%ASTM D955
收缩率(TD:24 hrs)
Shrinkage rate
%ASTM D955
收缩率(TD:24 hrs)
Shrinkage rate
%ISO 294-4
机械性能 MECHANICAL
LNP™ THERMOCOMP™ Compound RF008H
Plaslube® PA6/6 GF40 TL10
单位 UNIT 测试方法 TEST METHOD
弯曲应力(--)
Bending stress
MPaISO 178
弯曲应力(断裂,50.0 mm 跨距)
Bending stress
MPaASTM D790
弯曲强度
bending strength
MPaASTM D790
弯曲模量
Bending modulus
MPaASTM D790
弯曲模量(--)
Bending modulus
MPaISO 178
弯曲模量(50 mm跨距)
Bending modulus
MPaASTM D790
抗张强度(断裂)
Tensile strength
MPaASTM D638
抗张强度(断裂)
Tensile strength
MPaISO 527-2/5
拉伸应变(断裂)
Tensile strain
%ASTM D638
拉伸应变(断裂)
Tensile strain
%ISO 527-2/5
拉伸强度(断裂)
tensile strength
MPaASTM D638
拉伸模量(--)
Tensile modulus
MPaASTM D638
拉伸模量(--)
Tensile modulus
MPaISO 527-1-2
摩擦系数(与钢 - 动态)
friction coefficient
ASTM D1894
摩擦系数(与钢 - 静态)
friction coefficient
ASTM D1894
洛氏硬度(R 级)
Rockwell hardness
ASTM D785
磨损因数
Wear factor
10^-8 mm³/N·mASTM D3702
冲击性能 IMPACT
LNP™ THERMOCOMP™ Compound RF008H
Plaslube® PA6/6 GF40 TL10
单位 UNIT 测试方法 TEST METHOD
悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam
J/mASTM D4812
悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam
kJ/m²ISO 180/1U
悬臂梁无缺口冲击强度(3.2 mm)
Notched impact strength of cantilever beam
J/mASTM D256
悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch
J/mASTM D256
悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch
kJ/m²ISO 180-1A
悬臂梁缺口冲击强度(23℃,3.2mm)
Impact strength of cantilever beam notch
J/mASTM D256
装有测量仪表的落镖冲击(--)
Dart impact equipped with measuring instruments
JISO 6603-2
装有测量仪表的落镖冲击(23°C,Total Energy)
Dart impact equipped with measuring instruments
JASTM D3763
热性能 THERMAL
LNP™ THERMOCOMP™ Compound RF008H
Plaslube® PA6/6 GF40 TL10
单位 UNIT 测试方法 TEST METHOD
热变形温度(0.45 MPa,未退火)
Hot deformation temperature
℃ASTM D648
热变形温度(1.8 MPa,未退火)
Hot deformation temperature
℃ASTM D648
热变形温度(1.8 MPa,未退火,3.2 mm)
Hot deformation temperature
℃ASTM D648
热变形温度(1.8 MPa,未退火,4.0 mm,64 mm跨距)
Hot deformation temperature
℃ISO 75-2/Af
线性热膨胀系数(MD)
Linear coefficient of thermal expansion
1/℃ASTM D696
线性热膨胀系数(MD:-40~40℃)
Linear coefficient of thermal expansion
1/℃ASTM E831
线性热膨胀系数(MD:-40~40℃)
Linear coefficient of thermal expansion
1/℃ISO 11359-2
线性热膨胀系数(TD:-40~40℃)
Linear coefficient of thermal expansion
1/℃ASTM E831
线性热膨胀系数(TD:-40℃)
Linear coefficient of thermal expansion
1/℃ISO 11359-2
电气性能 ELECTRICAL
LNP™ THERMOCOMP™ Compound RF008H
Plaslube® PA6/6 GF40 TL10
单位 UNIT 测试方法 TEST METHOD
介电强度
Dielectric strength
kV/mmASTM D149
体积电阻率
Volume resistivity
ohms·cmASTM D257
阻燃性能 FLAMMABILITY
LNP™ THERMOCOMP™ Compound RF008H
Plaslube® PA6/6 GF40 TL10
单位 UNIT 测试方法 TEST METHOD