EBANTIX® E1303
EBA & 西班牙莱普索尔
ALCUDIA® EBA PA-1303
EBA & 西班牙莱普索尔
牌号信息 |
EBA & 西班牙莱普索尔 指导价格:暂无 塑料库存: 缺货 |
EBA & 西班牙莱普索尔 指导价格:暂无 塑料库存: 缺货 |
|
牌号简介 | EBA Repsol Ebantix E1303是一种共聚物,适用于要求良好柔韧性和良好机械性能的吹塑薄膜应用。丙烯酸丁酯含量为13%。它含有抗氧化添加剂。用途:薄膜挤出。拉伸软篷薄膜。农用薄膜。电缆。推荐的熔融温度180°C。E1303的加工特性与LDPE相似,推荐使用传统的聚乙烯挤出机。各生产线的加工条件应得到优化。 EBA REPSOL EBANTIX ® E1303 is a copolymer suitable for blown film applications where good flexibility and very good mechanical properties are required. The butyl acrylate content is 13%. It contains antioxidant additives. Applications: Film extrusion. Stretch hood film. Agricultural films. Cables. Recommended melt temperature 180°C. Processing characteristics of E1303 are similar to LDPE and conventional polyethylene extruders are recommended. Processing conditions should be optimised for each production line. |
EBA Alcudia PA-1303是一种共聚物,适用于需要良好柔韧性和良好机械性能的吹塑薄膜应用。丙烯酸丁酯含量为13%。典型应用膜挤出拉伸罩膜农业膜推荐熔融温度180°C。PA-1303的加工特性与低密度聚乙烯相似,推荐使用传统的聚乙烯挤出机。各生产线的加工条件应得到优化。 EBA ALCUDIA® PA-1303 is a copolymer suitable for blown film applications where good flexibility and very good mechanical properties are required. The butyl acrylate content is 13%. TYPICAL APPLICATIONS Film extrusion Stretch hood film Agricultural films Recommended melt temperature 180°C. Processing characteristics of PA-1303 are similar to LDPE and conventional polyethylene extruders are recommended. Processing conditions should be optimised for each production line. |
|
产品描述 | |||
厂家: | 西班牙莱普索尔 REPSOL | 西班牙莱普索尔 REPSOL | |
类别: | EBA EBA | EBA EBA | |
填料: | |||
用途: | 吹塑成型应用,薄膜,农业应用,拉伸缠绕 | 拉伸缠绕,薄膜,农业应用 | |
性能特点: | 韧性好,食品接触,抗氧化,共聚物 Good flexibility,Food contact compliance,Inoxidizability,Copolymer | 韧性好,食品接触 Good flexibility,Food contact compliance | |
加工条件: | 薄膜挤出 Film extrusion | 吹塑薄膜 |
备注 |
2、blow up ratio 1:2.5, frost line height 50 cm
3、F 50
|